General
| Property | Temperature | Value | Comment |
|---|---|---|---|
Density | 23.0 °C | 1.3 g/cm³ Show Material materials with Density of 1.3 g/cm³ | ASTM D792 |
Mechanical
| Property | Temperature | Value | Comment | ||
|---|---|---|---|---|---|
Compressive modulus | 23.0 °C | 1.73 MPa Show Material materials with Compressive modulus of 1.73 MPa | ASTM D695 | ||
Compressive strength | 23.0 °C | 98.9 MPa Show Material materials with Compressive strength of 98.9 MPa | ASTM D695 | ||
Elastic modulus | 23.0 °C | 2.34 GPa Show Material materials with Elastic modulus of 2.34 GPa | ASTM D638 | ||
Elongation | 23.0 °C | 60 % Show Material materials with Elongation of 60 % | ASTM D638 | ||
Elongation at yield | 23.0 °C | 7.2 % Show Material materials with Elongation at yield of 7.2 % | ASTM D638 | ||
Flexural modulus | 23.0 °C | 1.7 GPa Show Material materials with Flexural modulus of 1.7 GPa | ASTM D790 | ||
Flexural yield strength | 23.0 °C | 91 MPa Show Material materials with Flexural yield strength of 91 MPa | ASTM D790 | ||
Impact strength, Izod notched, ASTM | 23.0 °C | 690 J/m Show Material materials with Impact strength, Izod notched, ASTM of 690 J/m | ASTM D256 | ||
Poisson's ratio | 23.0 °C | 0.42 [-] Show Material materials with Poisson's ratio of 0.42 [-] | ASTM E132 | ||
Shear strength | 23.0 °C | 62.7 MPa Show Material materials with Shear strength of 62.7 MPa | ASTM D732 | ||
Tensile strength | 23.0 °C | 69.6 MPa Show Material materials with Tensile strength of 69.6 MPa | ASTM D638 | ||
Yield strength | 23.0 °C | 69.6 MPa Show Material materials with Yield strength of 69.6 MPa | ASTM D638 | ||
Impact strength, Izod unnotched, ASTM | No Break, ASTM D256 | ||||
Thermal
| Property | Temperature | Value | Comment | ||
|---|---|---|---|---|---|
Coefficient of thermal expansion | 23.0 °C | 5.6E-5 1/K Show Material materials with Coefficient of thermal expansion of 5.6E-5 1/K | ASTM D696 | ||
Glass transition temperature | 220 °C Show Material materials with Glass transition temperature of 220 °C | ASTM E1356 | |||
Heat deflection temperature, 0.45 MPa | 214 °C Show Material materials with Heat deflection temperature, 0.45 MPa of 214 °C | ASTM D648 | |||
Thermal conductivity | 23.0 °C | 0.35 W/(m·K) Show Material materials with Thermal conductivity of 0.35 W/(m·K) | ASTM C177 | ||
Flammability | V-0 UL94 | ||||
Electrical
| Property | Temperature | Value | Comment |
|---|---|---|---|
Dielectric constant | 23.0 °C | 3.44 [-] Show Material materials with Dielectric constant of 3.44 [-] | ASTM D150, at 60 Hz |
Dielectric strength | 23.0 °C | 14 kV/mm Show Material materials with Dielectric strength of 14 kV/mm | ASTM D149 |
Electrical resistivity | 23.0 °C | 9.00E+13 Ω·m Show Material materials with Electrical resistivity of 9.00E+13 Ω·m |
Optical
| Property | Value | Comment |
|---|---|---|
Refractive index | 1.67 [-] Show Material materials with Refractive index of 1.67 [-] | ASTM D542 |
Technological properties
| Property | ||
|---|---|---|
| Application areas | Aerospace Applications, Connectors,Dental Applications, Food Service Applications, Hospital Goods, Medical Devices,Medical/Healthcare Applications, Plumbing Parts,Surgical Instruments | |
| Color | Transparent, Opaque, Black, Grey, Violet, Brown, Red, Yellow, Orange, Green, Violet | |
| Processing methods | Blow Molding, Extrusion, Film Extrusion, Profile Extrusion, Sheet Extrusion, Thermoforming - Injection Molding: Drying Temperature: 149°C, Drying Time: 2.5 hr, Rear Temperature: 321°C, Middle Temperature: 349°C, Front Temperature: 349°C, Melt Temperature: 343-388°C, Mold Temperature: 138-163°C, Back Pressure: 0.345-0.689 MPa, Screw Compression Ratio: 2.2:1 | |