General
Property | Temperature | Value |
---|---|---|
Density | 23.0 °C | 7.8 - 7.9 g/cm³ Show Material materials with Density of 7.8 - 7.9 g/cm³ |
Mechanical
Property | Temperature | Value | Comment |
---|---|---|---|
Elastic modulus | 23.0 °C | 205 GPa Show Material materials with Elastic modulus of 205 GPa | |
Elongation A5 | 23.0 °C | 10 - 25 % Show Material materials with Elongation A5 of 10 - 25 % | |
Hardness, Rockwell C | 23.0 °C | 30 [-] Show Material materials with Hardness, Rockwell C of 30 [-] | |
Poisson's ratio | 23.0 °C | 0.3 [-] Show Material materials with Poisson's ratio of 0.3 [-] | Typical for Austenitic Stainless Steel |
Reduction of area | 23.0 °C | 6 - 25 % Show Material materials with Reduction of area of 6 - 25 % | |
Shear modulus | 23.0 °C | 77 GPa Show Material materials with Shear modulus of 77 GPa | Typical for Austenitic Stainless Steel |
Tensile strength | 23.0 °C | 950 - 1190 MPa Show Material materials with Tensile strength of 950 - 1190 MPa | |
Yield strength | 23.0 °C | 580 - 880 MPa Show Material materials with Yield strength of 580 - 880 MPa |
Thermal
Property | Temperature | Value | Comment |
---|---|---|---|
Coefficient of thermal expansion | 100.0 °C | 1.55E-5 1/K Show Material materials with Coefficient of thermal expansion of 1.55E-5 1/K | The mentioned values are between 20°C and the mentioned temperature |
300.0 °C | 1.75E-5 1/K Show Material materials with Coefficient of thermal expansion of 1.75E-5 1/K | The mentioned values are between 20°C and the mentioned temperature | |
500.0 °C | 1.85E-5 1/K Show Material materials with Coefficient of thermal expansion of 1.85E-5 1/K | The mentioned values are between 20°C and the mentioned temperature | |
700.0 °C | 1.88E-5 1/K Show Material materials with Coefficient of thermal expansion of 1.88E-5 1/K | The mentioned values are between 20°C and the mentioned temperature | |
Melting point | 1230 - 1480 °C Show Material materials with Melting point of 1230 - 1480 °C | Typical for Austenitic Stainless Steel | |
Specific heat capacity | 23.0 °C | 500 J/(kg·K) Show Material materials with Specific heat capacity of 500 J/(kg·K) | |
Thermal conductivity | 23.0 °C | 14.5 W/(m·K) Show Material materials with Thermal conductivity of 14.5 W/(m·K) |
Electrical
Property | Temperature | Value | Comment |
---|---|---|---|
Electrical resistivity | 23.0 °C | 8.5E-7 Ω·m Show Material materials with Electrical resistivity of 8.5E-7 Ω·m | Typical for Austenitic Stainless Steel |
Chemical properties
Property | Value | Comment |
---|---|---|
Carbon | 0.45 - 0.55 % Show Material materials with Carbon of 0.45 - 0.55 % | |
Chromium | 20 - 22 % Show Material materials with Chromium of 20 - 22 % | |
Iron | 59.4 - 66.85 % Show Material materials with Iron of 59.4 - 66.85 % | Balance |
Manganese | 8 - 10 % Show Material materials with Manganese of 8 - 10 % | |
Nickel | 3.5 - 5.5 % Show Material materials with Nickel of 3.5 - 5.5 % | |
Nitrogen | 0.4 - 0.6 % Show Material materials with Nitrogen of 0.4 - 0.6 % | |
Phosphorus | 0.05 % Show Material materials with Phosphorus of 0.05 % | |
Silicon | 0.45 % Show Material materials with Silicon of 0.45 % | |
Sulfur | 0.03 % Show Material materials with Sulfur of 0.03 % | |
Tungsten | 0.8 - 1.5 % Show Material materials with Tungsten of 0.8 - 1.5 % |