Zytel® RS LC3090 NC010

Alternative and trade names
PA610
Want to keep this datasheet? Save it now in your required format

Description

DuPont™ Zytel® LCPA long chain polyamide resins provide an innovative and growing portfolio of flexible polymers with excellent thermal, chemical, and hydrolysis resistance. The diverse selection of Zytel® LCPA grades is targeted for a range of performance characteristics, balancing temperature resistance, flexibility and low permeation. DuPont™ Zytel® RS LCPA resins contain between 20% and 100% renewably sourced material (by weight) derived from castor beans.Zytel® RS LC3090 NC010 is a renewable sourced polyamide 610 containing a minimum of 60% renewably sourced ingredient by weight. It is an unreinforced, high viscosity grade, developed for extrusion applications.

Equivalent Materials

This material data has been provided by Matmatch.

All metrics apply to room temperature unless otherwise stated. SI units used unless otherwise stated.
Equivalent standards are similar to one or more standards provided by the supplier. Some equivalent standards may be stricter whereas others may be outside the bounds of the original standard.

Ashby charts

See where falls on the material property chart for against in your materials selection and design process. Our Ashby charts are interactive with more technical data upon clicking. Sign up to get access to this premium feature for free.

Properties

General

PropertyTemperatureValueComment

Density

23.0 °C

1.08 g/cm³

Show Material materials with Density of 1.08 g/cm³

ISO 1183

Water absorption

23.0 °C

0.58 %

Show Material materials with Water absorption of 0.58 %

Sim. to ISO 62 | Immersion 24h

Mechanical

PropertyTemperatureValueComment

Elastic modulus

23.0 °C

2.3 GPa

Show Material materials with Elastic modulus of 2.3 GPa

ISO 527-1/-2

Flexural modulus

23.0 °C

1.9 GPa

Show Material materials with Flexural modulus of 1.9 GPa

ISO 178

Flexural strength

23.0 °C

86 MPa

Show Material materials with Flexural strength of 86 MPa

ISO 178

Impact strength, Charpy notched

23.0 °C

5.6 kJ/m²

Show Material materials with Impact strength, Charpy notched of 5.6 kJ/m²

ISO 179/1eA

Poisson's ratio

23.0 °C

0.39 [-]

Show Material materials with Poisson's ratio of 0.39 [-]

Impact strength, Charpy unnotched

No Break @ 23°C, ISO 179/1eU

Thermal

PropertyValueComment

Heat deflection temperature, 0.45 MPa

151 °C

Show Material materials with Heat deflection temperature, 0.45 MPa of 151 °C

ISO 75-1/-2

Heat deflection temperature, 1.80 MPa

54 °C

Show Material materials with Heat deflection temperature, 1.80 MPa of 54 °C

ISO 75-1/-2

Melting point

225 °C

Show Material materials with Melting point of 225 °C

ISO 11357-1/-3 | 18°F/min

Flammability

FMVSS Class: B -, Burning rate, Thickness 1 mm: <80 mm/min

Rheological Properties

PropertyTemperatureValueComment

Shrinkage

23.0 °C

1.2 %

Show Material materials with Shrinkage of 1.2 %

ISO 294-4, 2577

Shrinkage, transverse

23.0 °C

1.2 %

Show Material materials with Shrinkage, transverse of 1.2 %

ISO 294-4, 2577