General
Property | Temperature | Value | Comment |
---|---|---|---|
Density | 23.0 °C | 1.34 g/cm³ Show Material materials with Density of 1.34 g/cm³ | ISO 1183 |
Water absorption | 23.0 °C | 6.2 % Show Material materials with Water absorption of 6.2 % | Sim. to ISO 62 | 80mil |
Mechanical
Property | Temperature | Value | Comment |
---|---|---|---|
Elastic modulus | 23.0 °C | 9 GPa Show Material materials with Elastic modulus of 9 GPa | ISO 527-1/-2 |
Elongation | 23.0 °C | 3.5 % Show Material materials with Elongation of 3.5 % | ISO 527-1/-2 |
Flexural modulus | 23.0 °C | 7.8 GPa Show Material materials with Flexural modulus of 7.8 GPa | ISO 178 |
Impact strength, Charpy notched | -6.0 °C | 13 kJ/m² Show Material materials with Impact strength, Charpy notched of 13 kJ/m² | ISO 179/1eA |
23.0 °C | 20 kJ/m² Show Material materials with Impact strength, Charpy notched of 20 kJ/m² | ISO 179/1eA | |
Impact strength, Charpy unnotched | -6.0 °C | 100 kJ/m² Show Material materials with Impact strength, Charpy unnotched of 100 kJ/m² | ISO 179/1eU |
23.0 °C | 100 kJ/m² Show Material materials with Impact strength, Charpy unnotched of 100 kJ/m² | ISO 179/1eU | |
Impact strength, Izod notched | 23.0 °C | 80 kJ/m² Show Material materials with Impact strength, Izod notched of 80 kJ/m² | ISO 180/1U |
Impact strength, Izod unnotched | -30.0 °C | 12 kJ/m² Show Material materials with Impact strength, Izod unnotched of 12 kJ/m² | ISO 180/1A |
23.0 °C | 17 kJ/m² Show Material materials with Impact strength, Izod unnotched of 17 kJ/m² | ISO 180/1A | |
Poisson's ratio | 23.0 °C | 0.34 [-] Show Material materials with Poisson's ratio of 0.34 [-] | |
Tensile strength | 23.0 °C | 160 MPa Show Material materials with Tensile strength of 160 MPa | ISO 527-1/-2 |
Thermal
Property | Temperature | Value | Comment | ||
---|---|---|---|---|---|
Coefficient of thermal expansion | 23.0 °C | 8E-6 1/K Show Material materials with Coefficient of thermal expansion of 8E-6 1/K | ISO 11359-1/-2 | 23 - 55°C | ||
Coefficient of thermal expansion, transverse | 23.0 °C | 1.1E-4 1/K Show Material materials with Coefficient of thermal expansion, transverse of 1.1E-4 1/K | ISO 11359-1/-2 | 55 - 160°C | ||
Glass transition temperature | 60 °C Show Material materials with Glass transition temperature of 60 °C | ISO 11357-1/-2 | 18°F/min | |||
Heat deflection temperature, 0.45 MPa | 221 °C Show Material materials with Heat deflection temperature, 0.45 MPa of 221 °C | ISO 75-1/-2 | |||
Heat deflection temperature, 1.80 MPa | 210 °C Show Material materials with Heat deflection temperature, 1.80 MPa of 210 °C | ISO 75-1/-2 | |||
Melting point | 221 °C Show Material materials with Melting point of 221 °C | ISO 11357-1/-3 | 18°F/min | |||
Relative temperature index, electrical | 65 °C Show Material materials with Relative temperature index, electrical of 65 °C | UL 746B | 60mil | |||
Relative temperature index, mechanical impact | 65 °C Show Material materials with Relative temperature index, mechanical impact of 65 °C | UL 746B | 60mil | |||
Relative temperature index, mechanical strength | 65 °C Show Material materials with Relative temperature index, mechanical strength of 65 °C | UL 746B | 60mil | |||
Specific heat capacity | 23.0 °C | 2200 J/(kg·K) Show Material materials with Specific heat capacity of 2200 J/(kg·K) | of melt | ||
Vicat softening temperature | 215 °C Show Material materials with Vicat softening temperature of 215 °C | ISO 306 | 90°F/h, 11 lbf | |||
Flammability | Burning Behav. at 60mil nom. thickn.: HB class, Thickness tested: 1.5 mm, UL recognition: yes -, Glow Wire Flammability Index, 40mil: 700 °C, Glow Wire Flammability Index, 80mil: 700 °C, Glow Wire Flammability Index, 120mil: 750 °C, Glow Wire Ignition Temperature, 40mil: 700 °C, Glow Wire Ignition Temperature, 80mil: 700 °C, Glow Wire Ignition Temperature, 120mil: 700 °C, FMVSS Class: B -, Burning rate, Thickness 1 mm: 22 mm/min |
Electrical
Property | Temperature | Value | Comment |
---|---|---|---|
Comparative tracking index | 23.0 °C | 550 V Show Material materials with Comparative tracking index of 550 V | IEC 60112 |
Rheological Properties
Technological properties
Property | ||
---|---|---|
Fillers | 30% Glass Fiber | |
Processing methods | Drying Recommended: yes, Drying Temperature: 80°C, Drying Time, Dehumidified Dryer: 2-4h, Processing Moisture Content: ≤0.2%, Melt Temperature Optimum: 270°C, Min. melt temperature: 260°C, Max. melt temperature: 280°C, Max. screw tangential speed: 0.2m/s, Mold Temperature Optimum: 80°C, Min. mold temperature: 50°C, Max. mold temperature: 100°C, Hold pressure range: 50-100MPa, Hold pressure time: 3s/mm |