Zytel® FE5382 BK276

Alternative and trade names
PA612-GF33
Want to keep this datasheet? Save it now in your required format

Description

DuPont™ Zytel® LCPA long chain polyamide resins provide an innovative and growing portfolio of flexible polymers with excellent thermal, chemical, and hydrolysis resistance. The diverse selection of Zytel® LCPA grades is targeted for a range of performance characteristics, balancing temperature resistance, flexibility and low permeation.Zytel® FE5382 BK276 is a 33% glass fiber reinforced, heat stabilized, black polyamide 612 resin developed for electrical bobbins and encapsulation applications.

Equivalent Materials

This material data has been provided by Matmatch.

All metrics apply to room temperature unless otherwise stated. SI units used unless otherwise stated.
Equivalent standards are similar to one or more standards provided by the supplier. Some equivalent standards may be stricter whereas others may be outside the bounds of the original standard.

Ashby charts

See where falls on the material property chart for against in your materials selection and design process. Our Ashby charts are interactive with more technical data upon clicking. Sign up to get access to this premium feature for free.

Properties

General

PropertyTemperatureValueComment

Density

23.0 °C

1.32 g/cm³

Show Material materials with Density of 1.32 g/cm³

ISO 1183

Water absorption

23.0 °C

1.8 %

Show Material materials with Water absorption of 1.8 %

Sim. to ISO 62 | 80mil

Mechanical

PropertyTemperatureValueComment

Elastic modulus

23.0 °C

10 GPa

Show Material materials with Elastic modulus of 10 GPa

ISO 527-1/-2

Elongation

23.0 °C

3 %

Show Material materials with Elongation of 3 %

ISO 527-1/-2

Flexural modulus

23.0 °C

9 GPa

Show Material materials with Flexural modulus of 9 GPa

ISO 178

Flexural strength

23.0 °C

250 MPa

Show Material materials with Flexural strength of 250 MPa

ISO 178

Impact strength, Charpy notched

-40.0 °C

10 kJ/m²

Show Material materials with Impact strength, Charpy notched of 10 kJ/m²

ISO 179/1eA

23.0 °C

12 kJ/m²

Show Material materials with Impact strength, Charpy notched of 12 kJ/m²

ISO 179/1eA

Impact strength, Izod notched

23.0 °C

60 kJ/m²

Show Material materials with Impact strength, Izod notched of 60 kJ/m²

ISO 180/1U

Impact strength, Izod unnotched

-40.0 °C

10 kJ/m²

Show Material materials with Impact strength, Izod unnotched of 10 kJ/m²

ISO 180/1A

23.0 °C

11 kJ/m²

Show Material materials with Impact strength, Izod unnotched of 11 kJ/m²

ISO 180/1A

Unlock all property charts

Poisson's ratio

23.0 °C

0.34 [-]

Show Material materials with Poisson's ratio of 0.34 [-]

Tensile strength

23.0 °C

180 MPa

Show Material materials with Tensile strength of 180 MPa

ISO 527-1/-2

Thermal

PropertyTemperatureValueComment

Coefficient of thermal expansion

23.0 °C

1.4E-5 1/K

Show Material materials with Coefficient of thermal expansion of 1.4E-5 1/K

ISO 11359-1/-2 | 23 - 55°C

Coefficient of thermal expansion, transverse

23.0 °C

1.6E-4 1/K

Show Material materials with Coefficient of thermal expansion, transverse of 1.6E-4 1/K

ISO 11359-1/-2 | 55 - 160°C

Heat deflection temperature, 0.45 MPa

216 °C

Show Material materials with Heat deflection temperature, 0.45 MPa of 216 °C

ISO 75-1/-2

Heat deflection temperature, 1.80 MPa

200 °C

Show Material materials with Heat deflection temperature, 1.80 MPa of 200 °C

ISO 75-1/-2

Melting point

218 °C

Show Material materials with Melting point of 218 °C

ISO 11357-1/-3 | 18°F/min

Relative temperature index, electrical

65 °C

Show Material materials with Relative temperature index, electrical of 65 °C

UL 746B | 120mil

Relative temperature index, mechanical impact

65 °C

Show Material materials with Relative temperature index, mechanical impact of 65 °C

UL 746B | 120mil

Relative temperature index, mechanical strength

65 °C

Show Material materials with Relative temperature index, mechanical strength of 65 °C

UL 746B | 120mil

Specific heat capacity

23.0 °C

2130 J/(kg·K)

Show Material materials with Specific heat capacity of 2130 J/(kg·K)

of melt

Flammability

Burning Behav. at 60mil nom. thickn.: HB class, Thickness tested: 1.5 mm, UL recognition: yes -, Burning Behav. at thickness h: HB class, Thickness tested: 0.75 mm, UL recognition: yes -, Glow Wire Flammability Index, 40mil: 725 °C, Glow Wire Flammability Index, 80mil: 750 °C, Glow Wire Flammability Index, 120mil: 750 °C, Glow Wire Ignition Temperature, 40mil: 725 °C, Glow Wire Ignition Temperature, 80mil: 750 °C, Glow Wire Ignition Temperature, 120mil: 750 °C, FMVSS Class: B -, Burning rate, Thickness 1 mm: 23 mm/min

Electrical

PropertyTemperatureValueComment

Comparative tracking index

23.0 °C

600 V

Show Material materials with Comparative tracking index of 600 V

IEC 60112

Dielectric strength

23.0 °C

34 kV/mm

Show Material materials with Dielectric strength of 34 kV/mm

IEC 60243-1

Volume resistivity

23.0 °C

6.00E+14 Ω·cm

Show Material materials with Volume resistivity of 6.00E+14 Ω·cm

IEC 62631-3-1

Rheological Properties

PropertyTemperatureValueComment

Shrinkage

23.0 °C

0.3 %

Show Material materials with Shrinkage of 0.3 %

ISO 294-4, 2577

Shrinkage, transverse

23.0 °C

0.9 %

Show Material materials with Shrinkage, transverse of 0.9 %

ISO 294-4, 2577

Technological properties

Property
Fillers

33% Glass Fiber

Processing methods

Drying Recommended: yes, Drying Time, Dehumidified Dryer: 2-4h, Processing Moisture Content: ≤0.15%, Melt Temperature Optimum: 290°C, Min. melt temperature: 280°C, Max. melt temperature: 300°C, Min. mold temperature: 70°C, Max. mold temperature: 120°C