Zytel® BM7300THS BK317

Alternative and trade names
PA6-HI
Want to keep this datasheet? Save it now in your required format

Description

Common features of Zytel® nylon resin include mechanical and physical properties such as high mechanical strength, excellent balance of stiffness and toughness, good high temperature performance, good electrical and flammability properties, good abrasion and chemical resistance. In addition, Zytel® nylon resins are available in different modified and reinforced grades to create a wide range of products with tailored properties for specific processes and end-uses. Zytel® nylon resin, including most flame retardant grades, offer the ability to be coloured. The good melt stability of Zytel® nylon resin normally enables the recycling of properly handled production waste. If recycling is not possible, DuPont recommends, as the preferred option, incineration with energy recovery (-31kJ/g of base polymer) in appropriately equipped installations. For disposal, local regulations have to be observed.Zytel® nylon resin typically is used in demanding applications in the automotive, furniture, domestic appliances, sporting goods and construction industry.Zytel® BM7300THS is an unreinforced, heat stabilized, lubricated, toughened polyamide 6 for blow molding.

Equivalent Materials

This material data has been provided by Matmatch.

All metrics apply to room temperature unless otherwise stated. SI units used unless otherwise stated.
Equivalent standards are similar to one or more standards provided by the supplier. Some equivalent standards may be stricter whereas others may be outside the bounds of the original standard.

Ashby charts

See where falls on the material property chart for against in your materials selection and design process. Our Ashby charts are interactive with more technical data upon clicking. Sign up to get access to this premium feature for free.

Properties

General

PropertyTemperatureValueComment

Density

23.0 °C

1.09 g/cm³

Show Material materials with Density of 1.09 g/cm³

ISO 1183

Mechanical

PropertyTemperatureValueComment

Elastic modulus

23.0 °C

2.2 GPa

Show Material materials with Elastic modulus of 2.2 GPa

ISO 527-1/-2

Elongation

23.0 °C

500 %

Show Material materials with Elongation of 500 %

min. | ISO 527-1/-2

Elongation at yield

23.0 °C

4.2 %

Show Material materials with Elongation at yield of 4.2 %

ISO 527-1/-2

Impact strength, Charpy notched

-40.0 °C

15 kJ/m²

Show Material materials with Impact strength, Charpy notched of 15 kJ/m²

ISO 179/1eA

-6.0 °C

22 kJ/m²

Show Material materials with Impact strength, Charpy notched of 22 kJ/m²

ISO 179/1eA

23.0 °C

45 kJ/m²

Show Material materials with Impact strength, Charpy notched of 45 kJ/m²

ISO 179/1eA

Impact strength, Izod unnotched

-30.0 °C

18 kJ/m²

Show Material materials with Impact strength, Izod unnotched of 18 kJ/m²

ISO 180/1A

23.0 °C

38 kJ/m²

Show Material materials with Impact strength, Izod unnotched of 38 kJ/m²

ISO 180/1A

Unlock all property charts

Poisson's ratio

23.0 °C

0.39 [-]

Show Material materials with Poisson's ratio of 0.39 [-]

Yield strength

23.0 °C

60 MPa

Show Material materials with Yield strength of 60 MPa

ISO 527-1/-2

Impact strength, Charpy unnotched

No Break @ 23,-6°C, ISO 179/1eA

Thermal

PropertyValueComment

Heat deflection temperature, 0.45 MPa

100 °C

Show Material materials with Heat deflection temperature, 0.45 MPa of 100 °C

ISO 75-1/-2

Heat deflection temperature, 1.80 MPa

52 °C

Show Material materials with Heat deflection temperature, 1.80 MPa of 52 °C

ISO 75-1/-2

Melting point

220 °C

Show Material materials with Melting point of 220 °C

ISO 11357-1/-3 | 18°F/min

Flammability

FMVSS Class: B -, Burning rate, Thickness 1 mm: <80 mm/min

Rheological Properties

PropertyTemperatureValueComment

Melt viscosity

280.0 °C

440 Pa·s

Show Material materials with Melt viscosity of 440 Pa·s

ISO 11443 | @ 1000 sec-1, 280°C

Shrinkage

23.0 °C

1.1 %

Show Material materials with Shrinkage of 1.1 %

ISO 294-4, 2577

Shrinkage, transverse

23.0 °C

1.1 %

Show Material materials with Shrinkage, transverse of 1.1 %

ISO 294-4, 2577

Technological properties

Property
Processing methods

Drying Recommended: yes, Drying Temperature: 80°C, Drying Time, Dehumidified Dryer: 2-4h, Processing Moisture Content: ≤0.2%, Melt Temperature Optimum: 270°C, Min. melt temperature: 260°C, Max. melt temperature: 280°C, Max. screw tangential speed: 0.2m/s, Mold Temperature Optimum: 70°C, Min. mold temperature: 50°C, Max. mold temperature: 100°C, Hold pressure range: 50-100MPa, Hold pressure time: 3s/mm