Zytel® RS LC2600 BK043A

Alternative and trade names
PA-IP
Want to keep this datasheet? Save it now in your required format

Description

Zytel® RS LC2600 BK043A is an unreinforced, plasticized, high viscosity, biobased long chain polyamide resin developed for air brake tubes and fluid handling applications.

Equivalent Materials

This material data has been provided by Matmatch.

"Typical" values were obtained via a literature search. "Predicted" values were imputed via artificial intelligence technology. While we have placed significant efforts in ensuring data accuracy, "typical" and "predicted" data should be considered indicative and verified by appropriate material testing. Please do contact us if additional information on the the predicted data method is required.
All metrics apply to room temperature unless otherwise stated. SI units used unless otherwise stated.
Equivalent standards are similar to one or more standards provided by the supplier. Some equivalent standards may be stricter whereas others may be outside the bounds of the original standard.

Ashby charts

See where falls on the material property chart for against in your materials selection and design process. Our Ashby charts are interactive with more technical data upon clicking. Sign up to get access to this premium feature for free.

Properties

General

PropertyTemperatureValueComment

Density

23.0 °C

1.05 g/cm³

Show Material materials with Density of 1.05 g/cm³

ISO 1183

Mechanical

PropertyTemperatureValueComment

Elastic modulus

23.0 °C

1.15 GPa

Show Material materials with Elastic modulus of 1.15 GPa

ISO 527-1/-2

Elongation

23.0 °C

500 %

Show Material materials with Elongation of 500 %

min. | ISO 527-1/-2

Elongation at yield

23.0 °C

19 %

Show Material materials with Elongation at yield of 19 %

ISO 527-1/-2

Flexural modulus

23.0 °C

0.9 GPa

Show Material materials with Flexural modulus of 0.9 GPa

ISO 178

Impact strength, Charpy notched

-6.0 °C

11 kJ/m²

Show Material materials with Impact strength, Charpy notched of 11 kJ/m²

ISO 179/1eA

23.0 °C

65 kJ/m²

Show Material materials with Impact strength, Charpy notched of 65 kJ/m²

ISO 179/1eA

Poisson's ratio

23.0 °C

0.44 [-]

Show Material materials with Poisson's ratio of 0.44 [-]

Tensile strength

23.0 °C

36 MPa

Show Material materials with Tensile strength of 36 MPa

ISO 527-1/-2 | 50mm/min

Yield strength

23.0 °C

37.2 MPa

Show Material materials with Yield strength of 37.2 MPa

ISO 527-1/-2

Impact strength, Charpy unnotched

No Break @ 23°C,ISO 179/1eU

Thermal

PropertyValueComment

Glass transition temperature

40 °C

Show Material materials with Glass transition temperature of 40 °C

ISO 11357-1/-2 | 18°F/min

Heat deflection temperature, 1.80 MPa

43 °C

Show Material materials with Heat deflection temperature, 1.80 MPa of 43 °C

ISO 75-1/-2

Melting point

220 °C

Show Material materials with Melting point of 220 °C

ISO 11357-1/-3 | 18°F/min

Flammability

FMVSS Class: B -, Burning rate, Thickness 1 mm: <80 mm/min

Technological properties

Property