General
| Property | Temperature | Value | Comment |
|---|---|---|---|
Density | 23.0 °C | 1.07 g/cm³ Show Material materials with Density of 1.07 g/cm³ | ISO 1183 |
Water absorption | 23.0 °C | 3.3 % Show Material materials with Water absorption of 3.3 % | Sim. to ISO 62 | 80mil |
Mechanical
| Property | Temperature | Value | Comment |
|---|---|---|---|
Elastic modulus | 23.0 °C | 2 GPa Show Material materials with Elastic modulus of 2 GPa | ISO 527-1/-2 |
Elongation | 23.0 °C | 230 % Show Material materials with Elongation of 230 % | ISO 527-1/-2 | 50mm/min |
Elongation at yield | 23.0 °C | 5 % Show Material materials with Elongation at yield of 5 % | ISO 527-1/-2 |
Flexural modulus | 23.0 °C | 1.9 GPa Show Material materials with Flexural modulus of 1.9 GPa | ISO 178 |
Hardness, Rockwell M | 23.0 °C | 75 [-] Show Material materials with Hardness, Rockwell M of 75 [-] | ISO 2039-2 |
Impact strength, Charpy notched | -40.0 °C | 7 kJ/m² Show Material materials with Impact strength, Charpy notched of 7 kJ/m² | ISO 179/1eA |
23.0 °C | 8 kJ/m² Show Material materials with Impact strength, Charpy notched of 8 kJ/m² | ISO 179/1eA | |
Impact strength, Izod unnotched | 23.0 °C | 5 kJ/m² Show Material materials with Impact strength, Izod unnotched of 5 kJ/m² | ISO 180/1A |
Poisson's ratio | 23.0 °C | 0.4 [-] Show Material materials with Poisson's ratio of 0.4 [-] | |
Tensile strength | 23.0 °C | 62 MPa Show Material materials with Tensile strength of 62 MPa | ISO 527-1/-2 | 50mm/min |
Yield strength | 23.0 °C | 64 MPa Show Material materials with Yield strength of 64 MPa | ISO 527-1/-2 |
Thermal
| Property | Temperature | Value | Comment | ||
|---|---|---|---|---|---|
Coefficient of thermal expansion | 23.0 °C | 9E-5 1/K Show Material materials with Coefficient of thermal expansion of 9E-5 1/K | ISO 11359-1/-2 | ||
Coefficient of thermal expansion, transverse | 23.0 °C | 1.5E-4 1/K Show Material materials with Coefficient of thermal expansion, transverse of 1.5E-4 1/K | ISO 11359-1/-2 | ||
Glass transition temperature | 60 °C Show Material materials with Glass transition temperature of 60 °C | ISO 11357-1/-2 | 18°F/min | |||
Heat deflection temperature, 0.45 MPa | 155 °C Show Material materials with Heat deflection temperature, 0.45 MPa of 155 °C | ISO 75-1/-2 | |||
Heat deflection temperature, 1.80 MPa | 55 °C Show Material materials with Heat deflection temperature, 1.80 MPa of 55 °C | ISO 75-1/-2 | |||
Melting point | 223 °C Show Material materials with Melting point of 223 °C | ISO 11357-1/-3 | 18°F/min | |||
Flammability | Burning Behav. at 60mil nom. thickn.: HB class, Thickness tested: 1.5 mm, Burning Behav. at thickness h: HB class, Thickness tested: 3 mm, Oxygen index: 24 %, FMVSS Class: B -, Burning rate, Thickness 1 mm: <80 mm/min | ||||
Electrical
| Property | Temperature | Value | Comment |
|---|---|---|---|
Comparative tracking index | 23.0 °C | 600 V Show Material materials with Comparative tracking index of 600 V | IEC 60112 |
Dielectric constant, 100Hz | 23.0 °C | 3.9 [-] Show Material materials with Dielectric constant, 100Hz of 3.9 [-] | IEC 62631-2-1 |
Dielectric constant, 10GHz | 23.0 °C | 2.7 [-] Show Material materials with Dielectric constant, 10GHz of 2.7 [-] | ASTM D 2520 B |
Dielectric constant, 1GHz | 23.0 °C | 2.8 [-] Show Material materials with Dielectric constant, 1GHz of 2.8 [-] | ASTM D 2520 B |
Dielectric constant, 1MHz | 23.0 °C | 3.3 [-] Show Material materials with Dielectric constant, 1MHz of 3.3 [-] | IEC 62631-2-1 |
Dissipation factor, 100Hz | 23.0 °C | 0.04 [-] Show Material materials with Dissipation factor, 100Hz of 0.04 [-] | IEC 62631-2-1 |
Dissipation factor, 1MHz | 23.0 °C | 0.03 [-] Show Material materials with Dissipation factor, 1MHz of 0.03 [-] | IEC 62631-2-1 |
Volume resistivity | 23.0 °C | 1.00E+15 Ω·cm Show Material materials with Volume resistivity of 1.00E+15 Ω·cm | IEC 62631-3-1 |
Rheological Properties
Technological properties
| Property |
|---|