General
Property | Temperature | Value | Comment |
---|---|---|---|
Density | 23.0 °C | 7.8 g/cm³ Show Material materials with Density of 7.8 g/cm³ | typical value |
Mechanical
Property | Temperature | Value | Comment |
---|---|---|---|
Charpy impact energy | -40.0 °C | 27 J Show Material materials with Charpy impact energy of 27 J | min. |
Elastic modulus | 23.0 °C | 190 - 210 GPa Show Material materials with Elastic modulus of 190 - 210 GPa | typical value |
Elongation | 23.0 °C | 16 % Show Material materials with Elongation of 16 % | min., A5.65 |
Poisson's ratio | 23.0 °C | 0.3 [-] Show Material materials with Poisson's ratio of 0.3 [-] | typical value |
Reduction of area | 23.0 °C | 32 % Show Material materials with Reduction of area of 32 % | min. |
Tensile strength | 23.0 °C | 700 - 850 MPa Show Material materials with Tensile strength of 700 - 850 MPa | |
Yield strength | 23.0 °C | 590 MPa Show Material materials with Yield strength of 590 MPa | min |
Thermal
Property | Temperature | Value | Comment |
---|---|---|---|
Coefficient of thermal expansion | 23.0 °C | 1.33E-5 1/K Show Material materials with Coefficient of thermal expansion of 1.33E-5 1/K | Typical for Manganese Steel |
Melting point | 1382 - 1529 °C Show Material materials with Melting point of 1382 - 1529 °C | Typical for Manganese Steel | |
Specific heat capacity | 23.0 °C | 510 - 553 J/(kg·K) Show Material materials with Specific heat capacity of 510 - 553 J/(kg·K) | Typical for Manganese Steel |
Thermal conductivity | 23.0 °C | 14 - 16 W/(m·K) Show Material materials with Thermal conductivity of 14 - 16 W/(m·K) | Typical for Manganese Steel |
Chemical properties
Property | Value | Comment | |
---|---|---|---|
Carbon | 0.16 - 0.22 % Show Material materials with Carbon of 0.16 - 0.22 % | ||
Iron | Balance | ||
Manganese | 1.3 - 1.7 % Show Material materials with Manganese of 1.3 - 1.7 % | ||
Phosphorus | 0.04 % Show Material materials with Phosphorus of 0.04 % | max. | |
Silicon | 0.1 - 0.5 % Show Material materials with Silicon of 0.1 - 0.5 % | ||
Sulfur | 0.035 % Show Material materials with Sulfur of 0.035 % | max. | |
Vanadium | 0.1 - 0.2 % Show Material materials with Vanadium of 0.1 - 0.2 % |
Technological properties
Property | ||
---|---|---|
Application areas | Typical applications are: Chrome plating, cylinders, conveyor rolls, hollow shafts, nuts, rings. | |
General machinability | Excellent | |
Welding | Excellent |