General
Property | Temperature | Value | Comment |
---|---|---|---|
Density | 23.0 °C | 1.41 g/cm³ Show Material materials with Density of 1.41 g/cm³ | ISO 1183 |
Mechanical
Property | Temperature | Value | Comment |
---|---|---|---|
Elastic modulus | 23.0 °C | 11 GPa Show Material materials with Elastic modulus of 11 GPa | ISO 527-1/-2 |
Elongation | 23.0 °C | 2.9 % Show Material materials with Elongation of 2.9 % | ISO 527-1/-2 |
Impact strength, Charpy notched | 23.0 °C | 12 kJ/m² Show Material materials with Impact strength, Charpy notched of 12 kJ/m² | ISO 179/1eA |
Impact strength, Charpy unnotched | 23.0 °C | 70 kJ/m² Show Material materials with Impact strength, Charpy unnotched of 70 kJ/m² | ISO 179/1eU |
Impact strength, Izod unnotched | 23.0 °C | 12 kJ/m² Show Material materials with Impact strength, Izod unnotched of 12 kJ/m² | ISO 180/1A |
Poisson's ratio | 23.0 °C | 0.34 [-] Show Material materials with Poisson's ratio of 0.34 [-] | |
Tensile strength | 23.0 °C | 210 MPa Show Material materials with Tensile strength of 210 MPa | ISO 527-1/-2 |
Thermal
Property | Value | Comment | |
---|---|---|---|
Glass transition temperature | 70 °C Show Material materials with Glass transition temperature of 70 °C | ISO 11357-1/-2 | 18°F/min | |
Heat deflection temperature, 0.45 MPa | 260 °C Show Material materials with Heat deflection temperature, 0.45 MPa of 260 °C | ISO 75-1/-2 | |
Heat deflection temperature, 1.80 MPa | 254 °C Show Material materials with Heat deflection temperature, 1.80 MPa of 254 °C | ISO 75-1/-2 | |
Melting point | 263 °C Show Material materials with Melting point of 263 °C | ISO 11357-1/-3 | 18°F/min | |
Flammability | Oxygen index: 21 %, FMVSS Class: B -, Burning rate, Thickness 1 mm: <80 mm/min |
Electrical
Property | Temperature | Value | Comment |
---|---|---|---|
Volume resistivity | 23.0 °C | 1.00E+15 Ω·cm Show Material materials with Volume resistivity of 1.00E+15 Ω·cm | min. | IEC 62631-3-1 |
Rheological Properties
Technological properties
Property | ||
---|---|---|
Fillers | 35% Glass Fiber | |
Processing methods | Drying Recommended: yes, Drying Temperature: 80°C, Drying Time, Dehumidified Dryer: 2-4h, Processing Moisture Content: ≤0.2%, Melt Temperature Optimum: 295°C, Min. melt temperature: 285°C, Max. melt temperature: 305°C, Max. screw tangential speed: 0.2m/s, Mold Temperature Optimum: 100°C, Min. mold temperature: 70°C, Max. mold temperature: 120°C, Hold pressure range: 50-100MPa, Hold pressure time: 3s/mm, Ejection temperature: 210°C |