Properties
General
| Property | Value | Comment |
|---|---|---|
Density | 7.8 g/cm³ Show Material materials with Density of 7.8 g/cm³ | Typical for Steel |
Mechanical
| Property | Temperature | Value | Condition | Related Standards | Shape | Comment |
|---|---|---|---|---|---|---|
Elastic modulus | 190 - 210 GPa Show Material materials with Elastic modulus of 190 - 210 GPa | Typical for Steel | ||||
Elongation | 9.6 % Show Material materials with Elongation of 9.6 % | Predicted Value, A80 | ||||
10.3 % Show Material materials with Elongation of 10.3 % | Predicted Value, A200 | |||||
10.6 % Show Material materials with Elongation of 10.6 % | Predicted Value, Transverse | |||||
11.2 % Show Material materials with Elongation of 11.2 % | Predicted Value, A50 | |||||
16.1 % Show Material materials with Elongation of 16.1 % | Predicted Value, A5 | |||||
19.3 % Show Material materials with Elongation of 19.3 % | Predicted Value, A80 Transverse | |||||
20 °C | 13 % Show Material materials with Elongation of 13 % | quenched and tempered (+QT) | ISO 683-2, EN 10083-3 | Bar, Forging, Sheet, Strip, Flat | ||
Hardness, Brinell | 260 [-] Show Material materials with Hardness, Brinell of 260 [-] | Predicted Value, Transverse | ||||
Poisson's ratio | 0.3 [-] Show Material materials with Poisson's ratio of 0.3 [-] | Typical for Steel | ||||
Reduction of area | 42.7 % Show Material materials with Reduction of area of 42.7 % | Predicted Value, Transverse | ||||
20 °C | 50 % Show Material materials with Reduction of area of 50 % | quenched and tempered (+QT) | ISO 683-2, EN 10083-3 | Bar, Forging, Sheet, Strip, Flat | ||
Shear modulus | 80.3 GPa Show Material materials with Shear modulus of 80.3 GPa | Predicted Value | ||||
Shear strength | 532 MPa Show Material materials with Shear strength of 532 MPa | Predicted Value | ||||
Tensile strength | 20 °C | 900 - 1300 MPa Show Material materials with Tensile strength of 900 - 1300 MPa | quenched and tempered (+QT) | ISO 683-2, EN 10083-3 | Bar, Forging, Sheet, Strip, Flat | |
20 °C | 900 - 1200 MPa Show Material materials with Tensile strength of 900 - 1200 MPa | quenched and tempered (+QT) | ISO 683-2, EN 10083-3 | Bar, Forging, Sheet, Strip, Flat | ||
20 °C | 900 - 1100 MPa Show Material materials with Tensile strength of 900 - 1100 MPa | quenched and tempered (+QT) | ISO 683-2, EN 10083-3 | Bar, Forging, Sheet, Strip, Flat | ||
20 °C | 950 - 1300 MPa Show Material materials with Tensile strength of 950 - 1300 MPa | quenched and tempered (+QT) | ISO 683-2, EN 10083-3 | Bar, Forging, Sheet, Strip, Flat | ||
20 °C | 950 - 1200 MPa Show Material materials with Tensile strength of 950 - 1200 MPa | quenched and tempered (+QT) | ISO 683-2, EN 10083-3 | Bar, Forging, Sheet, Strip, Flat | ||
20 °C | 950 - 1100 MPa Show Material materials with Tensile strength of 950 - 1100 MPa | quenched and tempered (+QT) | ISO 683-2, EN 10083-3 | Bar, Forging, Sheet, Strip, Flat | ||
20 °C | 1050 - 1300 MPa Show Material materials with Tensile strength of 1050 - 1300 MPa | quenched and tempered (+QT) | ISO 683-2, EN 10083-3 | Bar, Forging, Sheet, Strip, Flat | ||
20 °C | 1050 - 1200 MPa Show Material materials with Tensile strength of 1050 - 1200 MPa | quenched and tempered (+QT) | ISO 683-2, EN 10083-3 | Bar, Forging, Sheet, Strip, Flat | ||
20 °C | 1050 - 1100 MPa Show Material materials with Tensile strength of 1050 - 1100 MPa | quenched and tempered (+QT) | ISO 683-2, EN 10083-3 | Bar, Forging, Sheet, Strip, Flat | ||
