Property | Temperature | Value | Comment |
---|---|---|---|
Density | 23.0 °C | 1.41 g/cm³ Show Material materials with Density of 1.41 g/cm³ | ISO 1183 |
Water absorption | 23.0 °C | 5.4 % Show Material materials with Water absorption of 5.4 % | Sim. to ISO 62 | 80mil |
Mechanical
Property | Temperature | Value | Comment |
---|---|---|---|
Elastic modulus | 23.0 °C | 12 GPa Show Material materials with Elastic modulus of 12 GPa | ISO 527-1/-2 |
Elongation | 23.0 °C | 3.5 % Show Material materials with Elongation of 3.5 % | ISO 527-1/-2 |
Impact strength, Charpy notched | -6.0 °C | 17 kJ/m² Show Material materials with Impact strength, Charpy notched of 17 kJ/m² | ISO 179/1eA |
23.0 °C | 24 kJ/m² Show Material materials with Impact strength, Charpy notched of 24 kJ/m² | ISO 179/1eA | |
Impact strength, Charpy unnotched | -6.0 °C | 118 kJ/m² Show Material materials with Impact strength, Charpy unnotched of 118 kJ/m² | ISO 179/1eU |
23.0 °C | 110 kJ/m² Show Material materials with Impact strength, Charpy unnotched of 110 kJ/m² | ISO 179/1eU | |
Impact strength, Izod unnotched | -30.0 °C | 19 kJ/m² Show Material materials with Impact strength, Izod unnotched of 19 kJ/m² | ISO 180/1A |
23.0 °C | 24 kJ/m² Show Material materials with Impact strength, Izod unnotched of 24 kJ/m² | ISO 180/1A | |
Poisson's ratio | 23.0 °C | 0.33 [-] Show Material materials with Poisson's ratio of 0.33 [-] | |
Tensile strength | 23.0 °C | 190 MPa Show Material materials with Tensile strength of 190 MPa | ISO 527-1/-2 |
Thermal
Property | Value | Comment | |
---|---|---|---|
Heat deflection temperature, 1.80 MPa | 212 °C Show Material materials with Heat deflection temperature, 1.80 MPa of 212 °C | ISO 75-1/-2 | |
Melting point | 221 °C Show Material materials with Melting point of 221 °C | ISO 11357-1/-3 | 18°F/min | |
Flammability | FMVSS Class: B -, Burning rate, Thickness 1 mm: 33 mm/min |
Rheological Properties
Technological properties
Property | ||
---|---|---|
Fillers | 40% Glass Fiber | |
Processing methods | Drying Recommended: yes, Drying Temperature: 80°C, Drying Time, Dehumidified Dryer: 2-4h, Processing Moisture Content: ≤0.2%, Melt Temperature Optimum: 270°C, Min. melt temperature: 260°C, Max. melt temperature: 280°C, Max. screw tangential speed: 0.2m/s, Mold Temperature Optimum: 100°C, Min. mold temperature: 50°C, Max. mold temperature: 90°C, Hold pressure range: 50-100MPa, Hold pressure time: 3s/mm |