Zytel® FE3734 NC010

Want to keep this datasheet? Save it now in your required format


DuPont™ Zytel® LCPA long chain polyamide resins provide an innovative and growing portfolio of flexible polymers with excellent thermal, chemical, and hydrolysis resistance. The diverse selection of Zytel® LCPA grades is targeted for a range of performance characteristics, balancing temperature resistance, flexibility and low permeation.Zytel® FE3734 NC010 is an unreinforced, lubricated polyamide 612 resin suitable for injection molding.

Equivalent Materials

This material data has been provided by Matmatch.

All metrics apply to room temperature unless otherwise stated. SI units used unless otherwise stated.
Equivalent standards are similar to one or more standards provided by the supplier. Some equivalent standards may be stricter whereas others may be outside the bounds of the original standard.

Ashby charts

See where falls on the material property chart for against in your materials selection and design process. Our Ashby charts are interactive with more technical data upon clicking. Sign up to get access to this premium feature for free.





23.0 °C

1.07 g/cm³

Show Material materials with Density of 1.07 g/cm³

ISO 1183

Water absorption

23.0 °C

3 %

Show Material materials with Water absorption of 3 %

Sim. to ISO 62 | 80mil



Elastic modulus

23.0 °C

2.4 GPa

Show Material materials with Elastic modulus of 2.4 GPa

ISO 527-1/-2


23.0 °C

38 %

Show Material materials with Elongation of 38 %

ISO 527-1/-2

Elongation at yield

23.0 °C

5 %

Show Material materials with Elongation at yield of 5 %

ISO 527-1/-2

Flexural modulus

23.0 °C

2.2 GPa

Show Material materials with Flexural modulus of 2.2 GPa

ISO 178

Hardness, Rockwell R

23.0 °C

114 [-]

Show Material materials with Hardness, Rockwell R of 114 [-]

ISO 2039-2

Impact strength, Charpy notched

23.0 °C

4.8 kJ/m²

Show Material materials with Impact strength, Charpy notched of 4.8 kJ/m²

ISO 179/1eA

Poisson's ratio

23.0 °C

0.38 [-]

Show Material materials with Poisson's ratio of 0.38 [-]

Yield strength

23.0 °C

59 MPa

Show Material materials with Yield strength of 59 MPa

ISO 527-1/-2

Impact strength, Charpy unnotched

No Break @ 23,-6°C, ISO 179/1eA



Heat deflection temperature, 1.80 MPa

63 °C

Show Material materials with Heat deflection temperature, 1.80 MPa of 63 °C

ISO 75-1/-2

Melting point

218 °C

Show Material materials with Melting point of 218 °C

ISO 11357-1/-3 | 18°F/min


FMVSS Class: B -, Burning rate, Thickness 1 mm: <80 mm/min

Rheological Properties



23.0 °C

1.3 %

Show Material materials with Shrinkage of 1.3 %

ISO 294-4, 2577

Shrinkage, transverse

23.0 °C

1.4 %

Show Material materials with Shrinkage, transverse of 1.4 %

ISO 294-4, 2577

Technological properties

Processing methods

Drying Recommended: yes, Drying Time, Dehumidified Dryer: 2-4h, Processing Moisture Content: ≤0.15%, Melt Temperature Optimum: 250°C, Min. melt temperature: 230°C, Max. melt temperature: 290°C, Min. mold temperature: 50°C, Max. mold temperature: 90°C