General
Property | Temperature | Value | Comment |
---|---|---|---|
Density | 23.0 °C | 1.06 g/cm³ Show Material materials with Density of 1.06 g/cm³ | ISO 1183 |
Mechanical
Property | Temperature | Value | Comment | ||
---|---|---|---|---|---|
Elastic modulus | 23.0 °C | 1.8 GPa Show Material materials with Elastic modulus of 1.8 GPa | ISO 527-1/-2 | ||
Elongation | 23.0 °C | 500 % Show Material materials with Elongation of 500 % | min. | ISO 527-1/-2 | ||
Elongation at yield | 23.0 °C | 4 % Show Material materials with Elongation at yield of 4 % | ISO 527-1/-2 | ||
Flexural modulus | 23.0 °C | 1.7 GPa Show Material materials with Flexural modulus of 1.7 GPa | ISO 178 | ||
Hardness, Ball Indentation | 23.0 °C | 95 MPa Show Material materials with Hardness, Ball Indentation of 95 MPa | ISO 2039-1 | ||
Impact strength, Charpy notched | -40.0 °C | 18 kJ/m² Show Material materials with Impact strength, Charpy notched of 18 kJ/m² | ISO 179/1eA | ||
-6.0 °C | 17 kJ/m² Show Material materials with Impact strength, Charpy notched of 17 kJ/m² | ISO 179/1eA | |||
23.0 °C | 80 kJ/m² Show Material materials with Impact strength, Charpy notched of 80 kJ/m² | ISO 179/1eA | |||
Impact strength, Izod unnotched | -40.0 °C | 15 kJ/m² Show Material materials with Impact strength, Izod unnotched of 15 kJ/m² | ISO 180/1A | ||
-30.0 °C | 14 kJ/m² Show Material materials with Impact strength, Izod unnotched of 14 kJ/m² | ISO 180/1A | |||
23.0 °C | 60 kJ/m² Show Material materials with Impact strength, Izod unnotched of 60 kJ/m² | ISO 180/1A | |||
Poisson's ratio | 23.0 °C | 0.41 [-] Show Material materials with Poisson's ratio of 0.41 [-] | |||
Yield strength | 23.0 °C | 48 MPa Show Material materials with Yield strength of 48 MPa | ISO 527-1/-2 | ||
Impact strength, Charpy unnotched | No Break @ 23,-6°C, ISO 179/1eA |
Thermal
Property | Temperature | Value | Comment | ||
---|---|---|---|---|---|
Heat deflection temperature, 0.45 MPa | 95 °C Show Material materials with Heat deflection temperature, 0.45 MPa of 95 °C | ISO 75-1/-2 | |||
Heat deflection temperature, 1.80 MPa | 51 °C Show Material materials with Heat deflection temperature, 1.80 MPa of 51 °C | ISO 75-1/-2 | |||
Melting point | 221 °C Show Material materials with Melting point of 221 °C | ISO 11357-1/-3 | 18°F/min | |||
Specific heat capacity | 23.0 °C | 2600 J/(kg·K) Show Material materials with Specific heat capacity of 2600 J/(kg·K) | of melt | ||
Flammability | FMVSS Class: B -, Burning rate, Thickness 1 mm: <80 mm/min |
Rheological Properties
Technological properties
Property | ||
---|---|---|
Processing methods | Drying Recommended: yes, Drying Temperature: 80°C, Drying Time, Dehumidified Dryer: 2-4h, Processing Moisture Content: ≤0.2%, Melt Temperature Optimum: 270°C, Min. melt temperature: 260°C, Max. melt temperature: 280°C, Max. screw tangential speed: 0.3m/s, Mold Temperature Optimum: 70°C, Min. mold temperature: 50°C, Max. mold temperature: 90°C, Hold pressure range: 50-100MPa, Hold pressure time: 4s/mm |