Zytel® HTNFR55G50NHLW NC010

Alternative and trade names
PA-GF50FR(40)

Want to keep this datasheet? Save it now in your required format

Description

Zytel® HTNFR55G50NHLW NC010 is a 50% glass reinforced, flame retardant, high performance polyamide with low warpage characteristics. It is also a PPA resin and uses a non-halogenated flame retardant.

Equivalent Materials

This material data has been provided by Matmatch.

"Typical" values were obtained via a literature search. "Predicted" values were imputed via artificial intelligence technology. While we have placed significant efforts in ensuring data accuracy, "typical" and "predicted" data should be considered indicative and verified by appropriate material testing. Please do contact us if additional information on the the predicted data method is required.
All metrics apply to room temperature unless otherwise stated. SI units used unless otherwise stated.
Equivalent standards are similar to one or more standards provided by the supplier. Some equivalent standards may be stricter whereas others may be outside the bounds of the original standard.

Ashby charts

See where falls on the material property chart for against in your materials selection and design process. Our Ashby charts are interactive with more technical data upon clicking. Sign up to get access to this premium feature for free.

All categories

Properties

General

Property	Temperature	Value	Comment
Density	23.0 °C	1.65 g/cm³ Show Material materials with Density of 1.65 g/cm³	ISO 1183

Mechanical

Property	Temperature	Value	Comment
Elastic modulus	23.0 °C	18 GPa Show Material materials with Elastic modulus of 18 GPa	ISO 527-1/-2
Elongation	23.0 °C	1.6 % Show Material materials with Elongation of 1.6 %	ISO 527-1/-2
Flexural modulus	23.0 °C	16.6 GPa Show Material materials with Flexural modulus of 16.6 GPa	ISO 178
Flexural strength	23.0 °C	305 MPa Show Material materials with Flexural strength of 305 MPa	ISO 178
Impact strength, Charpy notched	23.0 °C	12 kJ/m² Show Material materials with Impact strength, Charpy notched of 12 kJ/m²	ISO 179/1eA
Poisson's ratio	23.0 °C	0.33 [-] Show Material materials with Poisson's ratio of 0.33 [-]
Tensile strength	23.0 °C	200 MPa Show Material materials with Tensile strength of 200 MPa	ISO 527-1/-2

Thermal

Property	Value	Comment
Heat deflection temperature, 1.80 MPa	217 °C Show Material materials with Heat deflection temperature, 1.80 MPa of 217 °C	ISO 75-1/-2
Melting point	298 °C Show Material materials with Melting point of 298 °C	ISO 11357-1/-3 \| first heat
Flammability	Burning Behav. at 60mil nom. thickn.: V-0 class, Thickness tested: 1.5 mm, UL recognition: yes -, Burning Behav. at thickness h: V-0 class, Thickness tested: 0.4 mm, UL recognition: yes -, FMVSS Class: B -, Burning rate, Thickness 1 mm: <80 mm/min

Electrical

Property	Temperature	Value	Comment
Comparative tracking index	23.0 °C	600 V Show Material materials with Comparative tracking index of 600 V	IEC 60112

Rheological Properties

Property	Temperature	Value	Comment
Shrinkage	23.0 °C	0.1 % Show Material materials with Shrinkage of 0.1 %	ISO 294-4, 2577
Shrinkage, transverse	23.0 °C	0.2 % Show Material materials with Shrinkage, transverse of 0.2 %	ISO 294-4, 2577

Technological properties

Property
Fillers	50% Glass Fiber
Processing methods	Drying Recommended: yes, Drying Temperature: 100°C, Drying Time, Dehumidified Dryer: 6-8h, Processing Moisture Content: ≤0.1%, Min. melt temperature: 300°C, Max. melt temperature: 315°C, Min. mold temperature: 70°C, Max. mold temperature: 130°C