Properties
General
| Property | Temperature | Value |
|---|---|---|
Density | 23.0 °C | 1.05 g/cm³ Show Material materials with Density of 1.05 g/cm³ |
Relative density | 23.0 °C | 1.05 [-] Show Material materials with Relative density of 1.05 [-] |
Mechanical
| Property | Temperature | Value | Comment |
|---|---|---|---|
Elongation | -40.0 °C | 220 % Show Material materials with Elongation of 220 % | |
23.0 °C | 380 % Show Material materials with Elongation of 380 % | ||
80.0 °C | 420 % Show Material materials with Elongation of 420 % | ||
Elongation at yield | 23.0 °C | 26 % Show Material materials with Elongation at yield of 26 % | |
Flexural modulus | -40.0 °C | 2.28 GPa Show Material materials with Flexural modulus of 2.28 GPa | |
23.0 °C | 0.31 GPa Show Material materials with Flexural modulus of 0.31 GPa | ||
80.0 °C | 0.16 GPa Show Material materials with Flexural modulus of 0.16 GPa | ||
Hardness, Rockwell R | 23.0 °C | 75 [-] Show Material materials with Hardness, Rockwell R of 75 [-] | |
Hardness, Shore D | 23.0 °C | 63 [-] Show Material materials with Hardness, Shore D of 63 [-] | |
Impact strength, Izod unnotched | -40.0 °C | 21 kJ/m² Show Material materials with Impact strength, Izod unnotched of 21 kJ/m² | No Break @ 23,80°C |
Tensile strength | -40.0 °C | 76 MPa Show Material materials with Tensile strength of 76 MPa | |
23.0 °C | 62 MPa Show Material materials with Tensile strength of 62 MPa | ||
80.0 °C | 54 MPa Show Material materials with Tensile strength of 54 MPa | ||
Yield strength | 23.0 °C | 21 MPa Show Material materials with Yield strength of 21 MPa | |
Thermal
| Property | Temperature | Value | Comment |
|---|---|---|---|
Coefficient of thermal expansion | 23.0 °C | 1.1E-4 1/K Show Material materials with Coefficient of thermal expansion of 1.1E-4 1/K | for -30 to 50°C |
Glass transition temperature | 41.85 °C Show Material materials with Glass transition temperature of 41.85 °C | ||
Heat deflection temperature | 39.85 °C Show Material materials with Heat deflection temperature of 39.85 °C | ||
Latent heat of fusion | 39 J/g Show Material materials with Latent heat of fusion of 39 J/g | 24% crystallinity | |
Melting point | 183.85 °C Show Material materials with Melting point of 183.85 °C | ||
Thermal conductivity | 23.0 °C | 0.19 W/(m·K) Show Material materials with Thermal conductivity of 0.19 W/(m·K) |
Electrical
| Property | Temperature | Value | Comment |
|---|---|---|---|
Dielectric constant, 1MHz | 23.0 °C | 3.1 [-] Show Material materials with Dielectric constant, 1MHz of 3.1 [-] | Dry |
Dielectric strength | 23.0 °C | 24 kV/mm Show Material materials with Dielectric strength of 24 kV/mm | |
Dissipation factor, 1MHz | 23.0 °C | 0.04 [-] Show Material materials with Dissipation factor, 1MHz of 0.04 [-] | Dry |
Technological properties
| Property | ||
|---|---|---|
| Application areas | Tubing, hoses, and pipes for automotive, trucking, industrial, and petroleum production applications. Examples are heavy truck airbrake tubing, automotive fuel lines, and submarine flexible pipes for offshore oil production. Thermoplastic powder coatings for industrial, transportation, and retail items are prepared in a Nylon 11 base. Nylon 11 is being used in a variety of food-contact applications, including sausage casing, beverage tubing, and reusable kitchen devices. | |