EN 10203 Grade TH435 cold rolled

Want to keep this datasheet? Save it now in your required format

Description

TH 435 is a single cold rolled band (black plate in coils) of soft unalloyed steel and in the surface qualities plain, stone finish and matt for conventional packaging sheet. The band is produced in thicknesses of 0,17 to 0,49 mm in steps of 0,005 mm. The surface is oiled in order to avoid corrosion. The strip is applicated for the production of - electrolytically tinned tinplate Tin used for coating has to show a purity grade of 99,85%. Preferred tin plating values (double-sided) are: 1,0 1,4 2,0 2,8 4,0 5,0 5,6 8,4 11,2 14,0 15,1 g/m² Tinplate is also delivered diferentially coated. In this case is necessary a special designation . Appearance of the tinplate surface is determined by the surface characteristics of the basic material and type of tincoating. Available surface qualities: bright, stone finish, silver matt and matt - electrolytically special chromed steel (ECCS) Total Cr-content used for coating consists of metallic chromium and chromium oxides. The mean coating weight of metallic chromium accounts for 50 to 140 mg/m² and 7 to 35 mg/m² for chromium oxides. Surface appearance of ECCS which follows from the application of work rolls of a special surface texture during the last cold rerolling steps is determined by the surface characteristics of the basic material. Available surface qualities: matt, plain, stone finish For the choice of surface refined extra-fine sheets has to be considered the final consumption purpose, e.g. requirements, such as suitability for punching, drawing, folding, beading, welding and soldering. Application of extra-fine sheets: - cans, jugs, canister, buckets - household articles, boxes, closures - ceiling elements, fittings, pressure plates etc.

Related Standards

Equivalent Materials

This material data has been provided by WIAM.

All metrics apply to room temperature unless otherwise stated. SI units used unless otherwise stated.
Equivalent standards are similar to one or more standards provided by the supplier. Some equivalent standards may be stricter whereas others may be outside the bounds of the original standard.

Ashby charts

See where falls on the material property chart for against in your materials selection and design process. Our Ashby charts are interactive with more technical data upon clicking. Sign up to get access to this premium feature for free.

Properties

General

PropertyTemperatureValueComment

Density

23.0 °C

7.8 - 7.9 g/cm³

Show Material materials with Density of 7.8 - 7.9 g/cm³

Typical for Low Carbon Steel

Mechanical

PropertyTemperatureValueComment

Elastic modulus

23.0 °C

200 - 215 GPa

Show Material materials with Elastic modulus of 200 - 215 GPa

Typical for Low Carbon Steel

Hardness, Rockwell T

20.0 °C

64 - 65 [-]

Show Material materials with Hardness, Rockwell T of 64 - 65 [-]

Poisson's ratio

23.0 °C

0.29 [-]

Show Material materials with Poisson's ratio of 0.29 [-]

Typical for Low Carbon Steel

Shear modulus

23.0 °C

82 GPa

Show Material materials with Shear modulus of 82 GPa

Typical for Low Carbon Steel

Tensile strength

20.0 °C

460 MPa

Show Material materials with Tensile strength of 460 MPa

Yield strength Rp0.2

20.0 °C

435 MPa

Show Material materials with Yield strength Rp0.2 of 435 MPa

Thermal

PropertyTemperatureValueComment

Coefficient of thermal expansion

23.0 °C

1.32E-5 - 1.38E-5 1/K

Show Material materials with Coefficient of thermal expansion of 1.32E-5 - 1.38E-5 1/K

Typical for Low Carbon Steel

Max service temperature

500 °C

Show Material materials with Max service temperature of 500 °C

Typical for Carbon Steel

Melting point

1480 - 1526 °C

Show Material materials with Melting point of 1480 - 1526 °C

Typical for Low Carbon Steel

Specific heat capacity

23.0 °C

465 J/(kg·K)

Show Material materials with Specific heat capacity of 465 J/(kg·K)

Typical for Low Carbon Steel

Thermal conductivity

23.0 °C

25 - 93 W/(m·K)

Show Material materials with Thermal conductivity of 25 - 93 W/(m·K)

Typical for Low Carbon Steel

Electrical

PropertyTemperatureValueComment

Electrical resistivity

23.0 °C

1.43E-7 - 1.74E-7 Ω·m

Show Material materials with Electrical resistivity of 1.43E-7 - 1.74E-7 Ω·m

Typical for Carbon Steel

Magnetic

PropertyValueComment

Curie temperature

770 °C

Show Material materials with Curie temperature of 770 °C

Typical for Low Carbon Steel