General
Property | Temperature | Value | Comment |
---|---|---|---|
Density | 23.0 °C | 1.42 g/cm³ Show Material materials with Density of 1.42 g/cm³ | ISO 1183 |
Mechanical
Property | Temperature | Value | Comment |
---|---|---|---|
Elastic modulus | 23.0 °C | 11 GPa Show Material materials with Elastic modulus of 11 GPa | ISO 527-1/-2 |
Elongation | 23.0 °C | 3 % Show Material materials with Elongation of 3 % | ISO 527-1/-2 |
Flexural modulus | 23.0 °C | 10 GPa Show Material materials with Flexural modulus of 10 GPa | ISO 178 |
Flexural strength | 23.0 °C | 270 MPa Show Material materials with Flexural strength of 270 MPa | ISO 178 |
Impact strength, Charpy notched | 23.0 °C | 11 kJ/m² Show Material materials with Impact strength, Charpy notched of 11 kJ/m² | ISO 179/1eA |
Impact strength, Charpy unnotched | 23.0 °C | 82 kJ/m² Show Material materials with Impact strength, Charpy unnotched of 82 kJ/m² | ISO 179/1eU |
Poisson's ratio | 23.0 °C | 0.34 [-] Show Material materials with Poisson's ratio of 0.34 [-] | |
Tensile strength | 23.0 °C | 190 MPa Show Material materials with Tensile strength of 190 MPa | ISO 527-1/-2 |
Thermal
Property | Temperature | Value | Comment | ||
---|---|---|---|---|---|
Coefficient of thermal expansion | 23.0 °C | 2E-5 1/K Show Material materials with Coefficient of thermal expansion of 2E-5 1/K | ISO 11359-1/-2 | -40 - 23°C | ||
Coefficient of thermal expansion, transverse | 23.0 °C | 5.5E-5 1/K Show Material materials with Coefficient of thermal expansion, transverse of 5.5E-5 1/K | ISO 11359-1/-2 | -40 - 23°C | ||
Glass transition temperature | 115 °C Show Material materials with Glass transition temperature of 115 °C | ISO 11357-1/-2 | 18°F/min | |||
Heat deflection temperature, 1.80 MPa | 262 °C Show Material materials with Heat deflection temperature, 1.80 MPa of 262 °C | ISO 75-1/-2 | |||
Melting point | 300 °C Show Material materials with Melting point of 300 °C | ISO 11357-1/-3 | first heat | |||
Flammability | Oxygen index: 23 %, Glow Wire Flammability Index, 120mil: 960 °C, Glow Wire Ignition Temperature, 120mil: 800 °C, FMVSS Class: SE - |
Electrical
Property | Temperature | Value | Comment |
---|---|---|---|
Comparative tracking index | 23.0 °C | 600 V Show Material materials with Comparative tracking index of 600 V | IEC 60112 |
Dielectric constant, 100Hz | 23.0 °C | 4.3 [-] Show Material materials with Dielectric constant, 100Hz of 4.3 [-] | IEC 62631-2-1 |
Dielectric constant, 1MHz | 23.0 °C | 3.9 [-] Show Material materials with Dielectric constant, 1MHz of 3.9 [-] | IEC 62631-2-1 |
Dielectric strength | 23.0 °C | 32 kV/mm Show Material materials with Dielectric strength of 32 kV/mm | IEC 60243-1 |
Dissipation factor, 100Hz | 23.0 °C | 5E-3 [-] Show Material materials with Dissipation factor, 100Hz of 5E-3 [-] | IEC 62631-2-1 |
Dissipation factor, 1MHz | 23.0 °C | 0.02 [-] Show Material materials with Dissipation factor, 1MHz of 0.02 [-] | IEC 62631-2-1 |
Volume resistivity | 23.0 °C | 1.00E+15 Ω·cm Show Material materials with Volume resistivity of 1.00E+15 Ω·cm | min. | IEC 62631-3-1 |
Rheological Properties
Technological properties
Property | ||
---|---|---|
Fillers | 35% Glass Fiber | |
Processing methods | Drying Recommended: yes, Drying Temperature: 100°C, Drying Time, Dehumidified Dryer: 6-8h, Processing Moisture Content: ≤0.1%, Melt Temperature Optimum: 325°C, Min. melt temperature: 320°C, Max. melt temperature: 330°C, Min. mold temperature: 90°C, Max. mold temperature: 130°C |