General
Property | Temperature | Value | Comment |
---|---|---|---|
Density | 23.0 °C | 1.43 g/cm³ Show Material materials with Density of 1.43 g/cm³ | ISO 1183 |
Water absorption | 23.0 °C | 6 % Show Material materials with Water absorption of 6 % | Sim. to ISO 62 | 80mil |
Mechanical
Property | Temperature | Value | Comment |
---|---|---|---|
Elastic modulus | 23.0 °C | 11 GPa Show Material materials with Elastic modulus of 11 GPa | ISO 527-1/-2 |
Elongation | 23.0 °C | 3.1 % Show Material materials with Elongation of 3.1 % | ISO 527-1/-2 |
Hardness, Ball Indentation | 23.0 °C | 285 MPa Show Material materials with Hardness, Ball Indentation of 285 MPa | ISO 2039-1 |
Impact strength, Charpy notched | 23.0 °C | 12 kJ/m² Show Material materials with Impact strength, Charpy notched of 12 kJ/m² | ISO 179/1eA |
Impact strength, Charpy unnotched | 23.0 °C | 80 kJ/m² Show Material materials with Impact strength, Charpy unnotched of 80 kJ/m² | ISO 179/1eU |
Poisson's ratio | 23.0 °C | 0.34 [-] Show Material materials with Poisson's ratio of 0.34 [-] | |
Tensile strength | 23.0 °C | 209 MPa Show Material materials with Tensile strength of 209 MPa | ISO 527-1/-2 |
Thermal
Property | Value | Comment | |
---|---|---|---|
Glass transition temperature | 65 °C Show Material materials with Glass transition temperature of 65 °C | ISO 11357-1/-2 | 18°F/min | |
Heat deflection temperature, 1.80 MPa | 249 °C Show Material materials with Heat deflection temperature, 1.80 MPa of 249 °C | ISO 75-1/-2 | |
Melting point | 269 °C Show Material materials with Melting point of 269 °C | ISO 11357-1/-3 | 18°F/min | |
Flammability | Burning Behav. at 60mil nom. thickn.: HB class, Thickness tested: 1.5 mm, FMVSS Class: B -, Burning rate, Thickness 1 mm: 25 mm/min |
Rheological Properties
Technological properties
Property | ||
---|---|---|
Fillers | 35% Glass Fiber | |
Processing methods | Drying Recommended: yes, Drying Temperature: 80°C, Drying Time, Dehumidified Dryer: 2-4h, Processing Moisture Content: ≤0.2%, Melt Temperature Optimum: 285°C, Min. melt temperature: 280°C, Max. melt temperature: 290°C, Max. screw tangential speed: 0.2m/s, Mold Temperature Optimum: 100°C, Min. mold temperature: 70°C, Max. mold temperature: 120°C, Hold pressure range: 50-100MPa, Hold pressure time: 3s/mm, Ejection temperature: 210°C |