Zytel® LC7602 BK010A

Alternative and trade names
PA-HIP

Want to keep this datasheet? Save it now in your required format

Description

DuPont™ Zytel® LCPA long chain polyamide resins provide an innovative and growing portfolio of flexible polymers with excellent thermal, chemical, and hydrolysis resistance. The diverse selection of Zytel® LCPA grades is targeted for a range of performance characteristics, balancing temperature resistance, flexibility and low permeation.Zytel® LC7602 BK010A is a flexible, toughened and plasticized black polyamide resin intended for extrusion applications.

Equivalent Materials

This material data has been provided by Matmatch.

"Typical" values were obtained via a literature search. "Predicted" values were imputed via artificial intelligence technology. While we have placed significant efforts in ensuring data accuracy, "typical" and "predicted" data should be considered indicative and verified by appropriate material testing. Please do contact us if additional information on the the predicted data method is required.
All metrics apply to room temperature unless otherwise stated. SI units used unless otherwise stated.
Equivalent standards are similar to one or more standards provided by the supplier. Some equivalent standards may be stricter whereas others may be outside the bounds of the original standard.

Ashby charts

See where falls on the material property chart for against in your materials selection and design process. Our Ashby charts are interactive with more technical data upon clicking. Sign up to get access to this premium feature for free.

All categories

Properties

General

Property	Temperature	Value	Comment
Density	23.0 °C	1.03 g/cm³ Show Material materials with Density of 1.03 g/cm³	ISO 1183

Mechanical

Property	Temperature	Value	Comment
Elastic modulus	23.0 °C	0.65 GPa Show Material materials with Elastic modulus of 0.65 GPa	ISO 527-1/-2
Elongation	23.0 °C	500 % Show Material materials with Elongation of 500 %	min. \| ISO 527-1/-2
Flexural modulus	23.0 °C	0.62 GPa Show Material materials with Flexural modulus of 0.62 GPa	ISO 178
Impact strength, Charpy notched	-40.0 °C	15 kJ/m² Show Material materials with Impact strength, Charpy notched of 15 kJ/m²	ISO 179/1eA
	23.0 °C	105 kJ/m² Show Material materials with Impact strength, Charpy notched of 105 kJ/m²	ISO 179/1eA

Poisson's ratio	23.0 °C	0.46 [-] Show Material materials with Poisson's ratio of 0.46 [-]
Impact strength, Charpy unnotched	No Break @ 23,-6°C,ISO 179/1eU

Thermal

Property	Value	Comment
Glass transition temperature	50 °C Show Material materials with Glass transition temperature of 50 °C	ISO 11357-1/-2 \| 18°F/min
Heat deflection temperature, 0.45 MPa	55 °C Show Material materials with Heat deflection temperature, 0.45 MPa of 55 °C	ISO 75-1/-2
Heat deflection temperature, 1.80 MPa	39 °C Show Material materials with Heat deflection temperature, 1.80 MPa of 39 °C	ISO 75-1/-2
Melting point	210 °C Show Material materials with Melting point of 210 °C	ISO 11357-1/-3 \| 18°F/min
Flammability	FMVSS Class: B -, Burning rate, Thickness 1 mm: <80 mm/min

Rheological Properties

Property	Value	Comment
Melt mass-flow rate	12 g/10min Show Material materials with Melt mass-flow rate of 12 g/10min	ISO 1133 \| 240°C/5kg

Technological properties

Property

Zytel® LC7602 BK010A

Description

Equivalent Materials

Ashby charts

Suggested reading

Properties