General
Property | Temperature | Value | Comment |
---|---|---|---|
Density | 23.0 °C | 1.42 g/cm³ Show Material materials with Density of 1.42 g/cm³ | ISO 1183 |
Mechanical
Property | Temperature | Value | Comment |
---|---|---|---|
Elastic modulus | 23.0 °C | 10.5 GPa Show Material materials with Elastic modulus of 10.5 GPa | ISO 527-1/-2 |
Elongation | 23.0 °C | 3 % Show Material materials with Elongation of 3 % | ISO 527-1/-2 |
Flexural modulus | 23.0 °C | 9.3 GPa Show Material materials with Flexural modulus of 9.3 GPa | ISO 178 |
Flexural strength | 23.0 °C | 280 MPa Show Material materials with Flexural strength of 280 MPa | ISO 178 |
Impact strength, Charpy notched | -40.0 °C | 9 kJ/m² Show Material materials with Impact strength, Charpy notched of 9 kJ/m² | ISO 179/1eA |
-6.0 °C | 10 kJ/m² Show Material materials with Impact strength, Charpy notched of 10 kJ/m² | ISO 179/1eA | |
23.0 °C | 12 kJ/m² Show Material materials with Impact strength, Charpy notched of 12 kJ/m² | ISO 179/1eA | |
Impact strength, Charpy unnotched | -40.0 °C | 75 kJ/m² Show Material materials with Impact strength, Charpy unnotched of 75 kJ/m² | ISO 179/1eU |
23.0 °C | 85 kJ/m² Show Material materials with Impact strength, Charpy unnotched of 85 kJ/m² | ISO 179/1eU | |
Impact strength, Izod unnotched | 23.0 °C | 12 kJ/m² Show Material materials with Impact strength, Izod unnotched of 12 kJ/m² | ISO 180/1A |
Poisson's ratio | 23.0 °C | 0.34 [-] Show Material materials with Poisson's ratio of 0.34 [-] | |
Tensile strength | 23.0 °C | 180 MPa Show Material materials with Tensile strength of 180 MPa | ISO 527-1/-2 |
Thermal
Property | Temperature | Value | Comment | ||
---|---|---|---|---|---|
Coefficient of thermal expansion | 23.0 °C | 2E-5 1/K Show Material materials with Coefficient of thermal expansion of 2E-5 1/K | ISO 11359-1/-2 | -40 - 23°C | ||
Coefficient of thermal expansion, transverse | 23.0 °C | 6.5E-5 1/K Show Material materials with Coefficient of thermal expansion, transverse of 6.5E-5 1/K | ISO 11359-1/-2 | -40 - 23°C | ||
Glass transition temperature | 115 °C Show Material materials with Glass transition temperature of 115 °C | ISO 11357-1/-2 | 18°F/min | |||
Heat deflection temperature, 0.45 MPa | 283 °C Show Material materials with Heat deflection temperature, 0.45 MPa of 283 °C | ISO 75-1/-2 | |||
Heat deflection temperature, 1.80 MPa | 255 °C Show Material materials with Heat deflection temperature, 1.80 MPa of 255 °C | ISO 75-1/-2 | |||
Melting point | 300 °C Show Material materials with Melting point of 300 °C | ISO 11357-1/-3 | first heat | |||
Relative temperature index, electrical | 150 °C Show Material materials with Relative temperature index, electrical of 150 °C | UL 746B | 120mil | |||
Relative temperature index, mechanical impact | 130 °C Show Material materials with Relative temperature index, mechanical impact of 130 °C | UL 746B | 120mil | |||
Relative temperature index, mechanical strength | 140 °C Show Material materials with Relative temperature index, mechanical strength of 140 °C | UL 746B | 120mil | |||
Flammability | Burning Behav. at 60mil nom. thickn.: HB class, Thickness tested: 1.5 mm, UL recognition: yes -, Burning Behav. at thickness h: HB class, Thickness tested: 0.75 mm, UL recognition: yes -, FMVSS Class: SE - |
Electrical
Property | Temperature | Value | Comment |
---|---|---|---|
Comparative tracking index | 23.0 °C | 600 V Show Material materials with Comparative tracking index of 600 V | IEC 60112 |
Dielectric strength | 23.0 °C | 43 kV/mm Show Material materials with Dielectric strength of 43 kV/mm | IEC 60243-1 |
Volume resistivity | 23.0 °C | 1.00E+15 Ω·cm Show Material materials with Volume resistivity of 1.00E+15 Ω·cm | IEC 62631-3-1 |
Rheological Properties
Technological properties
Property | ||
---|---|---|
Fillers | 35% Glass Fiber | |
Processing methods | Drying Recommended: yes, Drying Temperature: 100°C, Drying Time, Dehumidified Dryer: 6-8h, Processing Moisture Content: ≤0.1%, Melt Temperature Optimum: 325°C, Min. melt temperature: 320°C, Max. melt temperature: 330°C, Min. mold temperature: 90°C, Max. mold temperature: 130°C |