Properties
General
| Property | Temperature | Value | Comment |
|---|---|---|---|
Density | 23.0 °C | 1.33 g/cm³ Show Material materials with Density of 1.33 g/cm³ | ISO 1183 |
Water absorption | 23.0 °C | 0.85 % Show Material materials with Water absorption of 0.85 % | Sim. to ISO 62 | Immersion 24h |
Mechanical
| Property | Temperature | Value | Comment |
|---|---|---|---|
Elastic modulus | 23.0 °C | 8.9 GPa Show Material materials with Elastic modulus of 8.9 GPa | ISO 527-1/-2 |
Elongation | 23.0 °C | 3.7 % Show Material materials with Elongation of 3.7 % | ISO 527-1/-2 |
Flexural modulus | 23.0 °C | 7.5 GPa Show Material materials with Flexural modulus of 7.5 GPa | ISO 178 |
Flexural strength | 23.0 °C | 205 MPa Show Material materials with Flexural strength of 205 MPa | ISO 178 |
Hardness, Ball Indentation | 23.0 °C | 220 MPa Show Material materials with Hardness, Ball Indentation of 220 MPa | ISO 2039-1 |
Hardness, Rockwell M | 23.0 °C | 70 [-] Show Material materials with Hardness, Rockwell M of 70 [-] | ISO 2039-2 |
Hardness, Rockwell R | 23.0 °C | 110 [-] Show Material materials with Hardness, Rockwell R of 110 [-] | ISO 2039-2 |
Impact strength, Charpy notched | -40.0 °C | 14 kJ/m² Show Material materials with Impact strength, Charpy notched of 14 kJ/m² | ISO 179/1eA |
-6.0 °C | 18 kJ/m² Show Material materials with Impact strength, Charpy notched of 18 kJ/m² | ISO 179/1eA | |
23.0 °C | 20 kJ/m² Show Material materials with Impact strength, Charpy notched of 20 kJ/m² | ISO 179/1eA | |
Impact strength, Charpy unnotched | -6.0 °C | 106 kJ/m² Show Material materials with Impact strength, Charpy unnotched of 106 kJ/m² | ISO 179/1eU |
23.0 °C | 97 kJ/m² Show Material materials with Impact strength, Charpy unnotched of 97 kJ/m² | ISO 179/1eU | |
Impact strength, Izod notched | -30.0 °C | 80 kJ/m² Show Material materials with Impact strength, Izod notched of 80 kJ/m² | ISO 180/1U |
23.0 °C | 80 kJ/m² Show Material materials with Impact strength, Izod notched of 80 kJ/m² | ISO 180/1U | |
Impact strength, Izod unnotched | -40.0 °C | 15 kJ/m² Show Material materials with Impact strength, Izod unnotched of 15 kJ/m² | ISO 180/1A |
-30.0 °C | 17 kJ/m² Show Material materials with Impact strength, Izod unnotched of 17 kJ/m² | ISO 180/1A | |
23.0 °C | 21 kJ/m² Show Material materials with Impact strength, Izod unnotched of 21 kJ/m² | ISO 180/1A | |
Poisson's ratio | 23.0 °C | 0.34 [-] Show Material materials with Poisson's ratio of 0.34 [-] | |
Tensile strength | 23.0 °C | 146 MPa Show Material materials with Tensile strength of 146 MPa | ISO 527-1/-2 |
Thermal
| Property | Temperature | Value | Comment | ||
|---|---|---|---|---|---|
Coefficient of thermal expansion | 23.0 °C | 1.5E-5 1/K Show Material materials with Coefficient of thermal expansion of 1.5E-5 1/K | ISO 11359-1/-2 | ||
Coefficient of thermal expansion, transverse | 23.0 °C | 1.2E-4 1/K Show Material materials with Coefficient of thermal expansion, transverse of 1.2E-4 1/K | ISO 11359-1/-2 | ||
Glass transition temperature | 75 °C Show Material materials with Glass transition temperature of 75 °C | ISO 11357-1/-2 | 18°F/min | |||
Heat deflection temperature, 0.45 MPa | 261 °C Show Material materials with Heat deflection temperature, 0.45 MPa of 261 °C | ISO 75-1/-2 | |||
Heat deflection temperature, 1.80 MPa | 246 °C Show Material materials with Heat deflection temperature, 1.80 MPa of 246 °C | ISO 75-1/-2 | |||
Melting point | 262 °C Show Material materials with Melting point of 262 °C | ISO 11357-1/-3 | 18°F/min | |||
Relative temperature index, electrical | 130 °C Show Material materials with Relative temperature index, electrical of 130 °C | UL 746B | 120mil | |||
Relative temperature index, mechanical impact | 105 °C Show Material materials with Relative temperature index, mechanical impact of 105 °C | UL 746B | 120mil | |||
Relative temperature index, mechanical strength | 105 °C Show Material materials with Relative temperature index, mechanical strength of 105 °C | UL 746B | 120mil | |||
Specific heat capacity | 23.0 °C | 2200 J/(kg·K) Show Material materials with Specific heat capacity of 2200 J/(kg·K) | of melt | ||
Thermal diffusivity | 23.0 °C | 0 mm²/s Show Material materials with Thermal diffusivity of 0 mm²/s | |||
Vicat softening temperature | 245 °C Show Material materials with Vicat softening temperature of 245 °C | ISO 306 | 90°F/h, 11 lbf | |||
Flammability | Burning Behav. at 60mil nom. thickn.: HB class, Thickness tested: 1.5 mm, UL recognition: yes -, Burning Behav. at thickness h: HB class, Thickness tested: 0.75 mm, UL recognition: yes -, Glow Wire Flammability Index, 40mil: 650 °C, Glow Wire Flammability Index, 80mil: 700 °C, Glow Wire Flammability Index, 120mil: 900 °C, Glow Wire Ignition Temperature, 40mil: 700 °C, Glow Wire Ignition Temperature, 80mil: 700 °C, Glow Wire Ignition Temperature, 120mil: 750 °C, FMVSS Class: SE -, Burning rate, Thickness 1 mm: 23 mm/min | ||||
Electrical
| Property | Temperature | Value | Comment |
|---|---|---|---|
Dielectric constant, 1MHz | 23.0 °C | 3.6 [-] Show Material materials with Dielectric constant, 1MHz of 3.6 [-] | IEC 62631-2-1 |
Dissipation factor, 1MHz | 23.0 °C | 0.01 [-] Show Material materials with Dissipation factor, 1MHz of 0.01 [-] | IEC 62631-2-1 |
Volume resistivity | 23.0 °C | 1.00E+15 Ω·cm Show Material materials with Volume resistivity of 1.00E+15 Ω·cm | min. | IEC 62631-3-1 |
Rheological Properties
Technological properties
| Property | ||
|---|---|---|
| Fillers | 33% Glass Fiber | |
| Processing methods | Drying Recommended: yes, Drying Temperature: 80°C, Drying Time, Dehumidified Dryer: 2-4h, Processing Moisture Content: ≤0.2%, Melt Temperature Optimum: 295°C, Min. melt temperature: 285°C, Max. melt temperature: 305°C, Max. screw tangential speed: 0.2m/s, Mold Temperature Optimum: 80°C, Min. mold temperature: 50°C, Max. mold temperature: 100°C, Hold pressure range: 50-100MPa, Hold pressure time: 3s/mm, Ejection temperature: 210°C | |