General
Property | Temperature | Value | Comment |
---|---|---|---|
Density | 23.0 °C | 1.41 g/cm³ Show Material materials with Density of 1.41 g/cm³ | ISO 1183 |
Mechanical
Property | Temperature | Value | Comment |
---|---|---|---|
Elastic modulus | 23.0 °C | 11 GPa Show Material materials with Elastic modulus of 11 GPa | ISO 527-1/-2 |
Elongation | 23.0 °C | 3.2 % Show Material materials with Elongation of 3.2 % | ISO 527-1/-2 |
Flexural modulus | 23.0 °C | 10 GPa Show Material materials with Flexural modulus of 10 GPa | ISO 178 |
Impact strength, Charpy notched | -40.0 °C | 11 kJ/m² Show Material materials with Impact strength, Charpy notched of 11 kJ/m² | ISO 179/1eA |
23.0 °C | 13 kJ/m² Show Material materials with Impact strength, Charpy notched of 13 kJ/m² | ISO 179/1eA | |
Impact strength, Charpy unnotched | -6.0 °C | 80 kJ/m² Show Material materials with Impact strength, Charpy unnotched of 80 kJ/m² | ISO 179/1eU |
23.0 °C | 90 kJ/m² Show Material materials with Impact strength, Charpy unnotched of 90 kJ/m² | ISO 179/1eU | |
Poisson's ratio | 23.0 °C | 0.34 [-] Show Material materials with Poisson's ratio of 0.34 [-] | |
Tensile strength | 23.0 °C | 200 MPa Show Material materials with Tensile strength of 200 MPa | ISO 527-1/-2 |
Thermal
Property | Temperature | Value | Comment | ||
---|---|---|---|---|---|
Coefficient of thermal expansion | 23.0 °C | 1.9E-5 1/K Show Material materials with Coefficient of thermal expansion of 1.9E-5 1/K | ISO 11359-1/-2 | ||
Coefficient of thermal expansion, transverse | 23.0 °C | 6E-5 1/K Show Material materials with Coefficient of thermal expansion, transverse of 6E-5 1/K | ISO 11359-1/-2 | ||
Glass transition temperature | 65 °C Show Material materials with Glass transition temperature of 65 °C | ISO 11357-1/-2 | 18°F/min | |||
Heat deflection temperature, 1.80 MPa | 250 °C Show Material materials with Heat deflection temperature, 1.80 MPa of 250 °C | ISO 75-1/-2 | |||
Melting point | 258 °C Show Material materials with Melting point of 258 °C | ISO 11357-1/-3 | 18°F/min | |||
Specific heat capacity | 23.0 °C | 2050 J/(kg·K) Show Material materials with Specific heat capacity of 2050 J/(kg·K) | of melt | ||
Flammability | FMVSS Class: B -, Burning rate, Thickness 1 mm: 33 mm/min |
Rheological Properties
Technological properties
Property | ||
---|---|---|
Fillers | 35% Glass Fiber | |
Processing methods | Drying Recommended: yes, Drying Temperature: 80°C, Drying Time, Dehumidified Dryer: 2-4h, Processing Moisture Content: ≤0.2%, Melt Temperature Optimum: 285°C, Min. melt temperature: 275°C, Max. melt temperature: 295°C, Mold Temperature Optimum: 100°C, Min. mold temperature: 70°C, Max. mold temperature: 120°C, Ejection temperature: 200°C |