Zytel® 77G33L BK031

Alternative and trade names
PA612-GF33
Want to keep this datasheet? Save it now in your required format

Description

DuPont™ Zytel® LCPA long chain polyamide resins provide an innovative and growing portfolio of flexible polymers with excellent thermal, chemical, and hydrolysis resistance. The diverse selection of Zytel® LCPA grades is targeted for a range of performance characteristics, balancing temperature resistance, flexibility and low permeation.Zytel® 77G33L BK031 is a 33% glass fiber reinforced, black polyamide 612 resin for injection molding.

Equivalent Materials

This material data has been provided by Matmatch.

"Typical" values were obtained via a literature search. "Predicted" values were imputed via artificial intelligence technology. While we have placed significant efforts in ensuring data accuracy, "typical" and "predicted" data should be considered indicative and verified by appropriate material testing. Please do contact us if additional information on the the predicted data method is required.
All metrics apply to room temperature unless otherwise stated. SI units used unless otherwise stated.
Equivalent standards are similar to one or more standards provided by the supplier. Some equivalent standards may be stricter whereas others may be outside the bounds of the original standard.

Ashby charts

See where falls on the material property chart for against in your materials selection and design process. Our Ashby charts are interactive with more technical data upon clicking. Sign up to get access to this premium feature for free.

Properties

General

PropertyTemperatureValueComment

Density

23.0 °C

1.32 g/cm³

Show Material materials with Density of 1.32 g/cm³

ISO 1183

Water absorption

23.0 °C

0.1 %

Show Material materials with Water absorption of 0.1 %

Sim. to ISO 62 | Immersion 24h

Mechanical

PropertyTemperatureValueComment

Elastic modulus

23.0 °C

9.5 GPa

Show Material materials with Elastic modulus of 9.5 GPa

ISO 527-1/-2

Elongation

23.0 °C

3 %

Show Material materials with Elongation of 3 %

ISO 527-1/-2

Flexural modulus

23.0 °C

8.5 GPa

Show Material materials with Flexural modulus of 8.5 GPa

ISO 178

Flexural strength

23.0 °C

250 MPa

Show Material materials with Flexural strength of 250 MPa

ISO 178

Impact strength, Charpy notched

-40.0 °C

12 kJ/m²

Show Material materials with Impact strength, Charpy notched of 12 kJ/m²

ISO 179/1eA

23.0 °C

13 kJ/m²

Show Material materials with Impact strength, Charpy notched of 13 kJ/m²

ISO 179/1eA

Impact strength, Izod notched

23.0 °C

60 kJ/m²

Show Material materials with Impact strength, Izod notched of 60 kJ/m²

ISO 180/1U

Impact strength, Izod unnotched

-40.0 °C

11 kJ/m²

Show Material materials with Impact strength, Izod unnotched of 11 kJ/m²

ISO 180/1A

23.0 °C

13 kJ/m²

Show Material materials with Impact strength, Izod unnotched of 13 kJ/m²

ISO 180/1A

Unlock all property charts

Poisson's ratio

23.0 °C

0.34 [-]

Show Material materials with Poisson's ratio of 0.34 [-]

Tensile strength

23.0 °C

170 MPa

Show Material materials with Tensile strength of 170 MPa

ISO 527-1/-2

Thermal

PropertyTemperatureValueComment

Coefficient of thermal expansion

23.0 °C

1.4E-5 1/K

Show Material materials with Coefficient of thermal expansion of 1.4E-5 1/K

ISO 11359-1/-2 | 23 - 55°C

Coefficient of thermal expansion, transverse

23.0 °C

1.6E-4 1/K

Show Material materials with Coefficient of thermal expansion, transverse of 1.6E-4 1/K

ISO 11359-1/-2 | 55 - 160°C

Glass transition temperature

65 °C

Show Material materials with Glass transition temperature of 65 °C

ISO 11357-1/-2 | 18°F/min

Heat deflection temperature, 1.80 MPa

200 °C

Show Material materials with Heat deflection temperature, 1.80 MPa of 200 °C

ISO 75-1/-2

Melting point

218 °C

Show Material materials with Melting point of 218 °C

ISO 11357-1/-3 | 18°F/min

Relative temperature index, electrical

120 °C

Show Material materials with Relative temperature index, electrical of 120 °C

UL 746B | 120mil

Relative temperature index, mechanical strength

120 °C

Show Material materials with Relative temperature index, mechanical strength of 120 °C

UL 746B | 120mil

Flammability

Burning Behav. at 60mil nom. thickn.: HB class, Thickness tested: 1.5 mm, UL recognition: yes -, Burning Behav. at thickness h: HB class, Thickness tested: 0.71 mm, UL recognition: yes -, Glow Wire Flammability Index, 30mil: 675 °C, Glow Wire Flammability Index, 60mil: 675 °C, Glow Wire Flammability Index, 120mil: 700 °C, Glow Wire Ignition Temperature, 30mil: 700 °C, Glow Wire Ignition Temperature, 60mil: 700 °C, Glow Wire Ignition Temperature, 120mil: 725 °C, FMVSS Class: B -, Burning rate, Thickness 1 mm: 23 mm/min

Electrical

PropertyTemperatureValueComment

Comparative tracking index

23.0 °C

600 V

Show Material materials with Comparative tracking index of 600 V

IEC 60112

Rheological Properties

PropertyTemperatureValueComment

Shrinkage

23.0 °C

0.3 %

Show Material materials with Shrinkage of 0.3 %

ISO 294-4, 2577

Shrinkage, transverse

23.0 °C

0.9 %

Show Material materials with Shrinkage, transverse of 0.9 %

ISO 294-4, 2577

Technological properties

Property
Fillers

33% Glass Fiber

Processing methods

Drying Recommended: yes, Drying Temperature: 80°C, Drying Time, Dehumidified Dryer: 2-4h, Processing Moisture Content: ≤0.2%, Melt Temperature Optimum: 290°C, Min. melt temperature: 280°C, Max. melt temperature: 300°C, Max. screw tangential speed: 0.2m/s, Mold Temperature Optimum: 100°C, Min. mold temperature: 70°C, Max. mold temperature: 120°C, Hold pressure range: 50-100MPa, Hold pressure time: 3s/mm, Ejection temperature: 210°C