General
Property | Temperature | Value | Comment |
---|---|---|---|
Density | 23.0 °C | 1.19 g/cm³ Show Material materials with Density of 1.19 g/cm³ | ISO 1183 |
Water absorption | 23.0 °C | 6.2 % Show Material materials with Water absorption of 6.2 % | Sim. to ISO 62 | 80mil |
Mechanical
Property | Temperature | Value | Comment |
---|---|---|---|
Elastic modulus | 23.0 °C | 4.8 GPa Show Material materials with Elastic modulus of 4.8 GPa | ISO 527-1/-2 |
Elongation | 23.0 °C | 3.8 % Show Material materials with Elongation of 3.8 % | ISO 527-1/-2 |
Flexural modulus | 23.0 °C | 4.4 GPa Show Material materials with Flexural modulus of 4.4 GPa | ISO 178 |
Impact strength, Charpy notched | -6.0 °C | 10 kJ/m² Show Material materials with Impact strength, Charpy notched of 10 kJ/m² | ISO 179/1eA |
23.0 °C | 13 kJ/m² Show Material materials with Impact strength, Charpy notched of 13 kJ/m² | ISO 179/1eA | |
Impact strength, Charpy unnotched | -6.0 °C | 90 kJ/m² Show Material materials with Impact strength, Charpy unnotched of 90 kJ/m² | ISO 179/1eU |
23.0 °C | 70 kJ/m² Show Material materials with Impact strength, Charpy unnotched of 70 kJ/m² | ISO 179/1eU | |
Impact strength, Izod unnotched | -40.0 °C | 6 kJ/m² Show Material materials with Impact strength, Izod unnotched of 6 kJ/m² | ISO 180/1A |
23.0 °C | 13 kJ/m² Show Material materials with Impact strength, Izod unnotched of 13 kJ/m² | ISO 180/1A | |
Poisson's ratio | 23.0 °C | 0.36 [-] Show Material materials with Poisson's ratio of 0.36 [-] | |
Tensile strength | 23.0 °C | 108 MPa Show Material materials with Tensile strength of 108 MPa | ISO 527-1/-2 |
Thermal
Property | Temperature | Value | Comment | ||
---|---|---|---|---|---|
Coefficient of thermal expansion | 23.0 °C | 4E-5 1/K Show Material materials with Coefficient of thermal expansion of 4E-5 1/K | ISO 11359-1/-2 | ||
Coefficient of thermal expansion, transverse | 23.0 °C | 1.2E-4 1/K Show Material materials with Coefficient of thermal expansion, transverse of 1.2E-4 1/K | ISO 11359-1/-2 | ||
Heat deflection temperature, 0.45 MPa | 258 °C Show Material materials with Heat deflection temperature, 0.45 MPa of 258 °C | ISO 75-1/-2 | |||
Heat deflection temperature, 1.80 MPa | 240 °C Show Material materials with Heat deflection temperature, 1.80 MPa of 240 °C | ISO 75-1/-2 | |||
Melting point | 263 °C Show Material materials with Melting point of 263 °C | ISO 11357-1/-3 | 18°F/min | |||
Specific heat capacity | 23.0 °C | 1240 J/(kg·K) Show Material materials with Specific heat capacity of 1240 J/(kg·K) | of solid | ||
Thermal diffusivity | 23.0 °C | 0 mm²/s Show Material materials with Thermal diffusivity of 0 mm²/s | |||
Vicat softening temperature | 215 °C Show Material materials with Vicat softening temperature of 215 °C | ISO 306 | 90°F/h, 11 lbf | |||
Flammability | Burning Behav. at 60mil nom. thickn.: HB class, Thickness tested: 1.5 mm, Burning Behav. at thickness h: HB class, Thickness tested: 0.75 mm, Oxygen index: 21 %, FMVSS Class: B -, Burning rate, Thickness 1 mm: 44 mm/min |
Electrical
Property | Temperature | Value | Comment |
---|---|---|---|
Comparative tracking index | 23.0 °C | 600 V Show Material materials with Comparative tracking index of 600 V | IEC 60112 |
Dielectric constant, 100Hz | 23.0 °C | 3.8 [-] Show Material materials with Dielectric constant, 100Hz of 3.8 [-] | IEC 62631-2-1 |
Dielectric constant, 1MHz | 23.0 °C | 3.5 [-] Show Material materials with Dielectric constant, 1MHz of 3.5 [-] | IEC 62631-2-1 |
Dielectric strength | 23.0 °C | 36 kV/mm Show Material materials with Dielectric strength of 36 kV/mm | IEC 60243-1 |
Dissipation factor, 100Hz | 23.0 °C | 0.03 [-] Show Material materials with Dissipation factor, 100Hz of 0.03 [-] | IEC 62631-2-1 |
Dissipation factor, 1MHz | 23.0 °C | 0.06 [-] Show Material materials with Dissipation factor, 1MHz of 0.06 [-] | IEC 62631-2-1 |
Volume resistivity | 23.0 °C | 1.00E+15 Ω·cm Show Material materials with Volume resistivity of 1.00E+15 Ω·cm | min. | IEC 62631-3-1 |
Rheological Properties
Technological properties
Property | ||
---|---|---|
Fillers | 14% Glass Fiber | |
Processing methods | Drying Recommended: yes, Drying Temperature: 80°C, Drying Time, Dehumidified Dryer: 2-4h, Processing Moisture Content: ≤0.2%, Melt Temperature Optimum: 295°C, Min. melt temperature: 285°C, Max. melt temperature: 305°C, Max. screw tangential speed: 0.2m/s, Mold Temperature Optimum: 80°C, Min. mold temperature: 50°C, Max. mold temperature: 100°C, Hold pressure range: 50-100MPa, Hold pressure time: 3s/mm, Ejection temperature: 210°C |