General
Property | Temperature | Value | Comment |
---|---|---|---|
Density | 23.0 °C | 7.6 - 7.7 g/cm³ Show Material materials with Density of 7.6 - 7.7 g/cm³ | Typical for Martensitic Stainless Steel |
Mechanical
Property | Temperature | Value | Comment |
---|---|---|---|
Elastic modulus | 23.0 °C | 220 GPa Show Material materials with Elastic modulus of 220 GPa | Typical for Martensitic Stainless Steel |
Poisson's ratio | 23.0 °C | 0.3 [-] Show Material materials with Poisson's ratio of 0.3 [-] | Typical for Martensitic Stainless Steel |
Reduction of area | 20.0 °C | 53 % Show Material materials with Reduction of area of 53 % | |
540.0 °C | 44 % Show Material materials with Reduction of area of 44 % | ||
650.0 °C | 97 % Show Material materials with Reduction of area of 97 % | ||
Shear modulus | 23.0 °C | 77 GPa Show Material materials with Shear modulus of 77 GPa | Typical for Martensitic Stainless Steel |
Tensile strength | 20.0 °C | 920 MPa Show Material materials with Tensile strength of 920 MPa | |
540.0 °C | 270 MPa Show Material materials with Tensile strength of 270 MPa | ||
650.0 °C | 130 MPa Show Material materials with Tensile strength of 130 MPa | ||
Yield strength | 20.0 °C | 690 MPa Show Material materials with Yield strength of 690 MPa | |
540.0 °C | 220 MPa Show Material materials with Yield strength of 220 MPa | ||
650.0 °C | 110 MPa Show Material materials with Yield strength of 110 MPa | ||
Thermal
Property | Temperature | Value | Comment |
---|---|---|---|
Coefficient of thermal expansion | 23.0 °C | 1E-5 - 1.5E-5 1/K Show Material materials with Coefficient of thermal expansion of 1E-5 - 1.5E-5 1/K | Typical for Martensitic Stainless Steel |
Melting point | 1370 - 1530 °C Show Material materials with Melting point of 1370 - 1530 °C | Typical for Martensitic Stainless Steel | |
Specific heat capacity | 23.0 °C | 460 J/(kg·K) Show Material materials with Specific heat capacity of 460 J/(kg·K) | Typical for Martensitic Stainless Steel |
Thermal conductivity | 23.0 °C | 14 - 31 W/(m·K) Show Material materials with Thermal conductivity of 14 - 31 W/(m·K) | Typical for Martensitic Stainless Steel |
Electrical
Property | Temperature | Value | Comment |
---|---|---|---|
Electrical resistivity | 23.0 °C | 6E-7 Ω·m Show Material materials with Electrical resistivity of 6E-7 Ω·m | Typical for Martensitic Stainless Steel |
Chemical properties
Property | Value |
---|---|
Carbon | 0.35 - 0.45 % Show Material materials with Carbon of 0.35 - 0.45 % |
Chromium | 1.85 - 2.5 % Show Material materials with Chromium of 1.85 - 2.5 % |
Copper | 0.25 % Show Material materials with Copper of 0.25 % |
Iron | 91.85 - 94 % Show Material materials with Iron of 91.85 - 94 % |
Manganese | 0.2 - 0.4 % Show Material materials with Manganese of 0.2 - 0.4 % |
Molybdenum | 0.1 % Show Material materials with Molybdenum of 0.1 % |
Nickel | 0.25 % Show Material materials with Nickel of 0.25 % |
Phosphorus | 0.03 % Show Material materials with Phosphorus of 0.03 % |
Silicon | 3.6 - 4.2 % Show Material materials with Silicon of 3.6 - 4.2 % |
Sulfur | 0.04 % Show Material materials with Sulfur of 0.04 % |