Property | Temperature | Value |
---|---|---|
Density | 20.0 °C | 7.7 g/cm³ Show Material materials with Density of 7.7 g/cm³ |
Mechanical
Property | Temperature | Value | Comment |
---|---|---|---|
Elastic modulus | 20.0 °C | 220 GPa Show Material materials with Elastic modulus of 220 GPa | |
100.0 °C | 215 GPa Show Material materials with Elastic modulus of 215 GPa | ||
200.0 °C | 210 GPa Show Material materials with Elastic modulus of 210 GPa | ||
300.0 °C | 205 GPa Show Material materials with Elastic modulus of 205 GPa | ||
400.0 °C | 195 GPa Show Material materials with Elastic modulus of 195 GPa | ||
Elongation | 20.0 °C | 12 % Show Material materials with Elongation of 12 % | |
Elongation A80 | 20.0 °C | 12 % Show Material materials with Elongation A80 of 12 % | |
Elongation A80, transverse | 20.0 °C | 12 % Show Material materials with Elongation A80, transverse of 12 % | |
Elongation, transverse | 20.0 °C | 12 % Show Material materials with Elongation, transverse of 12 % | |
Poisson's ratio | 23.0 °C | 0.3 [-] Show Material materials with Poisson's ratio of 0.3 [-] | Typical for Ferritic Stainless Steel |
Shear modulus | 23.0 °C | 77 GPa Show Material materials with Shear modulus of 77 GPa | Typical for Ferritic Stainless Steel |
Tensile strength | 20.0 °C | 500 - 750 MPa Show Material materials with Tensile strength of 500 - 750 MPa | |
Tensile strength, transverse | 20.0 °C | 500 - 750 MPa Show Material materials with Tensile strength, transverse of 500 - 750 MPa | |
Yield strength Rp0.2 | 20.0 °C | 330 MPa Show Material materials with Yield strength Rp0.2 of 330 MPa | |
Yield strength Rp0.2, transverse | 20.0 °C | 350 MPa Show Material materials with Yield strength Rp0.2, transverse of 350 MPa |
Thermal
Property | Temperature | Value | Comment |
---|---|---|---|
Coefficient of thermal expansion | 100.0 °C | 1.02E-5 1/K Show Material materials with Coefficient of thermal expansion of 1.02E-5 1/K | |
300.0 °C | 1.08E-5 1/K Show Material materials with Coefficient of thermal expansion of 1.08E-5 1/K | ||
Melting point | 1425 - 1530 °C Show Material materials with Melting point of 1425 - 1530 °C | Typical for Ferritic Stainless Steel | |
Specific heat capacity | 20.0 °C | 460 J/(kg·K) Show Material materials with Specific heat capacity of 460 J/(kg·K) | |
Thermal conductivity | 20.0 °C | 30 W/(m·K) Show Material materials with Thermal conductivity of 30 W/(m·K) |
Electrical
Property | Temperature | Value |
---|---|---|
Electrical resistivity | 20.0 °C | 7E-7 Ω·m Show Material materials with Electrical resistivity of 7E-7 Ω·m |
Chemical properties
Property | Value |
---|---|
Carbon | 0.08 % Show Material materials with Carbon of 0.08 % |
Chromium | 16 - 18 % Show Material materials with Chromium of 16 - 18 % |
Manganese | 1 % Show Material materials with Manganese of 1 % |
Nickel | 1.2 - 1.6 % Show Material materials with Nickel of 1.2 - 1.6 % |
Phosphorus | 0.04 % Show Material materials with Phosphorus of 0.04 % |
Silicon | 1 % Show Material materials with Silicon of 1 % |
Sulfur | 0.015 % Show Material materials with Sulfur of 0.015 % |