General
Property | Temperature | Value | Comment |
---|---|---|---|
Density | 23.0 °C | 1.08 g/cm³ Show Material materials with Density of 1.08 g/cm³ | ISO 1183 |
Water absorption | 23.0 °C | 1.17 % Show Material materials with Water absorption of 1.17 % | Sim. to ISO 62 | Immersion 24h |
Mechanical
Property | Temperature | Value | Comment | ||
---|---|---|---|---|---|
Elastic modulus | 23.0 °C | 1.9 GPa Show Material materials with Elastic modulus of 1.9 GPa | ISO 527-1/-2 | ||
Elongation | 23.0 °C | 74 % Show Material materials with Elongation of 74 % | ISO 527-1/-2 | 50mm/min | ||
Elongation at yield | 23.0 °C | 5 % Show Material materials with Elongation at yield of 5 % | ISO 527-1/-2 | ||
Flexural modulus | 23.0 °C | 1.8 GPa Show Material materials with Flexural modulus of 1.8 GPa | ISO 178 | ||
Hardness, Rockwell R | 23.0 °C | 110 [-] Show Material materials with Hardness, Rockwell R of 110 [-] | ISO 2039-2 | ||
Impact strength, Charpy notched | -40.0 °C | 21 kJ/m² Show Material materials with Impact strength, Charpy notched of 21 kJ/m² | ISO 179/1eA | ||
-6.0 °C | 23 kJ/m² Show Material materials with Impact strength, Charpy notched of 23 kJ/m² | ISO 179/1eA | |||
23.0 °C | 80 kJ/m² Show Material materials with Impact strength, Charpy notched of 80 kJ/m² | ISO 179/1eA | |||
Impact strength, Izod unnotched | -40.0 °C | 21 kJ/m² Show Material materials with Impact strength, Izod unnotched of 21 kJ/m² | ISO 180/1A | ||
23.0 °C | 80 kJ/m² Show Material materials with Impact strength, Izod unnotched of 80 kJ/m² | ISO 180/1A | |||
Poisson's ratio | 23.0 °C | 0.41 [-] Show Material materials with Poisson's ratio of 0.41 [-] | |||
Tensile strength | 23.0 °C | 45 MPa Show Material materials with Tensile strength of 45 MPa | ISO 527-1/-2 | 50mm/min | ||
Yield strength | 23.0 °C | 49 MPa Show Material materials with Yield strength of 49 MPa | ISO 527-1/-2 | ||
Impact strength, Charpy unnotched | No Break @ 23,-6°C, ISO 179/1eU | ||||
Impact strength, Izod notched | No Break @ 23,-30°C, ISO180/1A |
Thermal
Property | Temperature | Value | Comment | ||
---|---|---|---|---|---|
Coefficient of thermal expansion | 23.0 °C | 1.4E-4 1/K Show Material materials with Coefficient of thermal expansion of 1.4E-4 1/K | ISO 11359-1/-2 | ||
Coefficient of thermal expansion, transverse | 23.0 °C | 1.2E-4 1/K Show Material materials with Coefficient of thermal expansion, transverse of 1.2E-4 1/K | ISO 11359-1/-2 | ||
Heat deflection temperature, 0.45 MPa | 155 °C Show Material materials with Heat deflection temperature, 0.45 MPa of 155 °C | ISO 75-1/-2 | |||
Heat deflection temperature, 1.80 MPa | 60 °C Show Material materials with Heat deflection temperature, 1.80 MPa of 60 °C | ISO 75-1/-2 | |||
Melting point | 262 °C Show Material materials with Melting point of 262 °C | ISO 11357-1/-3 | 18°F/min | |||
Relative temperature index, electrical | 125 °C Show Material materials with Relative temperature index, electrical of 125 °C | UL 746B | 120mil | |||
Relative temperature index, mechanical impact | 75 °C Show Material materials with Relative temperature index, mechanical impact of 75 °C | UL 746B | 120mil | |||
Relative temperature index, mechanical strength | 85 °C Show Material materials with Relative temperature index, mechanical strength of 85 °C | UL 746B | 120mil | |||
Flammability | Burning Behav. at 60mil nom. thickn.: HB class, Thickness tested: 1.5 mm, UL recognition: yes -, Burning Behav. at thickness h: HB class, Thickness tested: 0.75 mm, UL recognition: yes -, FMVSS Class: B -, Burning rate, Thickness 1 mm: 26 mm/min |
Electrical
Property | Temperature | Value | Comment |
---|---|---|---|
Comparative tracking index | 23.0 °C | 600 V Show Material materials with Comparative tracking index of 600 V | IEC 60112 |
Dielectric constant, 100Hz | 23.0 °C | 3.4 [-] Show Material materials with Dielectric constant, 100Hz of 3.4 [-] | IEC 62631-2-1 |
Dielectric constant, 1MHz | 23.0 °C | 3.2 [-] Show Material materials with Dielectric constant, 1MHz of 3.2 [-] | IEC 62631-2-1 |
Dielectric strength | 23.0 °C | 26 kV/mm Show Material materials with Dielectric strength of 26 kV/mm | IEC 60243-1 | Short Time, 2mm |
Dissipation factor, 100Hz | 23.0 °C | 5E-3 [-] Show Material materials with Dissipation factor, 100Hz of 5E-3 [-] | IEC 62631-2-1 |
Dissipation factor, 1MHz | 23.0 °C | 0.01 [-] Show Material materials with Dissipation factor, 1MHz of 0.01 [-] | IEC 62631-2-1 |
Volume resistivity | 23.0 °C | 1.00E+15 Ω·cm Show Material materials with Volume resistivity of 1.00E+15 Ω·cm | min. | IEC 62631-3-1 |
Rheological Properties
Technological properties
Property | ||
---|---|---|
Processing methods | Drying Recommended: yes, Drying Temperature: 80°C, Drying Time, Dehumidified Dryer: 2-4h, Processing Moisture Content: ≤0.2%, Melt Temperature Optimum: 290°C, Min. melt temperature: 280°C, Max. melt temperature: 300°C, Max. screw tangential speed: 0.3m/s, Mold Temperature Optimum: 80°C, Min. mold temperature: 50°C, Max. mold temperature: 100°C, Hold pressure range: 50-100MPa, Hold pressure time: 4s/mm, Ejection temperature: 190°C |