Zytel® RS LC1610 BK387

Alternative and trade names
PA1010-HIP

Want to keep this datasheet? Save it now in your required format

Description

Zytel® RS LC1610 BK387 is an unreinforced, toughened, plasticized, and heat stabilized,biobased polyamide 1010 resin for extrusion.

Equivalent Materials

This material data has been provided by Matmatch.

"Typical" values were obtained via a literature search. "Predicted" values were imputed via artificial intelligence technology. While we have placed significant efforts in ensuring data accuracy, "typical" and "predicted" data should be considered indicative and verified by appropriate material testing. Please do contact us if additional information on the the predicted data method is required.
All metrics apply to room temperature unless otherwise stated. SI units used unless otherwise stated.
Equivalent standards are similar to one or more standards provided by the supplier. Some equivalent standards may be stricter whereas others may be outside the bounds of the original standard.

Ashby charts

See where falls on the material property chart for against in your materials selection and design process. Our Ashby charts are interactive with more technical data upon clicking. Sign up to get access to this premium feature for free.

All categories

Properties

General

Property	Temperature	Value	Comment
Density	23.0 °C	1.05 g/cm³ Show Material materials with Density of 1.05 g/cm³	ISO 1183
Water absorption	23.0 °C	1.5 % Show Material materials with Water absorption of 1.5 %	Sim. to ISO 62 \| 80mil

Mechanical

Property	Temperature	Value	Comment
Elastic modulus	23.0 °C	0.79 GPa Show Material materials with Elastic modulus of 0.79 GPa	ISO 527-1/-2
Elongation	23.0 °C	230 % Show Material materials with Elongation of 230 %	ISO 527-1/-2 \| 50mm/min
Elongation at yield	23.0 °C	32 % Show Material materials with Elongation at yield of 32 %	ISO 527-1/-2
Flexural strength	23.0 °C	24 MPa Show Material materials with Flexural strength of 24 MPa	ISO 178
Impact strength, Charpy notched	-6.0 °C	7 kJ/m² Show Material materials with Impact strength, Charpy notched of 7 kJ/m²	ISO 179/1eA
	23.0 °C	24 kJ/m² Show Material materials with Impact strength, Charpy notched of 24 kJ/m²	ISO 179/1eA

Impact strength, Izod unnotched	-30.0 °C	6 kJ/m² Show Material materials with Impact strength, Izod unnotched of 6 kJ/m²	ISO 180/1A
	23.0 °C	24 kJ/m² Show Material materials with Impact strength, Izod unnotched of 24 kJ/m²	ISO 180/1A
	Unlock all property charts
Poisson's ratio	23.0 °C	0.46 [-] Show Material materials with Poisson's ratio of 0.46 [-]
Tensile strength	23.0 °C	38 MPa Show Material materials with Tensile strength of 38 MPa	ISO 527-1/-2 \| 50mm/min
Yield strength	23.0 °C	38 MPa Show Material materials with Yield strength of 38 MPa	ISO 527-1/-2
Impact strength, Charpy unnotched	No Break @ 23,-6°C, ISO 179/1eA

Thermal

Property	Value	Comment
Heat deflection temperature, 0.45 MPa	110 °C Show Material materials with Heat deflection temperature, 0.45 MPa of 110 °C	ISO 75-1/-2
Heat deflection temperature, 1.80 MPa	46 °C Show Material materials with Heat deflection temperature, 1.80 MPa of 46 °C	ISO 75-1/-2
Melting point	197 °C Show Material materials with Melting point of 197 °C	ISO 11357-1/-3 \| 18°F/min
Flammability	Burning Behav. at 60mil nom. thickn.: HB class, Thickness tested: 1.5 mm, Burning Behav. at thickness h: HB class, Thickness tested: 3 mm, FMVSS Class: B -, Burning rate, Thickness 1 mm: <80 mm/min

Rheological Properties

Property	Temperature	Value	Comment
Melt viscosity	250.0 °C	210 Pa·s Show Material materials with Melt viscosity of 210 Pa·s	ISO 11443 \| @ 1000 sec-1, 250°C
Shrinkage	23.0 °C	1.6 % Show Material materials with Shrinkage of 1.6 %	ISO 294-4, 2577
Shrinkage, transverse	23.0 °C	1 % Show Material materials with Shrinkage, transverse of 1 %	ISO 294-4, 2577

Technological properties

Property
Processing methods	Drying Recommended: yes, Drying Time, Dehumidified Dryer: 4-6h, Processing Moisture Content: ≤0.1%, Melt Temperature Optimum: 230°C, Min. melt temperature: 225°C, Max. melt temperature: 235°C, Mold Temperature Optimum: 55°C, Min. mold temperature: 50°C, Max. mold temperature: 80°C