PMD.M BOPP (Biaxially Oriented Polypropylene) Metallized Film

.XLSX
.PDF
Save

Description

Non-heat-sealable metallized BOPP film for the production of decorative packaging. With increased coefficient of friction. For printing and lamination and for decorative packaging. The main advantages are: Standard barrier properties of metallized films; contains antiblock additives; mechanical properties are good; high adhesion of the aluminum layer; intended for contact with food; without coating or primer.

Properties

Dimension

Thickness t

0.02 - 0.04 mm

General

Density ρ

0.91 g/cm³ at 20 °C

Film yield Yfilm

27.5 - 54.9 m²/kg at 20 °C

Shrinkage cshrink

4 % at 120 °C

GOST 18616, ISO 11501, ASTM D1204 (Thermal shrinkage at 120˚C, 5 min)

Shrinkage, transverse cshrink, trans

2 % at 120 °C

GOST 18616, ISO 11501, ASTM D1204 (Thermal shrinkage at 120˚C, 5 min)

Surface density ρsurf

1.82E-3 - 3.64E-3 g/cm² at 20 °C

Material Information

Dimension

Available thicknesses: 20, 25, 30, 35, 40µm.

Mechanical

Elongation A

200 % at 20 °C

GOST 14236, ISO 527, ASTM D882

Elongation, transverse A

70 % at 20 °C

GOST 14236, ISO 527, ASTM D882

Tensile strength Rm

140 MPa at 20 °C

GOST 14236, ISO 527, ASTM D882

Tensile strength, transverse Rm,trans

280 MPa at 20 °C

GOST 14236, ISO 527, ASTM D882

Technological properties

Application areas

High quality rotogravure and flexographic solvent based printing; for lamination with solvent based or solventless polyurethane adhesives; production of decorative packaging for flowers, gift wrap and etc.; heat sealing by string is possible; lamination with films, paper and cardboard.

Friction

Kinetic coefficient of friction µ= 0.2-0.4 (GOST 27492, ISO 8295, ASTM D 1894).

Other

PMD.M BOPP films comprise: An aluminum layer, a treated modified copolymer layer for aluminum adhesion, a transparent oriented polypropylene core layer, a non-heat-sealable skin layer with high coefficient of friction, without treatment.

Processing history

Treatment level: 36 mN/m (ISO 8296, ASTM D 2578).

This material data has been provided by SIBUR.