Zytel® LC6200 BK385

Alternative and trade names
PA612-HI

Want to keep this datasheet? Save it now in your required format

Description

DuPont™ Zytel® LCPA long chain polyamide resins provide an innovative and growing portfolio of flexible polymers with excellent thermal, chemical, and hydrolysis resistance. The diverse selection of Zytel® LCPA grades is targeted for a range of performance characteristics, balancing temperature resistance, flexibility and low permeation.Zytel® LC6200 BK385 is a toughened polyamide 612 resin for extrusion applications.

Equivalent Materials

This material data has been provided by Matmatch.

"Typical" values were obtained via a literature search. "Predicted" values were imputed via artificial intelligence technology. While we have placed significant efforts in ensuring data accuracy, "typical" and "predicted" data should be considered indicative and verified by appropriate material testing. Please do contact us if additional information on the the predicted data method is required.
All metrics apply to room temperature unless otherwise stated. SI units used unless otherwise stated.
Equivalent standards are similar to one or more standards provided by the supplier. Some equivalent standards may be stricter whereas others may be outside the bounds of the original standard.

Ashby charts

See where falls on the material property chart for against in your materials selection and design process. Our Ashby charts are interactive with more technical data upon clicking. Sign up to get access to this premium feature for free.

All categories

Properties

General

Property	Temperature	Value	Comment
Density	23.0 °C	1 g/cm³ Show Material materials with Density of 1 g/cm³	ISO 1183

Mechanical

Property	Temperature	Value	Comment
Elastic modulus	23.0 °C	1.08 GPa Show Material materials with Elastic modulus of 1.08 GPa	ISO 527-1/-2
Elongation	23.0 °C	100 % Show Material materials with Elongation of 100 %	ISO 527-1/-2 \| 50mm/min
Elongation at yield	23.0 °C	13 % Show Material materials with Elongation at yield of 13 %	ISO 527-1/-2
Impact strength, Charpy notched	-6.0 °C	15 kJ/m² Show Material materials with Impact strength, Charpy notched of 15 kJ/m²	ISO 179/1eA
	23.0 °C	40 kJ/m² Show Material materials with Impact strength, Charpy notched of 40 kJ/m²	ISO 179/1eA

Impact strength, Izod unnotched	-30.0 °C	13 kJ/m² Show Material materials with Impact strength, Izod unnotched of 13 kJ/m²	ISO 180/1A
	23.0 °C	27 kJ/m² Show Material materials with Impact strength, Izod unnotched of 27 kJ/m²	ISO 180/1A
	Unlock all property charts
Poisson's ratio	23.0 °C	0.45 [-] Show Material materials with Poisson's ratio of 0.45 [-]
Yield strength	23.0 °C	32.2 MPa Show Material materials with Yield strength of 32.2 MPa	ISO 527-1/-2

Thermal

Property	Temperature	Value	Comment
Heat deflection temperature, 0.45 MPa		85 °C Show Material materials with Heat deflection temperature, 0.45 MPa of 85 °C	ISO 75-1/-2
Heat deflection temperature, 1.80 MPa		46 °C Show Material materials with Heat deflection temperature, 1.80 MPa of 46 °C	ISO 75-1/-2
Melting point		218 °C Show Material materials with Melting point of 218 °C	ISO 11357-1/-3 \| 18°F/min
Specific heat capacity	23.0 °C	2700 J/(kg·K) Show Material materials with Specific heat capacity of 2700 J/(kg·K)	of melt
Flammability	FMVSS Class: B -, Burning rate, Thickness 1 mm: <80 mm/min

Technological properties

Property

Zytel® LC6200 BK385

Description

Equivalent Materials

Ashby charts

Suggested reading

Properties