Zytel® FG151L NC010

Alternative and trade names
PA612
Want to keep this datasheet? Save it now in your required format

Description

DuPont™ Zytel® LCPA long chain polyamide resins provide an innovative and growing portfolio of flexible polymers with excellent thermal, chemical, and hydrolysis resistance. The diverse selection of Zytel® LCPA grades is targeted for a range of performance characteristics, balancing temperature resistance, flexibility and low permeation.Zytel® FG151L is a lubricated polyamide 612 resin for injection molding. It has been developed for consideration into applications in contact with food. FOOD CONTACTThis product is manufactured according to Good Manufacturing Practice (GMP) principles and generally accepted in food contact applications in Europe and the USA when meeting applicable use conditions. For details, individual compliance statements are available from your DuPont representative.

Equivalent Materials

This material data has been provided by Matmatch.

All metrics apply to room temperature unless otherwise stated. SI units used unless otherwise stated.
Equivalent standards are similar to one or more standards provided by the supplier. Some equivalent standards may be stricter whereas others may be outside the bounds of the original standard.

Ashby charts

See where falls on the material property chart for against in your materials selection and design process. Our Ashby charts are interactive with more technical data upon clicking. Sign up to get access to this premium feature for free.

Properties

General

PropertyTemperatureValueComment

Density

23.0 °C

1.06 g/cm³

Show Material materials with Density of 1.06 g/cm³

ISO 1183

Water absorption

23.0 °C

3 %

Show Material materials with Water absorption of 3 %

Sim. to ISO 62 | 80mil

Mechanical

PropertyTemperatureValueComment

Elastic modulus

23.0 °C

2.4 GPa

Show Material materials with Elastic modulus of 2.4 GPa

ISO 527-1/-2

Elongation

23.0 °C

17 %

Show Material materials with Elongation of 17 %

ISO 527-1/-2

Elongation at yield

23.0 °C

4.5 %

Show Material materials with Elongation at yield of 4.5 %

ISO 527-1/-2

Flexural modulus

23.0 °C

2.1 GPa

Show Material materials with Flexural modulus of 2.1 GPa

ISO 178

Impact strength, Charpy notched

-6.0 °C

3.5 kJ/m²

Show Material materials with Impact strength, Charpy notched of 3.5 kJ/m²

ISO 179/1eA

23.0 °C

3.5 kJ/m²

Show Material materials with Impact strength, Charpy notched of 3.5 kJ/m²

ISO 179/1eA

Poisson's ratio

23.0 °C

0.38 [-]

Show Material materials with Poisson's ratio of 0.38 [-]

Yield strength

23.0 °C

62 MPa

Show Material materials with Yield strength of 62 MPa

ISO 527-1/-2

Impact strength, Charpy unnotched

No Break @ 23,-6°C, ISO 179/1eA

Thermal

PropertyTemperatureValueComment

Coefficient of thermal expansion

23.0 °C

1.6E-4 1/K

Show Material materials with Coefficient of thermal expansion of 1.6E-4 1/K

ISO 11359-1/-2 | 23 - 55°C

Coefficient of thermal expansion, transverse

23.0 °C

1.8E-4 1/K

Show Material materials with Coefficient of thermal expansion, transverse of 1.8E-4 1/K

ISO 11359-1/-2 | 55 - 160°C

Glass transition temperature

65 °C

Show Material materials with Glass transition temperature of 65 °C

ISO 11357-1/-2 | 18°F/min

Heat deflection temperature, 0.45 MPa

135 °C

Show Material materials with Heat deflection temperature, 0.45 MPa of 135 °C

ISO 75-1/-2

Heat deflection temperature, 1.80 MPa

62 °C

Show Material materials with Heat deflection temperature, 1.80 MPa of 62 °C

ISO 75-1/-2

Melting point

218 °C

Show Material materials with Melting point of 218 °C

ISO 11357-1/-3 | 18°F/min

Relative temperature index, electrical

105 °C

Show Material materials with Relative temperature index, electrical of 105 °C

UL 746B | 120mil

Relative temperature index, mechanical impact

65 °C

Show Material materials with Relative temperature index, mechanical impact of 65 °C

UL 746B | 120mil

Relative temperature index, mechanical strength

65 °C

Show Material materials with Relative temperature index, mechanical strength of 65 °C

UL 746B | 120mil

Vicat softening temperature

181 °C

Show Material materials with Vicat softening temperature of 181 °C

ISO 306 | 90°F/h, 11 lbf

Flammability

Burning Behav. at 60mil nom. thickn.: V-2 class, Thickness tested: 1.5 mm, UL recognition: yes -, Burning Behav. at thickness h: V-2 class, Thickness tested: 0.86 mm, UL recognition: yes -, FMVSS Class: SE -

Rheological Properties

PropertyTemperatureValueComment

Shrinkage

23.0 °C

1.3 %

Show Material materials with Shrinkage of 1.3 %

ISO 294-4, 2577

Shrinkage, transverse

23.0 °C

1.4 %

Show Material materials with Shrinkage, transverse of 1.4 %

ISO 294-4, 2577

Technological properties

Property
Processing methods

Drying Recommended: yes, Drying Time, Dehumidified Dryer: 2-4h, Processing Moisture Content: ≤0.15%, Melt Temperature Optimum: 250°C, Min. melt temperature: 230°C, Max. melt temperature: 290°C, Min. mold temperature: 50°C, Max. mold temperature: 90°C