Zytel® ST801A NC010A

Alternative and trade names
PA66-HI
Want to keep this datasheet? Save it now in your required format

Description

Zytel® ST801A NC010A is an Unreinforced, Super Toughened, Polyamide 66

Equivalent Materials

This material data has been provided by Matmatch.

All metrics apply to room temperature unless otherwise stated. SI units used unless otherwise stated.
Equivalent standards are similar to one or more standards provided by the supplier. Some equivalent standards may be stricter whereas others may be outside the bounds of the original standard.

Ashby charts

See where falls on the material property chart for against in your materials selection and design process. Our Ashby charts are interactive with more technical data upon clicking. Sign up to get access to this premium feature for free.

Properties

General

PropertyTemperatureValueComment

Density

23.0 °C

1.07 g/cm³

Show Material materials with Density of 1.07 g/cm³

ISO 1183

Water absorption

23.0 °C

1.1 %

Show Material materials with Water absorption of 1.1 %

Sim. to ISO 62 | Immersion 24h

Mechanical

PropertyTemperatureValueComment

Elastic modulus

23.0 °C

2 GPa

Show Material materials with Elastic modulus of 2 GPa

ISO 527-1/-2

Elongation

23.0 °C

500 %

Show Material materials with Elongation of 500 %

min. | ISO 527-1/-2

Flexural modulus

23.0 °C

1.8 GPa

Show Material materials with Flexural modulus of 1.8 GPa

ISO 178

Impact strength, Charpy notched

-6.0 °C

20 kJ/m²

Show Material materials with Impact strength, Charpy notched of 20 kJ/m²

ISO 179/1eA

23.0 °C

70 kJ/m²

Show Material materials with Impact strength, Charpy notched of 70 kJ/m²

ISO 179/1eA

Impact strength, Izod unnotched

-40.0 °C

20 kJ/m²

Show Material materials with Impact strength, Izod unnotched of 20 kJ/m²

ISO 180/1A

-30.0 °C

15 kJ/m²

Show Material materials with Impact strength, Izod unnotched of 15 kJ/m²

ISO 180/1A

23.0 °C

80 kJ/m²

Show Material materials with Impact strength, Izod unnotched of 80 kJ/m²

ISO 180/1A

Unlock all property charts

Poisson's ratio

23.0 °C

0.4 [-]

Show Material materials with Poisson's ratio of 0.4 [-]

Thermal

PropertyTemperatureValueComment

Coefficient of thermal expansion

23.0 °C

1.4E-4 1/K

Show Material materials with Coefficient of thermal expansion of 1.4E-4 1/K

ASTM E 831 | 55 - 160°C

Coefficient of thermal expansion, transverse

23.0 °C

1.3E-4 1/K

Show Material materials with Coefficient of thermal expansion, transverse of 1.3E-4 1/K

ASTM E 831 | 23 - 55°C

Glass transition temperature

75 °C

Show Material materials with Glass transition temperature of 75 °C

ISO 11357-1/-2 | 18°F/min

Heat deflection temperature, 0.45 MPa

157 °C

Show Material materials with Heat deflection temperature, 0.45 MPa of 157 °C

ISO 75-1/-2

Heat deflection temperature, 1.80 MPa

63 °C

Show Material materials with Heat deflection temperature, 1.80 MPa of 63 °C

ISO 75-1/-2

Melting point

262 °C

Show Material materials with Melting point of 262 °C

ISO 11357-1/-3 | 18°F/min

Relative temperature index, electrical

125 °C

Show Material materials with Relative temperature index, electrical of 125 °C

UL 746B | 120mil

Relative temperature index, mechanical impact

75 °C

Show Material materials with Relative temperature index, mechanical impact of 75 °C

UL 746B | 120mil

Relative temperature index, mechanical strength

85 °C

Show Material materials with Relative temperature index, mechanical strength of 85 °C

UL 746B | 120mil

Vicat softening temperature

205 °C

Show Material materials with Vicat softening temperature of 205 °C

ISO 306 | 90°F/h, 11 lbf

Flammability

Burning Behav. at 60mil nom. thickn.: HB class, Thickness tested: 1.5 mm, UL recognition: yes -, Burning Behav. at thickness h: HB class, Thickness tested: 0.81 mm, UL recognition: yes -, Oxygen index: 20 %, FMVSS Class: B -, Burning rate, Thickness 1 mm: <80 mm/min, Hot Wire Ignition, 60mil: 15 s, Hot Wire Ignition, 120mil: 20 s

Electrical

PropertyTemperatureValueComment

Comparative tracking index

23.0 °C

600 V

Show Material materials with Comparative tracking index of 600 V

IEC 60112

Dielectric constant, 100Hz

23.0 °C

3.5 [-]

Show Material materials with Dielectric constant, 100Hz of 3.5 [-]

IEC 62631-2-1

Dielectric constant, 1MHz

23.0 °C

3.3 [-]

Show Material materials with Dielectric constant, 1MHz of 3.3 [-]

IEC 62631-2-1

Dielectric strength

23.0 °C

25 kV/mm

Show Material materials with Dielectric strength of 25 kV/mm

IEC 60243-1 | Short Time, 2mm

Dissipation factor, 100Hz

23.0 °C

5E-3 [-]

Show Material materials with Dissipation factor, 100Hz of 5E-3 [-]

IEC 62631-2-1

Dissipation factor, 1MHz

23.0 °C

0.01 [-]

Show Material materials with Dissipation factor, 1MHz of 0.01 [-]

IEC 62631-2-1

Volume resistivity

23.0 °C

1.00E+15 Ω·cm

Show Material materials with Volume resistivity of 1.00E+15 Ω·cm

min. | IEC 62631-3-1

Rheological Properties

PropertyTemperatureValueComment

Shrinkage

23.0 °C

1.8 %

Show Material materials with Shrinkage of 1.8 %

ISO 294-4, 2577

Shrinkage, transverse

23.0 °C

1.4 %

Show Material materials with Shrinkage, transverse of 1.4 %

ISO 294-4, 2577

Technological properties

Property
Processing methods

Drying Recommended: yes, Drying Temperature: 80°C, Drying Time, Dehumidified Dryer: 2-4h, Processing Moisture Content: ≤0.2%, Melt Temperature Optimum: 290°C, Min. melt temperature: 280°C, Max. melt temperature: 300°C, Max. screw tangential speed: 0.3m/s, Mold Temperature Optimum: 80°C, Min. mold temperature: 50°C, Max. mold temperature: 100°C, Hold pressure range: 50-100MPa, Hold pressure time: 4s/mm, Ejection temperature: 190°C