General
Property | Temperature | Value | Comment |
---|---|---|---|
Density | 23.0 °C | 1.6 g/cm³ Show Material materials with Density of 1.6 g/cm³ | ISO 1183 |
Mechanical
Property | Temperature | Value | Comment |
---|---|---|---|
Elastic modulus | 23.0 °C | 15.5 GPa Show Material materials with Elastic modulus of 15.5 GPa | ISO 527-1/-2 |
Elongation | 23.0 °C | 1.7 % Show Material materials with Elongation of 1.7 % | ISO 527-1/-2 |
Flexural modulus | 23.0 °C | 15.1 GPa Show Material materials with Flexural modulus of 15.1 GPa | ISO 178 |
Flexural strength | 23.0 °C | 249 MPa Show Material materials with Flexural strength of 249 MPa | ISO 178 |
Impact strength, Charpy notched | -6.0 °C | 8 kJ/m² Show Material materials with Impact strength, Charpy notched of 8 kJ/m² | ISO 179/1eA |
23.0 °C | 8 kJ/m² Show Material materials with Impact strength, Charpy notched of 8 kJ/m² | ISO 179/1eA | |
Impact strength, Charpy unnotched | -6.0 °C | 45 kJ/m² Show Material materials with Impact strength, Charpy unnotched of 45 kJ/m² | ISO 179/1eU |
23.0 °C | 48 kJ/m² Show Material materials with Impact strength, Charpy unnotched of 48 kJ/m² | ISO 179/1eU | |
Poisson's ratio | 23.0 °C | 0.33 [-] Show Material materials with Poisson's ratio of 0.33 [-] | |
Tensile strength | 23.0 °C | 167 MPa Show Material materials with Tensile strength of 167 MPa | ISO 527-1/-2 |
Thermal
Property | Temperature | Value | Comment | ||
---|---|---|---|---|---|
Coefficient of thermal expansion | 23.0 °C | 1.4E-5 1/K Show Material materials with Coefficient of thermal expansion of 1.4E-5 1/K | ISO 11359-1/-2 | 23 - 55°C | ||
Coefficient of thermal expansion, transverse | 23.0 °C | 8E-5 1/K Show Material materials with Coefficient of thermal expansion, transverse of 8E-5 1/K | ISO 11359-1/-2 | 55 - 160°C | ||
Heat deflection temperature, 1.80 MPa | 284 °C Show Material materials with Heat deflection temperature, 1.80 MPa of 284 °C | ISO 75-1/-2 | |||
Melting point | 310 °C Show Material materials with Melting point of 310 °C | ISO 11357-1/-3 | first heat | |||
Relative temperature index, electrical | 140 °C Show Material materials with Relative temperature index, electrical of 140 °C | UL 746B | 120mil | |||
Relative temperature index, mechanical strength | 130 °C Show Material materials with Relative temperature index, mechanical strength of 130 °C | UL 746B | 120mil | |||
Flammability | Burning Behav. at thickness h: V-0 class, Thickness tested: 0.4 mm, UL recognition: yes -, Glow Wire Flammability Index, 15mil: 960 °C, Glow Wire Flammability Index, 30mil: 960 °C, Glow Wire Flammability Index, 60mil: 960 °C, Glow Wire Flammability Index, 120mil: 960 °C, Glow Wire Ignition Temperature, 30mil: 750 °C, Glow Wire Ignition Temperature, 15mil: 700 °C, Glow Wire Ignition Temperature, 60mil: 750 °C, Glow Wire Ignition Temperature, 120mil: 800 °C |
Electrical
Property | Temperature | Value | Comment |
---|---|---|---|
Comparative tracking index | 23.0 °C | 600 V Show Material materials with Comparative tracking index of 600 V | IEC 60112 |
Dielectric constant, 100Hz | 23.0 °C | 4.7 [-] Show Material materials with Dielectric constant, 100Hz of 4.7 [-] | IEC 62631-2-1 |
Dielectric constant, 1MHz | 23.0 °C | 4.4 [-] Show Material materials with Dielectric constant, 1MHz of 4.4 [-] | IEC 62631-2-1 |
Dielectric strength | 23.0 °C | 40 kV/mm Show Material materials with Dielectric strength of 40 kV/mm | IEC 60243-1 |
Dissipation factor, 100Hz | 23.0 °C | 6E-3 [-] Show Material materials with Dissipation factor, 100Hz of 6E-3 [-] | IEC 62631-2-1 |
Dissipation factor, 1MHz | 23.0 °C | 0.01 [-] Show Material materials with Dissipation factor, 1MHz of 0.01 [-] | IEC 62631-2-1 |
Volume resistivity | 23.0 °C | 1.00E+15 Ω·cm Show Material materials with Volume resistivity of 1.00E+15 Ω·cm | min. | IEC 62631-3-1 |
Rheological Properties
Technological properties
Property | ||
---|---|---|
Fillers | 45% Glass Fiber | |
Processing methods | Drying Recommended: yes, Drying Temperature: 100°C, Drying Time, Dehumidified Dryer: 6-8h, Processing Moisture Content: ≤0.1%, Min. melt temperature: 320°C, Max. melt temperature: 325°C, Min. mold temperature: 90°C, Max. mold temperature: 130°C |