General
Property | Temperature | Value | Comment |
---|---|---|---|
Density | 23.0 °C | 1.2 g/cm³ Show Material materials with Density of 1.2 g/cm³ | ISO 1183 |
Mechanical
Property | Temperature | Value | Comment |
---|---|---|---|
Elastic modulus | 23.0 °C | 10.4 GPa Show Material materials with Elastic modulus of 10.4 GPa | ISO 527-1/-2 |
Elongation | 23.0 °C | 2.4 % Show Material materials with Elongation of 2.4 % | ISO 527-1/-2 |
Flexural modulus | 23.0 °C | 8.7 GPa Show Material materials with Flexural modulus of 8.7 GPa | ISO 178 |
Flexural strength | 23.0 °C | 240 MPa Show Material materials with Flexural strength of 240 MPa | ISO 178 |
Impact strength, Charpy notched | -40.0 °C | 3 kJ/m² Show Material materials with Impact strength, Charpy notched of 3 kJ/m² | ISO 179/1eA |
23.0 °C | 6 kJ/m² Show Material materials with Impact strength, Charpy notched of 6 kJ/m² | ISO 179/1eA | |
Impact strength, Charpy unnotched | 23.0 °C | 48 kJ/m² Show Material materials with Impact strength, Charpy unnotched of 48 kJ/m² | ISO 179/1eU |
Poisson's ratio | 23.0 °C | 0.34 [-] Show Material materials with Poisson's ratio of 0.34 [-] | |
Tensile strength | 23.0 °C | 168 MPa Show Material materials with Tensile strength of 168 MPa | ISO 527-1/-2 |
Thermal
Property | Temperature | Value | Comment | ||
---|---|---|---|---|---|
Coefficient of thermal expansion | 23.0 °C | 1.5E-5 1/K Show Material materials with Coefficient of thermal expansion of 1.5E-5 1/K | ISO 11359-1/-2 | 23 - 55°C | ||
Coefficient of thermal expansion, transverse | 23.0 °C | 8.5E-5 1/K Show Material materials with Coefficient of thermal expansion, transverse of 8.5E-5 1/K | ISO 11359-1/-2 | 55 - 160°C | ||
Heat deflection temperature, 1.80 MPa | 258 °C Show Material materials with Heat deflection temperature, 1.80 MPa of 258 °C | ISO 75-1/-2 | |||
Melting point | 300 °C Show Material materials with Melting point of 300 °C | ISO 11357-1/-3 | first heat | |||
Flammability | FMVSS Class: B -, Burning rate, Thickness 1 mm: <80 mm/min |
Electrical
Property | Temperature | Value | Comment |
---|---|---|---|
Volume resistivity | 23.0 °C | 100000 Ω·cm Show Material materials with Volume resistivity of 100000 Ω·cm | ASTM D 4496 | conductive plastics |
Rheological Properties
Technological properties
Property | ||
---|---|---|
Fillers | 15% Carbon Fiber | |
Processing methods | Drying Recommended: yes, Drying Temperature: 100°C, Drying Time, Dehumidified Dryer: 6-8h, Processing Moisture Content: ≤0.1%, Melt Temperature Optimum: 325°C, Min. melt temperature: 320°C, Max. melt temperature: 330°C, Min. mold temperature: 85°C, Max. mold temperature: 135°C |