Zytel® XT70G50HSL BK044A

Alternative and trade names
PA66-GF50
Want to keep this datasheet? Save it now in your required format

Description

Zytel® XT70G50HSL BK044A is a 50% glass fiber reinforced, heat stabilized polyamide 66 resin for injection molding.

Equivalent Materials

This material data has been provided by Matmatch.

All metrics apply to room temperature unless otherwise stated. SI units used unless otherwise stated.
Equivalent standards are similar to one or more standards provided by the supplier. Some equivalent standards may be stricter whereas others may be outside the bounds of the original standard.

Ashby charts

See where falls on the material property chart for against in your materials selection and design process. Our Ashby charts are interactive with more technical data upon clicking. Sign up to get access to this premium feature for free.

Properties

General

PropertyTemperatureValueComment

Density

23.0 °C

1.59 g/cm³

Show Material materials with Density of 1.59 g/cm³

ISO 1183

Mechanical

PropertyTemperatureValueComment

Elastic modulus

23.0 °C

17 GPa

Show Material materials with Elastic modulus of 17 GPa

ISO 527-1/-2

Elongation

23.0 °C

2.6 %

Show Material materials with Elongation of 2.6 %

ISO 527-1/-2

Flexural modulus

23.0 °C

15 GPa

Show Material materials with Flexural modulus of 15 GPa

ISO 178

Flexural strength

23.0 °C

340 MPa

Show Material materials with Flexural strength of 340 MPa

ISO 178

Impact strength, Charpy notched

-6.0 °C

13 kJ/m²

Show Material materials with Impact strength, Charpy notched of 13 kJ/m²

ISO 179/1eA

23.0 °C

15 kJ/m²

Show Material materials with Impact strength, Charpy notched of 15 kJ/m²

ISO 179/1eA

Impact strength, Charpy unnotched

23.0 °C

90 kJ/m²

Show Material materials with Impact strength, Charpy unnotched of 90 kJ/m²

ISO 179/1eU

Poisson's ratio

23.0 °C

0.33 [-]

Show Material materials with Poisson's ratio of 0.33 [-]

Tensile strength

23.0 °C

240 MPa

Show Material materials with Tensile strength of 240 MPa

ISO 527-1/-2

Thermal

PropertyTemperatureValueComment

Coefficient of thermal expansion

23.0 °C

1.9E-5 1/K

Show Material materials with Coefficient of thermal expansion of 1.9E-5 1/K

ISO 11359-1/-2

Coefficient of thermal expansion, transverse

23.0 °C

6.5E-5 1/K

Show Material materials with Coefficient of thermal expansion, transverse of 6.5E-5 1/K

ISO 11359-1/-2

Glass transition temperature

70 °C

Show Material materials with Glass transition temperature of 70 °C

ISO 11357-1/-2 | 18°F/min

Heat deflection temperature, 0.45 MPa

260 °C

Show Material materials with Heat deflection temperature, 0.45 MPa of 260 °C

ISO 75-1/-2

Heat deflection temperature, 1.80 MPa

253 °C

Show Material materials with Heat deflection temperature, 1.80 MPa of 253 °C

ISO 75-1/-2

Melting point

259 °C

Show Material materials with Melting point of 259 °C

ISO 11357-1/-3 | 18°F/min

Flammability

FMVSS Class: SE -, Burning rate, Thickness 1 mm: 22 mm/min

Rheological Properties

PropertyTemperatureValueComment

Shrinkage

23.0 °C

0.3 %

Show Material materials with Shrinkage of 0.3 %

ISO 294-4 | Annealed

Shrinkage, transverse

23.0 °C

1 %

Show Material materials with Shrinkage, transverse of 1 %

ISO 294-4 | Annealed

Technological properties

Property
Fillers

50% Glass Fiber

Processing methods

Drying Recommended: yes, Drying Temperature: 80°C, Drying Time, Dehumidified Dryer: 2-4h, Processing Moisture Content: ≤0.2%, Melt Temperature Optimum: 285°C, Min. melt temperature: 275°C, Max. melt temperature: 295°C, Mold Temperature Optimum: 100°C, Min. mold temperature: 70°C, Max. mold temperature: 120°C, Ejection temperature: 200°C