Description

Zytel® HTNFR42G30NHNC010 is a 30% glass reinforced, flame retardant high performance polyamide resindeveloped for improved reflow soldering performance in connector applications. It is also a PPA resin and it uses a non-halogenated flame retardant.

Equivalent Materials

This material data has been provided by Matmatch.

All metrics apply to room temperature unless otherwise stated. SI units used unless otherwise stated.
Equivalent standards are similar to one or more standards provided by the supplier. Some equivalent standards may be stricter whereas others may be outside the bounds of the original standard.

Ashby charts

See where falls on the material property chart for against in your materials selection and design process. Our Ashby charts are interactive with more technical data upon clicking. Sign up to get access to this premium feature for free.

Properties

General

PropertyTemperatureValueComment

Density

23.0 °C

1.45 g/cm³

Show Material materials with Density of 1.45 g/cm³

ISO 1183

Mechanical

PropertyTemperatureValueComment

Elastic modulus

23.0 °C

10.6 GPa

Show Material materials with Elastic modulus of 10.6 GPa

ISO 527-1/-2

Elongation

23.0 °C

1.8 %

Show Material materials with Elongation of 1.8 %

ISO 527-1/-2

Flexural modulus

23.0 °C

11.2 GPa

Show Material materials with Flexural modulus of 11.2 GPa

ISO 178

Flexural strength

23.0 °C

216 MPa

Show Material materials with Flexural strength of 216 MPa

ISO 178

Impact strength, Charpy notched

23.0 °C

7 kJ/m²

Show Material materials with Impact strength, Charpy notched of 7 kJ/m²

ISO 179/1eA

Impact strength, Charpy unnotched

23.0 °C

46 kJ/m²

Show Material materials with Impact strength, Charpy unnotched of 46 kJ/m²

ISO 179/1eU

Poisson's ratio

23.0 °C

0.34 [-]

Show Material materials with Poisson's ratio of 0.34 [-]

Tensile strength

23.0 °C

138 MPa

Show Material materials with Tensile strength of 138 MPa

ISO 527-1/-2

Thermal

PropertyValueComment

Heat deflection temperature, 1.80 MPa

276 °C

Show Material materials with Heat deflection temperature, 1.80 MPa of 276 °C

ISO 75-1/-2 | annealed

Melting point

315 °C

Show Material materials with Melting point of 315 °C

ISO 11357-1/-3 | first heat

Relative temperature index, electrical

130 °C

Show Material materials with Relative temperature index, electrical of 130 °C

UL 746B | 120mil

Relative temperature index, mechanical impact

120 °C

Show Material materials with Relative temperature index, mechanical impact of 120 °C

UL 746B | 120mil

Relative temperature index, mechanical strength

130 °C

Show Material materials with Relative temperature index, mechanical strength of 130 °C

UL 746B | 120mil

Flammability

Burning Behav. at thickness h: V-0 class, Thickness tested: 0.4 mm, UL recognition: yes -, Glow Wire Flammability Index, 15mil: 960 °C, Glow Wire Flammability Index, 60mil: 960 °C, Glow Wire Flammability Index, 120mil: 960 °C, Glow Wire Ignition Temperature, 15mil: 750 °C, Glow Wire Ignition Temperature, 60mil: 800 °C, Glow Wire Ignition Temperature, 120mil: 825 °C

Electrical

PropertyTemperatureValueComment

Comparative tracking index

23.0 °C

600 V

Show Material materials with Comparative tracking index of 600 V

IEC 60112

Technological properties

Property
Fillers

30% Glass Fiber

Processing methods

Drying Recommended: yes, Drying Temperature: 100°C, Drying Time, Dehumidified Dryer: 6-8h, Processing Moisture Content: ≤0.1%, Min. melt temperature: 330°C, Max. melt temperature: 335°C, Min. mold temperature: 110°C, Max. mold temperature: 130°C