Zytel® HTN510EFT NC010 is an unreinforced, toughened, high performance polyamide resin. It is also a PPA resin.

This material data has been provided by Matmatch.

All metrics apply to room temperature unless otherwise stated. SI units used unless otherwise stated.
Equivalent standards are similar to one or more standards provided by the supplier. Some equivalent standards may be stricter whereas others may be outside the bounds of the original standard.

Ashby charts

See where falls on the material property chart for against in your materials selection and design process. Our Ashby charts are interactive with more technical data upon clicking. Sign up to get access to this premium feature for free.

Properties

General

PropertyTemperatureValueComment

Density

23.0 °C

1.12 g/cm³

Show Material materials with Density of 1.12 g/cm³

ISO 1183

Mechanical

PropertyTemperatureValueComment

Elastic modulus

23.0 °C

2.1 GPa

Show Material materials with Elastic modulus of 2.1 GPa

ISO 527-1/-2

Elongation

23.0 °C

12 %

Show Material materials with Elongation of 12 %

ISO 527-1/-2

Elongation at yield

23.0 °C

6 %

Show Material materials with Elongation at yield of 6 %

ISO 527-1/-2

Impact strength, Charpy notched

23.0 °C

90 kJ/m²

Show Material materials with Impact strength, Charpy notched of 90 kJ/m²

ISO 179/1eA

Poisson's ratio

23.0 °C

0.4 [-]

Show Material materials with Poisson's ratio of 0.4 [-]

Yield strength

23.0 °C

68 MPa

Show Material materials with Yield strength of 68 MPa

ISO 527-1/-2

Thermal

PropertyValueComment

Heat deflection temperature, 1.80 MPa

124 °C

Show Material materials with Heat deflection temperature, 1.80 MPa of 124 °C

ISO 75-1/-2

Melting point

300 °C

Show Material materials with Melting point of 300 °C

ISO 11357-1/-3 | first heat

Electrical

PropertyTemperatureValueComment

Comparative tracking index

23.0 °C

600 V

Show Material materials with Comparative tracking index of 600 V

IEC 60112

Rheological Properties

PropertyTemperatureValueComment

Shrinkage

23.0 °C

0.7 %

Show Material materials with Shrinkage of 0.7 %

ISO 294-4, 2577

Shrinkage, transverse

23.0 °C

0.8 %

Show Material materials with Shrinkage, transverse of 0.8 %

ISO 294-4, 2577

Technological properties

Property
Processing methods

Drying Recommended: yes, Drying Temperature: 100°C, Drying Time, Dehumidified Dryer: 6-8h, Processing Moisture Content: ≤0.1%, Melt Temperature Optimum: 325°C, Min. melt temperature: 320°C, Max. melt temperature: 330°C, Min. mold temperature: 80°C, Max. mold temperature: 120°C