General
Property | Temperature | Value | Comment |
---|---|---|---|
Density | 23.0 °C | 1.06 g/cm³ Show Material materials with Density of 1.06 g/cm³ | ISO 1183 |
Mechanical
Property | Temperature | Value | Comment |
---|---|---|---|
Elastic modulus | 23.0 °C | 1.8 GPa Show Material materials with Elastic modulus of 1.8 GPa | ISO 527-1/-2 |
Elongation | 23.0 °C | 45 % Show Material materials with Elongation of 45 % | ISO 527-1/-2 |
Elongation at yield | 23.0 °C | 4 % Show Material materials with Elongation at yield of 4 % | ISO 527-1/-2 |
Flexural modulus | 23.0 °C | 1.8 GPa Show Material materials with Flexural modulus of 1.8 GPa | ISO 178 |
Impact strength, Charpy notched | -40.0 °C | 16 kJ/m² Show Material materials with Impact strength, Charpy notched of 16 kJ/m² | ISO 179/1eA |
-6.0 °C | 17 kJ/m² Show Material materials with Impact strength, Charpy notched of 17 kJ/m² | ISO 179/1eA | |
23.0 °C | 77 kJ/m² Show Material materials with Impact strength, Charpy notched of 77 kJ/m² | ISO 179/1eA | |
Impact strength, Izod unnotched | -40.0 °C | 13 kJ/m² Show Material materials with Impact strength, Izod unnotched of 13 kJ/m² | ISO 180/1A |
-30.0 °C | 16 kJ/m² Show Material materials with Impact strength, Izod unnotched of 16 kJ/m² | ISO 180/1A | |
23.0 °C | 57 kJ/m² Show Material materials with Impact strength, Izod unnotched of 57 kJ/m² | ISO 180/1A | |
Poisson's ratio | 23.0 °C | 0.41 [-] Show Material materials with Poisson's ratio of 0.41 [-] | |
Yield strength | 23.0 °C | 48 MPa Show Material materials with Yield strength of 48 MPa | ISO 527-1/-2 |
Thermal
Property | Value | Comment | |
---|---|---|---|
Heat deflection temperature, 0.45 MPa | 88 °C Show Material materials with Heat deflection temperature, 0.45 MPa of 88 °C | ISO 75-1/-2 | |
Heat deflection temperature, 1.80 MPa | 45 °C Show Material materials with Heat deflection temperature, 1.80 MPa of 45 °C | ISO 75-1/-2 | |
Melting point | 221 °C Show Material materials with Melting point of 221 °C | ISO 11357-1/-3 | 18°F/min | |
Flammability | FMVSS Class: B -, Burning rate, Thickness 1 mm: <80 mm/min |
Rheological Properties
Technological properties
Property | ||
---|---|---|
Processing methods | Drying Recommended: yes, Drying Temperature: 80°C, Drying Time, Dehumidified Dryer: 2-4h, Processing Moisture Content: ≤0.2%, Melt Temperature Optimum: 270°C, Min. melt temperature: 260°C, Max. melt temperature: 280°C, Max. screw tangential speed: 0.3m/s, Mold Temperature Optimum: 70°C, Min. mold temperature: 50°C, Max. mold temperature: 90°C, Hold pressure range: 50-100MPa, Hold pressure time: 4s/mm, Ejection temperature: 140°C |