Yield strength | 318.7 MPa Show Material materials with Yield strength of 318.7 MPa | Predicted Value, RP1 | ||||
326.9 MPa Show Material materials with Yield strength of 326.9 MPa | Predicted Value, RP1 Transverse | |||||
347.3 MPa Show Material materials with Yield strength of 347.3 MPa | Predicted Value, RP05 | |||||
517.9 MPa Show Material materials with Yield strength of 517.9 MPa | Predicted Value, Transverse | |||||
573.8 MPa Show Material materials with Yield strength of 573.8 MPa | Predicted Value, RP02 Transverse | |||||
745.8 MPa Show Material materials with Yield strength of 745.8 MPa | Predicted Value, RP002 | |||||
866.7 MPa Show Material materials with Yield strength of 866.7 MPa | Predicted Value, RP02 | |||||
20 °C | 750 MPa Show Material materials with Yield strength of 750 MPa | quenched and tempered (+QT) | ISO 683-2, EN 10083-3 | Bar, Forging, Sheet, Strip, Flat | ||
20 °C | 800 MPa Show Material materials with Yield strength of 800 MPa | quenched and tempered (+QT) | ISO 683-2, EN 10083-3 | Bar, Forging, Sheet, Strip, Flat | ||
20 °C | 850 MPa Show Material materials with Yield strength of 850 MPa | quenched and tempered (+QT) | ISO 683-2, EN 10083-3 | Bar, Forging, Sheet, Strip, Flat |
Thermal
| Property | Value | Comment |
|---|---|---|
Coefficient of thermal expansion | 12.21 1/K Show Material materials with Coefficient of thermal expansion of 12.21 1/K | Predicted Value |
Max service temperature | 287.1 °C Show Material materials with Max service temperature of 287.1 °C | Predicted Value, Long |
Specific heat capacity | 456.8 J/(kg·K) Show Material materials with Specific heat capacity of 456.8 J/(kg·K) | Predicted Value |
Thermal conductivity | 36.54 W/(m·K) Show Material materials with Thermal conductivity of 36.54 W/(m·K) | Predicted Value |
Electrical
Chemical properties
| Property | Value | Condition | Related Standards | Shape |
|---|---|---|---|---|
Boron | 0.0008 - 0.005 % Show Material materials with Boron of 0.0008 - 0.005 % | quenched and tempered (+QT) | ISO 683-2, EN 10083-3 | Bar, Forging, Sheet, Strip, Flat |
0.001 - 0.005 % Show Material materials with Boron of 0.001 - 0.005 % | quenched and tempered (+QT) | EN 10083-3, ISO 683-2 | Bar, Forging, Sheet, Strip, Flat | |
Carbon | 0.3 - 0.36 % Show Material materials with Carbon of 0.3 - 0.36 % | quenched and tempered (+QT) | ISO 683-2, EN 10083-3 | Bar, Forging, Sheet, Strip, Flat |
Chromium | 0.3 - 0.6 % Show Material materials with Chromium of 0.3 - 0.6 % | quenched and tempered (+QT) | ISO 683-2, EN 10083-3 | Bar, Forging, Sheet, Strip, Flat |
Copper | 0.4 % Show Material materials with Copper of 0.4 % | quenched and tempered (+QT) | ISO 683-2, EN 10083-3 | Bar, Forging, Sheet, Strip, Flat |
Manganese | 1.2 - 1.5 % Show Material materials with Manganese of 1.2 - 1.5 % | quenched and tempered (+QT) | ISO 683-2, EN 10083-3 | Bar, Forging, Sheet, Strip, Flat |
Phosphorus | 0.025 % Show Material materials with Phosphorus of 0.025 % | quenched and tempered (+QT) | ISO 683-2, EN 10083-3 | Bar, Forging, Sheet, Strip, Flat |
Silicon | 0.4 % Show Material materials with Silicon of 0.4 % | quenched and tempered (+QT) | ISO 683-2, EN 10083-3 | Bar, Forging, Sheet, Strip, Flat |
Sulfur | 0.035 % Show Material materials with Sulfur of 0.035 % | quenched and tempered (+QT) | ISO 683-2, EN 10083-3 | Bar, Forging, Sheet, Strip, Flat |