General
Property | Temperature | Value | Comment |
---|---|---|---|
Density | 23.0 °C | 1.47 g/cm³ Show Material materials with Density of 1.47 g/cm³ | ISO 1183 |
Mechanical
Property | Temperature | Value | Comment |
---|---|---|---|
Elastic modulus | 23.0 °C | 12 GPa Show Material materials with Elastic modulus of 12 GPa | ISO 527-1/-2 |
Elongation | 23.0 °C | 2.3 % Show Material materials with Elongation of 2.3 % | ISO 527-1/-2 |
Flexural modulus | 23.0 °C | 10.5 GPa Show Material materials with Flexural modulus of 10.5 GPa | ISO 178 |
Hardness, Ball Indentation | 23.0 °C | 310 MPa Show Material materials with Hardness, Ball Indentation of 310 MPa | ISO 2039-1 |
Impact strength, Charpy notched | 23.0 °C | 9 kJ/m² Show Material materials with Impact strength, Charpy notched of 9 kJ/m² | ISO 179/1eA |
Impact strength, Charpy unnotched | 23.0 °C | 50 kJ/m² Show Material materials with Impact strength, Charpy unnotched of 50 kJ/m² | ISO 179/1eU |
Poisson's ratio | 23.0 °C | 0.33 [-] Show Material materials with Poisson's ratio of 0.33 [-] | |
Tensile strength | 23.0 °C | 200 MPa Show Material materials with Tensile strength of 200 MPa | ISO 527-1/-2 |
Thermal
Property | Temperature | Value | Comment | ||
---|---|---|---|---|---|
Coefficient of thermal expansion | 23.0 °C | 2E-5 1/K Show Material materials with Coefficient of thermal expansion of 2E-5 1/K | ISO 11359-1/-2 | -40 - 23°C | ||
Coefficient of thermal expansion, transverse | 23.0 °C | 5.5E-5 1/K Show Material materials with Coefficient of thermal expansion, transverse of 5.5E-5 1/K | ISO 11359-1/-2 | -40 - 23°C | ||
Glass transition temperature | 135 °C Show Material materials with Glass transition temperature of 135 °C | ISO 11357-1/-2 | 18°F/min | |||
Heat deflection temperature, 0.45 MPa | 276 °C Show Material materials with Heat deflection temperature, 0.45 MPa of 276 °C | ISO 75-1/-2 | |||
Heat deflection temperature, 1.80 MPa | 262 °C Show Material materials with Heat deflection temperature, 1.80 MPa of 262 °C | ISO 75-1/-2 | |||
Melting point | 300 °C Show Material materials with Melting point of 300 °C | ISO 11357-1/-3 | first heat | |||
Flammability | FMVSS Class: B -, Burning rate, Thickness 1 mm: 28 mm/min |
Electrical
Property | Temperature | Value | Comment |
---|---|---|---|
Dielectric strength | 23.0 °C | 34 kV/mm Show Material materials with Dielectric strength of 34 kV/mm | IEC 60243-1 |
Volume resistivity | 23.0 °C | 1.00E+15 Ω·cm Show Material materials with Volume resistivity of 1.00E+15 Ω·cm | IEC 62631-3-1 |
Rheological Properties
Technological properties
Property | ||
---|---|---|
Processing methods | Drying Recommended: yes, Drying Temperature: 100°C, Drying Time, Dehumidified Dryer: 6-8h, Processing Moisture Content: ≤0.1%, Melt Temperature Optimum: 325°C, Min. melt temperature: 320°C, Max. melt temperature: 330°C, Mold Temperature Optimum: 150°C, Min. mold temperature: 140°C, Max. mold temperature: 180°C |