Zytel® FG133F1 NC010

Want to keep this datasheet? Save it now in your required format

Description

Zytel® FG133F1 NC010 is unreinforced, nucleated polyamide 66. It has been developed for consideration into applications such as parts for the food industry.FOOD CONTACTThis product is manufactured according to Good Manufacturing Practice (GMP) principles and generally accepted in food contact applications in Europe and the USA when meeting applicable use conditions. For details, individual compliance statements are available from your DuPont representative.

Equivalent Materials

This material data has been provided by Matmatch.

"Typical" values were obtained via a literature search. "Predicted" values were imputed via artificial intelligence technology. While we have placed significant efforts in ensuring data accuracy, "typical" and "predicted" data should be considered indicative and verified by appropriate material testing. Please do contact us if additional information on the the predicted data method is required.
All metrics apply to room temperature unless otherwise stated. SI units used unless otherwise stated.
Equivalent standards are similar to one or more standards provided by the supplier. Some equivalent standards may be stricter whereas others may be outside the bounds of the original standard.

Ashby charts

See where falls on the material property chart for against in your materials selection and design process. Our Ashby charts are interactive with more technical data upon clicking. Sign up to get access to this premium feature for free.

All categories

Properties

General

Property	Temperature	Value	Comment
Density	23.0 °C	1.14 g/cm³ Show Material materials with Density of 1.14 g/cm³	ISO 1183

Mechanical

Property	Temperature	Value	Comment
Elastic modulus	23.0 °C	3.8 GPa Show Material materials with Elastic modulus of 3.8 GPa	ISO 527-1/-2
Elongation	23.0 °C	14 % Show Material materials with Elongation of 14 %	ISO 527-1/-2
Elongation at yield	23.0 °C	6 % Show Material materials with Elongation at yield of 6 %	ISO 527-1/-2
Impact strength, Charpy notched	23.0 °C	3 kJ/m² Show Material materials with Impact strength, Charpy notched of 3 kJ/m²	ISO 179/1eA
Poisson's ratio	23.0 °C	0.36 [-] Show Material materials with Poisson's ratio of 0.36 [-]
Yield strength	23.0 °C	94 MPa Show Material materials with Yield strength of 94 MPa	ISO 527-1/-2

Thermal

Property	Value	Comment
Heat deflection temperature, 1.80 MPa	78 °C Show Material materials with Heat deflection temperature, 1.80 MPa of 78 °C	ISO 75-1/-2
Melting point	262 °C Show Material materials with Melting point of 262 °C	ISO 11357-1/-3 \| 18°F/min
Flammability	FMVSS Class: B -, Burning rate, Thickness 1 mm: <80 mm/min

Rheological Properties

Property	Temperature	Value	Comment
Shrinkage	23.0 °C	0.8 % Show Material materials with Shrinkage of 0.8 %	ISO 294-4, 2577
Shrinkage, transverse	23.0 °C	1 % Show Material materials with Shrinkage, transverse of 1 %	ISO 294-4, 2577

Technological properties

Property
Processing methods	Drying Recommended: yes, Drying Temperature: 80°C, Drying Time, Dehumidified Dryer: 2-4h, Processing Moisture Content: ≤0.2%, Melt Temperature Optimum: 290°C, Min. melt temperature: 280°C, Max. melt temperature: 300°C, Max. screw tangential speed: 0.4m/s, Mold Temperature Optimum: 70°C, Min. mold temperature: 50°C, Max. mold temperature: 90°C, Hold pressure range: 50-100MPa, Hold pressure time: 4s/mm, Ejection temperature: 190°C

Zytel® FG133F1 NC010

Description

Equivalent Materials

Ashby charts

Suggested reading

Properties