Properties
General
| Property | Value | Comment |
|---|---|---|
Density | 7.8 - 7.9 g/cm³ Show Material materials with Density of 7.8 - 7.9 g/cm³ | Typical for Medium Carbon Steel |
Mechanical
| Property | Temperature | Value | Condition | Related Standards | Shape | Comment |
|---|---|---|---|---|---|---|
Elastic modulus | 200 - 215 GPa Show Material materials with Elastic modulus of 200 - 215 GPa | Typical for Medium Carbon Steel | ||||
Elongation | 10.2 % Show Material materials with Elongation of 10.2 % | Predicted Value, A200 | ||||
10.5 % Show Material materials with Elongation of 10.5 % | Predicted Value, A80 | |||||
10.7 % Show Material materials with Elongation of 10.7 % | Predicted Value, Transverse | |||||
13.1 % Show Material materials with Elongation of 13.1 % | Predicted Value, A50 | |||||
16.4 % Show Material materials with Elongation of 16.4 % | Predicted Value, A5 | |||||
19.1 % Show Material materials with Elongation of 19.1 % | Predicted Value, A80 Transverse | |||||
20 °C | 13 % Show Material materials with Elongation of 13 % | quenched and tempered (+QT) | ISO 683-2, EN 10083-3 | Bar, Forging, Sheet, Strip, Flat | ||
Hardness, Brinell | 254 [-] Show Material materials with Hardness, Brinell of 254 [-] | Predicted Value, Transverse | ||||
Poisson's ratio | 0.29 [-] Show Material materials with Poisson's ratio of 0.29 [-] | Typical for Medium Carbon Steel | ||||
Reduction of area | 42.5 % Show Material materials with Reduction of area of 42.5 % | Predicted Value, Transverse | ||||
20 °C | 50 % Show Material materials with Reduction of area of 50 % | quenched and tempered (+QT) | ISO 683-2, EN 10083-3 | Bar, Forging, Sheet, Strip, Flat | ||
Shear modulus | 75 - 80 GPa Show Material materials with Shear modulus of 75 - 80 GPa | Typical for Carbon Steel | ||||
Shear strength | 502.4 MPa Show Material materials with Shear strength of 502.4 MPa | Predicted Value | ||||
Tensile strength | 20 °C | 800 - 1150 MPa Show Material materials with Tensile strength of 800 - 1150 MPa | quenched and tempered (+QT) | ISO 683-2, EN 10083-3 | Bar, Forging, Sheet, Strip, Flat | |
20 °C | 800 - 950 MPa Show Material materials with Tensile strength of 800 - 950 MPa | quenched and tempered (+QT) | ISO 683-2, EN 10083-3 | Bar, Forging, Sheet, Strip, Flat | ||
20 °C | 950 - 1150 MPa Show Material materials with Tensile strength of 950 - 1150 MPa | quenched and tempered (+QT) | ISO 683-2, EN 10083-3 | Bar, Forging, Sheet, Strip, Flat | ||
20 °C | 950 MPa Show Material materials with Tensile strength of 950 MPa | quenched and tempered (+QT) | ISO 683-2, EN 10083-3 | Bar, Forging, Sheet, Strip, Flat | ||
Yield strength | 314 MPa Show Material materials with Yield strength of 314 MPa | Predicted Value, RP05 | ||||
320.1 MPa Show Material materials with Yield strength of 320.1 MPa | Predicted Value, RP1 | |||||
325.6 MPa Show Material materials with Yield strength of 325.6 MPa | Predicted Value, RP1 Transverse | |||||
491.8 MPa Show Material materials with Yield strength of 491.8 MPa | Predicted Value, Transverse | |||||
502.3 MPa Show Material materials with Yield strength of 502.3 MPa | Predicted Value, RP02 Transverse | |||||
725.9 MPa Show Material materials with Yield strength of 725.9 MPa | Predicted Value, RP002 | |||||
762.5 MPa Show Material materials with Yield strength of 762.5 MPa | Predicted Value, RP02 | |||||
20 °C | 650 MPa Show Material materials with Yield strength of 650 MPa | quenched and tempered (+QT) | ISO 683-2, EN 10083-3 | Bar, Forging, Sheet, Strip, Flat | ||
20 °C | 800 MPa Show Material materials with Yield strength of 800 MPa | quenched and tempered (+QT) | ISO 683-2, EN 10083-3 | Bar, Forging, Sheet, Strip, Flat |
Thermal
| Property | Value | Comment |
|---|---|---|
Coefficient of thermal expansion | 1.32e-05 1/K Show Material materials with Coefficient of thermal expansion of 1.32e-05 1/K | Typical for Medium Carbon Steel |
Max service temperature | 305.9 °C Show Material materials with Max service temperature of 305.9 °C | Predicted Value, Long |
500 °C Show Material materials with Max service temperature of 500 °C | Typical for Carbon Steel | |
Melting point | 1380 - 1514 °C Show Material materials with Melting point of 1380 - 1514 °C | Typical for Medium Carbon Steel |
Specific heat capacity | 470 - 520 J/(kg·K) Show Material materials with Specific heat capacity of 470 - 520 J/(kg·K) | Typical for Medium Carbon Steel |
Thermal conductivity | 21 - 52 W/(m·K) Show Material materials with Thermal conductivity of 21 - 52 W/(m·K) | Typical for Medium Carbon Steel |
Electrical
| Property | Value | Comment |
|---|---|---|
Electrical conductivity | 7 S/m Show Material materials with Electrical conductivity of 7 S/m | Predicted Value |
Electrical resistivity | 1.43e-07 - 1.74e-07 Ω·m Show Material materials with Electrical resistivity of 1.43e-07 - 1.74e-07 Ω·m | Typical for Carbon Steel |
Chemical properties
| Property | Value | Condition | Related Standards | Shape |
|---|---|---|---|---|
Boron | 0.0008 - 0.005 % Show Material materials with Boron of 0.0008 - 0.005 % | quenched and tempered (+QT) | ISO 683-2, EN 10083-3 | Bar, Forging, Sheet, Strip, Flat |
0.001 - 0.005 % Show Material materials with Boron of 0.001 - 0.005 % | quenched and tempered (+QT) | EN 10083-3, ISO 683-2 | Bar, Forging, Sheet, Strip, Flat | |
Carbon | 0.27 - 0.33 % Show Material materials with Carbon of 0.27 - 0.33 % | quenched and tempered (+QT) | ISO 683-2, EN 10083-3 | Bar, Forging, Sheet, Strip, Flat |
Copper | 0.4 % Show Material materials with Copper of 0.4 % | quenched and tempered (+QT) | ISO 683-2, EN 10083-3 | Bar, Forging, Sheet, Strip, Flat |
Manganese | 1.15 - 1.45 % Show Material materials with Manganese of 1.15 - 1.45 % | quenched and tempered (+QT) | ISO 683-2, EN 10083-3 | Bar, Forging, Sheet, Strip, Flat |
Phosphorus | 0.025 % Show Material materials with Phosphorus of 0.025 % | quenched and tempered (+QT) | ISO 683-2, EN 10083-3 | Bar, Forging, Sheet, Strip, Flat |
Silicon | 0.4 % Show Material materials with Silicon of 0.4 % | quenched and tempered (+QT) | ISO 683-2, EN 10083-3 | Bar, Forging, Sheet, Strip, Flat |
Sulfur | 0.035 % Show Material materials with Sulfur of 0.035 % | quenched and tempered (+QT) | ISO 683-2, EN 10083-3 | Bar, Forging, Sheet, Strip, Flat |