HGFL BOPP (Biaxially Oriented Polypropylene) Transparent Film

Want to keep this datasheet? Save it now in your required format

Description

Heat-sealing transparent BOPP film with a low threshold of welding, with high coefficient of friction for a special purposes, for high quality rotogravure and flexographic printing and lamination. The main advantages are: A wide range of heat sealing; contains antistatic and antiblocking additives; excellent optical properties; good mechanical properties; intended for contact with food; high coefficient of friction stable in time; without coatings and primers.

This material data has been provided by Matmatch.

All metrics apply to room temperature unless otherwise stated. SI units used unless otherwise stated.
Equivalent standards are similar to one or more standards provided by the supplier. Some equivalent standards may be stricter whereas others may be outside the bounds of the original standard.

Ashby charts

Properties

General

PropertyValueTemperatureComment

Density

0.91 g/cm³

Show Material materials with Density of 0.91 g/cm³ at 20.0 °C

20.0 °C

Film yield

22.89 - 73.26 m²/kg

Show Material materials with Film yield of 22.89 - 73.26 m²/kg at 20.0 °C

20.0 °C

Shrinkage

4 - 5 %

Show Material materials with Shrinkage of 4 - 5 % at 120.0 °C

120.0 °C

GOST 18616, ISO 11501, ASTM D1204 (Thermal shrinkage at 120˚C, 5 min)

Shrinkage, transverse

2 - 3 %

Show Material materials with Shrinkage, transverse of 2 - 3 % at 120.0 °C

120.0 °C

GOST 18616, ISO 11501, ASTM D1204 (Thermal shrinkage at 120˚C, 5 min)

Surface density

1.36E-3 - 4.37E-3 g/cm²

Show Material materials with Surface density of 1.36E-3 - 4.37E-3 g/cm² at 20.0 °C

20.0 °C

Dimension

PropertyValue

Dimensions

Available thicknesses: 15, 18, 20, 25, 30, 35, 40, 48µm.

Thickness

0.02 - 0.05 mm

Show Material materials with Thickness of 0.02 - 0.05 mm

Mechanical

PropertyValueTemperatureComment

Elongation

200 - 220 %

Show Material materials with Elongation of 200 - 220 % at 20.0 °C

20.0 °C

GOST 14236, ISO 527, ASTM D882

Elongation, transverse

70 - 80 %

Show Material materials with Elongation, transverse of 70 - 80 % at 20.0 °C

20.0 °C

GOST 14236, ISO 527, ASTM D882

Tensile strength

130 - 140 MPa

Show Material materials with Tensile strength of 130 - 140 MPa at 20.0 °C

20.0 °C

GOST 14236, ISO 527, ASTM D882

Tensile strength, transverse

230 - 250 MPa

Show Material materials with Tensile strength, transverse of 230 - 250 MPa at 20.0 °C

20.0 °C

GOST 14236, ISO 527, ASTM D882

Optical

PropertyValueComment

Haze

2.5 - 3.2 %

Show Material materials with Haze of 2.5 - 3.2 %

GOST 15875, ISO 14782, ASTM D 1003

Technological properties

Property
Application areas

High quality solvent based rotogravure and flexographic printing; solvent based and solvent free lamination with polyurethane adhesives; manufacture of flexible packaging for food products; for vertical VFFS and horizontal HFFS packaging machines; laminating with PE and CPP films with a high content of slipping additives; to reduce the impact of slip additives transition from PE or CPP film to the BOPP film side, which leads to a significant coefficient of friction reduction. The high coefficient of friction of the HGFL film, provides a certain margin in this case. For a case in which the bondage process of packed products is present, for example, in pasta packaging; to save the packed packages in a single group without sliding over each other (if necessary); in the other cases, when slip reduction on BOPP side of the flexible packaging is necessary; for cold seal glue frame coating onto UT film side (if necessary).

Friction

Kinetic coefficient of friction µ= 0.4-0.65 (GOST 27492, ISO 8295, ASTM D 1894).

Other

HGFL BOPP films comprise: A treated modified heat sealable copolymer skin layer, a transparent oriented polypropylene core layer, a heat sealable, non treated skin layer with low seal intention temperature and high coefficient of friction.

Processing history

Treatment level: 38 mN/m (ISO 8296, ASTM D 2578)