General
Property | Temperature | Value | Comment |
---|---|---|---|
Density | 23.0 °C | 1.01 g/cm³ Show Material materials with Density of 1.01 g/cm³ | ISO 1183 |
Mechanical
Property | Temperature | Value | Comment |
---|---|---|---|
Elastic modulus | 23.0 °C | 1.1 GPa Show Material materials with Elastic modulus of 1.1 GPa | ISO 527-1/-2 |
Elongation | 23.0 °C | 100 % Show Material materials with Elongation of 100 % | ISO 527-1/-2 | 50mm/min |
Elongation at yield | 23.0 °C | 12 % Show Material materials with Elongation at yield of 12 % | ISO 527-1/-2 |
Hardness, Shore D | 23.0 °C | 69 [-] Show Material materials with Hardness, Shore D of 69 [-] | ISO 7619-1 | 15 seconds |
Impact strength, Charpy notched | -6.0 °C | 13 kJ/m² Show Material materials with Impact strength, Charpy notched of 13 kJ/m² | ISO 179/1eA |
23.0 °C | 35 kJ/m² Show Material materials with Impact strength, Charpy notched of 35 kJ/m² | ISO 179/1eA | |
Poisson's ratio | 23.0 °C | 0.45 [-] Show Material materials with Poisson's ratio of 0.45 [-] | |
Yield strength | 23.0 °C | 32 MPa Show Material materials with Yield strength of 32 MPa | ISO 527-1/-2 |
Thermal
Property | Value | Comment | |
---|---|---|---|
Heat deflection temperature, 0.45 MPa | 83 °C Show Material materials with Heat deflection temperature, 0.45 MPa of 83 °C | ISO 75-1/-2 | |
Heat deflection temperature, 1.80 MPa | 47 °C Show Material materials with Heat deflection temperature, 1.80 MPa of 47 °C | ISO 75-1/-2 | |
Melting point | 216 °C Show Material materials with Melting point of 216 °C | ISO 11357-1/-3 | 18°F/min | |
Flammability | FMVSS Class: B -, Burning rate, Thickness 1 mm: <80 mm/min |
Technological properties
Property |
---|