General
Property | Temperature | Value | Comment |
---|---|---|---|
Density | 23.0 °C | 1.04 g/cm³ Show Material materials with Density of 1.04 g/cm³ | ISO 1183 |
Water absorption | 23.0 °C | 6.8 % Show Material materials with Water absorption of 6.8 % | Sim. to ISO 62 | 80mil |
Mechanical
Property | Temperature | Value | Comment | ||
---|---|---|---|---|---|
Elastic modulus | 23.0 °C | 0.9 GPa Show Material materials with Elastic modulus of 0.9 GPa | ISO 527-1/-2 | ||
Elongation | 23.0 °C | 250 % Show Material materials with Elongation of 250 % | ISO 527-1/-2 | 50mm/min | ||
Elongation at yield | 23.0 °C | 29 % Show Material materials with Elongation at yield of 29 % | ISO 527-1/-2 | ||
Flexural modulus | 23.0 °C | 0.85 GPa Show Material materials with Flexural modulus of 0.85 GPa | ISO 178 | ||
Hardness, Rockwell M | 23.0 °C | 60 [-] Show Material materials with Hardness, Rockwell M of 60 [-] | ISO 2039-2 | ||
Impact strength, Charpy notched | -6.0 °C | 14 kJ/m² Show Material materials with Impact strength, Charpy notched of 14 kJ/m² | ISO 179/1eA | ||
23.0 °C | 71 kJ/m² Show Material materials with Impact strength, Charpy notched of 71 kJ/m² | ISO 179/1eA | |||
Impact strength, Izod unnotched | -40.0 °C | 14 kJ/m² Show Material materials with Impact strength, Izod unnotched of 14 kJ/m² | ISO 180/1A | ||
Poisson's ratio | 23.0 °C | 0.45 [-] Show Material materials with Poisson's ratio of 0.45 [-] | |||
Yield strength | 23.0 °C | 31 MPa Show Material materials with Yield strength of 31 MPa | ISO 527-1/-2 | ||
Impact strength, Charpy unnotched | No Break @ 23,-6°C, ISO 179/1eA |
Thermal
Property | Temperature | Value | Comment | ||
---|---|---|---|---|---|
Coefficient of thermal expansion | 23.0 °C | 2E-4 1/K Show Material materials with Coefficient of thermal expansion of 2E-4 1/K | ISO 11359-1/-2 | ||
Coefficient of thermal expansion, transverse | 23.0 °C | 1.8E-4 1/K Show Material materials with Coefficient of thermal expansion, transverse of 1.8E-4 1/K | ISO 11359-1/-2 | ||
Glass transition temperature | 50 °C Show Material materials with Glass transition temperature of 50 °C | ISO 11357-1/-2 | 18°F/min | |||
Heat deflection temperature, 1.80 MPa | 47 °C Show Material materials with Heat deflection temperature, 1.80 MPa of 47 °C | ISO 75-1/-2 | |||
Melting point | 218 °C Show Material materials with Melting point of 218 °C | ISO 11357-1/-3 | 18°F/min | |||
Relative temperature index, electrical | 130 °C Show Material materials with Relative temperature index, electrical of 130 °C | UL 746B | 120mil | |||
Relative temperature index, mechanical impact | 105 °C Show Material materials with Relative temperature index, mechanical impact of 105 °C | UL 746B | 120mil | |||
Relative temperature index, mechanical strength | 110 °C Show Material materials with Relative temperature index, mechanical strength of 110 °C | UL 746B | 120mil | |||
Specific heat capacity | 23.0 °C | 2600 J/(kg·K) Show Material materials with Specific heat capacity of 2600 J/(kg·K) | of melt | ||
Vicat softening temperature | 95 °C Show Material materials with Vicat softening temperature of 95 °C | ISO 306 | 90°F/h, 11 lbf | |||
Flammability | Burning Behav. at 60mil nom. thickn.: HB class, Thickness tested: 1.5 mm, UL recognition: yes -, Burning Behav. at thickness h: HB class, Thickness tested: 0.75 mm, UL recognition: yes -, FMVSS Class: B -, Burning rate, Thickness 1 mm: <80 mm/min |
Electrical
Property | Temperature | Value | Comment |
---|---|---|---|
Dielectric strength | 23.0 °C | 31 kV/mm Show Material materials with Dielectric strength of 31 kV/mm | IEC 60243-1 |
Dissipation factor, 100Hz | 23.0 °C | 8E-3 [-] Show Material materials with Dissipation factor, 100Hz of 8E-3 [-] | IEC 62631-2-1 |
Dissipation factor, 1MHz | 23.0 °C | 0.01 [-] Show Material materials with Dissipation factor, 1MHz of 0.01 [-] | IEC 62631-2-1 |
Volume resistivity | 23.0 °C | 1.00E+15 Ω·cm Show Material materials with Volume resistivity of 1.00E+15 Ω·cm | IEC 62631-3-1 |
Rheological Properties
Technological properties
Property | ||
---|---|---|
Processing methods | Drying Recommended: yes, Drying Temperature: 60°C, Drying Time, Dehumidified Dryer: 2-4h, Processing Moisture Content: ≤0.2%, Melt Temperature Optimum: 270°C, Min. melt temperature: 260°C, Max. melt temperature: 280°C, Max. screw tangential speed: 0.3m/s, Mold Temperature Optimum: 70°C, Min. mold temperature: 50°C, Max. mold temperature: 90°C, Hold pressure range: 50-100MPa, Hold pressure time: 4s/mm, Ejection temperature: 190°C |