Properties
General
| Property | Temperature | Value |
|---|---|---|
Density | 23.0 °C | 7.72 g/cm³ Show Material materials with Density of 7.72 g/cm³ |
Mechanical
| Property | Temperature | Value | Comment |
|---|---|---|---|
Elastic modulus | 23.0 °C | 195 GPa Show Material materials with Elastic modulus of 195 GPa | Typical for Austenitic Stainless Steel |
Elongation | 23.0 °C | 20 % Show Material materials with Elongation of 20 % | |
Poisson's ratio | 23.0 °C | 0.3 [-] Show Material materials with Poisson's ratio of 0.3 [-] | Typical for Austenitic Stainless Steel |
Reduction of area | 20.0 °C | 15 % Show Material materials with Reduction of area of 15 % | |
650.0 °C | 48 % Show Material materials with Reduction of area of 48 % | ||
760.0 °C | 14 % Show Material materials with Reduction of area of 14 % | ||
Shear modulus | 23.0 °C | 77 GPa Show Material materials with Shear modulus of 77 GPa | Typical for Austenitic Stainless Steel |
Tensile strength | 20.0 °C | 1030 MPa Show Material materials with Tensile strength of 1030 MPa | |
650.0 °C | 500 MPa Show Material materials with Tensile strength of 500 MPa | ||
760.0 °C | 340 MPa Show Material materials with Tensile strength of 340 MPa | ||
Yield strength | 20.0 °C | 520 MPa Show Material materials with Yield strength of 520 MPa | |
650.0 °C | 260 MPa Show Material materials with Yield strength of 260 MPa | ||
760.0 °C | 210 MPa Show Material materials with Yield strength of 210 MPa | ||
Thermal
| Property | Temperature | Value | Comment |
|---|---|---|---|
Coefficient of thermal expansion | 760.0 °C | 1.88E-5 1/K Show Material materials with Coefficient of thermal expansion of 1.88E-5 1/K | The mentioned value is between 20°C and the mentioned temperature |
Melting point | 1230 - 1480 °C Show Material materials with Melting point of 1230 - 1480 °C | Typical for Austenitic Stainless Steel | |
Specific heat capacity | 23.0 °C | 440 J/(kg·K) Show Material materials with Specific heat capacity of 440 J/(kg·K) | Typical for Austenitic Stainless Steel |
Thermal conductivity | 23.0 °C | 11 - 21 W/(m·K) Show Material materials with Thermal conductivity of 11 - 21 W/(m·K) | Typical for Austenitic Stainless Steel |
Electrical
| Property | Temperature | Value | Comment |
|---|---|---|---|
Electrical resistivity | 23.0 °C | 8.5E-7 Ω·m Show Material materials with Electrical resistivity of 8.5E-7 Ω·m | Typical for Austenitic Stainless Steel |
Chemical properties
| Property | Value | Comment |
|---|---|---|
Carbon | 0.65 - 0.75 % Show Material materials with Carbon of 0.65 - 0.75 % | |
Chromium | 20 - 22 % Show Material materials with Chromium of 20 - 22 % | |
Iron | 67.22 - 71.82 % Show Material materials with Iron of 67.22 - 71.82 % | Balance |
Manganese | 5.5 - 7 % Show Material materials with Manganese of 5.5 - 7 % | |
Nickel | 1.4 - 1.9 % Show Material materials with Nickel of 1.4 - 1.9 % | |
Nitrogen | 0.18 - 0.28 % Show Material materials with Nitrogen of 0.18 - 0.28 % | |
Phosphorus | 0.05 % Show Material materials with Phosphorus of 0.05 % | |
Silicon | 0.45 - 0.85 % Show Material materials with Silicon of 0.45 - 0.85 % | |
Sulfur | 0.025 - 0.065 % Show Material materials with Sulfur of 0.025 - 0.065 % |