Property | Temperature | Value | Comment |
---|---|---|---|
Density | 23.0 °C | 1.44 g/cm³ Show Material materials with Density of 1.44 g/cm³ | ISO 1183 |
Mechanical
Property | Temperature | Value | Comment |
---|---|---|---|
Elastic modulus | 23.0 °C | 10 GPa Show Material materials with Elastic modulus of 10 GPa | ISO 527-1/-2 |
Elongation | 23.0 °C | 2.2 % Show Material materials with Elongation of 2.2 % | ISO 527-1/-2 |
Flexural modulus | 23.0 °C | 8.7 GPa Show Material materials with Flexural modulus of 8.7 GPa | ISO 178 |
Flexural strength | 23.0 °C | 230 MPa Show Material materials with Flexural strength of 230 MPa | ISO 178 |
Impact strength, Charpy notched | 23.0 °C | 8 kJ/m² Show Material materials with Impact strength, Charpy notched of 8 kJ/m² | ISO 179/1eA |
Poisson's ratio | 23.0 °C | 0.34 [-] Show Material materials with Poisson's ratio of 0.34 [-] | |
Tensile strength | 23.0 °C | 150 MPa Show Material materials with Tensile strength of 150 MPa | ISO 527-1/-2 |
Thermal
Property | Value | Comment | |
---|---|---|---|
Heat deflection temperature, 1.80 MPa | 283 °C Show Material materials with Heat deflection temperature, 1.80 MPa of 283 °C | ISO 75-1/-2 | |
Melting point | 310 °C Show Material materials with Melting point of 310 °C | ISO 11357-1/-3 | first heat | |
Relative temperature index, electrical | 140 °C Show Material materials with Relative temperature index, electrical of 140 °C | UL 746B | 120mil | |
Relative temperature index, mechanical impact | 120 °C Show Material materials with Relative temperature index, mechanical impact of 120 °C | UL 746B | 120mil | |
Relative temperature index, mechanical strength | 130 °C Show Material materials with Relative temperature index, mechanical strength of 130 °C | UL 746B | 120mil | |
Flammability | Burning Behav. at 60mil nom. thickn.: V-0 class, Thickness tested: 1.5 mm, UL recognition: yes -, Burning Behav. at thickness h: V-0 class, Thickness tested: 0.4 mm, UL recognition: yes -, Oxygen index: 37 %, Glow Wire Flammability Index, 30mil: 960 °C, Glow Wire Flammability Index, 120mil: 960 °C, Glow Wire Ignition Temperature, 30mil: 725 °C, Glow Wire Ignition Temperature, 15mil: 700 °C, Glow Wire Ignition Temperature, 120mil: 775 °C, FMVSS Class: DNI -, Railway classification: R23 -, Railway classification rating: HL2 - |
Electrical
Property | Temperature | Value | Comment |
---|---|---|---|
Comparative tracking index | 23.0 °C | 600 V Show Material materials with Comparative tracking index of 600 V | IEC 60112 |
Dielectric constant, 100Hz | 23.0 °C | 4.3 [-] Show Material materials with Dielectric constant, 100Hz of 4.3 [-] | IEC 62631-2-1 |
Dielectric constant, 10GHz | 23.0 °C | 3.8 [-] Show Material materials with Dielectric constant, 10GHz of 3.8 [-] | ASTM D 2520 B |
Dielectric constant, 1GHz | 23.0 °C | 3.7 [-] Show Material materials with Dielectric constant, 1GHz of 3.7 [-] | ASTM D 2520 B |
Dielectric constant, 1MHz | 23.0 °C | 4 [-] Show Material materials with Dielectric constant, 1MHz of 4 [-] | IEC 62631-2-1 |
Dielectric strength | 23.0 °C | 26 kV/mm Show Material materials with Dielectric strength of 26 kV/mm | IEC 60243-1 | Short Time, 2mm |
Dissipation factor, 100Hz | 23.0 °C | 7E-3 [-] Show Material materials with Dissipation factor, 100Hz of 7E-3 [-] | IEC 62631-2-1 |
Dissipation factor, 1GHz | 23.0 °C | 0.01 [-] Show Material materials with Dissipation factor, 1GHz of 0.01 [-] | ASTM D 2520 B |
Dissipation factor, 1MHz | 23.0 °C | 0.01 [-] Show Material materials with Dissipation factor, 1MHz of 0.01 [-] | IEC 62631-2-1 |
Volume resistivity | 23.0 °C | 1.00E+15 Ω·cm Show Material materials with Volume resistivity of 1.00E+15 Ω·cm | min. | IEC 62631-3-1 |
Rheological Properties
Technological properties
Property | ||
---|---|---|
Fillers | 30% Glass Fiber | |
Processing methods | Drying Recommended: yes, Drying Temperature: 100°C, Drying Time, Dehumidified Dryer: 6-8h, Processing Moisture Content: ≤0.1%, Min. melt temperature: 320°C, Max. melt temperature: 325°C, Min. mold temperature: 90°C, Max. mold temperature: 130°C |