EN 10088-1 Grade X1CrNiSi18-15-4 solution annealed (+AT)

Want to keep this datasheet? Save it now in your required format

Description

The austenitic material X1CrNiSi18-15-4 isavailable in solution annealed condition. It is used in the form of warm rolled sheet. It is resistant to intercrystalline corrosion also in welded condition.

Related Standards

Equivalent Materials

This material data has been provided by WIAM.

All metrics apply to room temperature unless otherwise stated. SI units used unless otherwise stated.
Equivalent standards are similar to one or more standards provided by the supplier. Some equivalent standards may be stricter whereas others may be outside the bounds of the original standard.

Ashby charts

See where falls on the material property chart for against in your materials selection and design process. Our Ashby charts are interactive with more technical data upon clicking. Sign up to get access to this premium feature for free.

Properties

General

PropertyTemperatureValue

Density

20.0 °C

7.7 g/cm³

Show Material materials with Density of 7.7 g/cm³

Mechanical

PropertyTemperatureValueComment

Elastic modulus

20.0 °C

200 GPa

Show Material materials with Elastic modulus of 200 GPa

100.0 °C

194 GPa

Show Material materials with Elastic modulus of 194 GPa

200.0 °C

186 GPa

Show Material materials with Elastic modulus of 186 GPa

300.0 °C

179 GPa

Show Material materials with Elastic modulus of 179 GPa

400.0 °C

172 GPa

Show Material materials with Elastic modulus of 172 GPa

500.0 °C

165 GPa

Show Material materials with Elastic modulus of 165 GPa

Elongation

20.0 °C

40 %

Show Material materials with Elongation of 40 %

Elongation A80, transverse

20.0 °C

40 %

Show Material materials with Elongation A80, transverse of 40 %

Elongation, transverse

20.0 °C

30 - 40 %

Show Material materials with Elongation, transverse of 30 - 40 %

Hardness, Brinell

20.0 °C

230 [-]

Show Material materials with Hardness, Brinell of 230 [-]

Hardness, Brinell, trans

20.0 °C

230 [-]

Show Material materials with Hardness, Brinell, trans of 230 [-]

Poisson's ratio

23.0 °C

0.3 [-]

Show Material materials with Poisson's ratio of 0.3 [-]

Typical for Austenitic Stainless Steel

Shear modulus

23.0 °C

77 GPa

Show Material materials with Shear modulus of 77 GPa

Typical for Austenitic Stainless Steel

Tensile strength

20.0 °C

530 - 730 MPa

Show Material materials with Tensile strength of 530 - 730 MPa

Tensile strength, transverse

20.0 °C

530 - 730 MPa

Show Material materials with Tensile strength, transverse of 530 - 730 MPa

Yield strength Rp0.2

20.0 °C

210 MPa

Show Material materials with Yield strength Rp0.2 of 210 MPa

100.0 °C

185 MPa

Show Material materials with Yield strength Rp0.2 of 185 MPa

150.0 °C

160 MPa

Show Material materials with Yield strength Rp0.2 of 160 MPa

200.0 °C

145 MPa

Show Material materials with Yield strength Rp0.2 of 145 MPa

250.0 °C

135 MPa

Show Material materials with Yield strength Rp0.2 of 135 MPa

300.0 °C

125 MPa

Show Material materials with Yield strength Rp0.2 of 125 MPa

350.0 °C

120 MPa

Show Material materials with Yield strength Rp0.2 of 120 MPa

400.0 °C

115 MPa

Show Material materials with Yield strength Rp0.2 of 115 MPa

Unlock all property charts

Yield strength Rp0.2, transverse

20.0 °C

210 - 220 MPa

Show Material materials with Yield strength Rp0.2, transverse of 210 - 220 MPa

Yield strength Rp1.0

20.0 °C

240 MPa

Show Material materials with Yield strength Rp1.0 of 240 MPa

100.0 °C

210 MPa

Show Material materials with Yield strength Rp1.0 of 210 MPa

150.0 °C

190 MPa

Show Material materials with Yield strength Rp1.0 of 190 MPa

200.0 °C

175 MPa

Show Material materials with Yield strength Rp1.0 of 175 MPa

250.0 °C

165 MPa

Show Material materials with Yield strength Rp1.0 of 165 MPa

300.0 °C

155 MPa

Show Material materials with Yield strength Rp1.0 of 155 MPa

350.0 °C

150 MPa

Show Material materials with Yield strength Rp1.0 of 150 MPa

Unlock all property charts

Yield strength Rp1.0, transverse

20.0 °C

240 - 260 MPa

Show Material materials with Yield strength Rp1.0, transverse of 240 - 260 MPa

Thermal

PropertyTemperatureValueComment

Coefficient of thermal expansion

100.0 °C

1.65E-5 1/K

Show Material materials with Coefficient of thermal expansion of 1.65E-5 1/K

Melting point

1230 - 1480 °C

Show Material materials with Melting point of 1230 - 1480 °C

Typical for Austenitic Stainless Steel

Specific heat capacity

23.0 °C

440 J/(kg·K)

Show Material materials with Specific heat capacity of 440 J/(kg·K)

Typical for Austenitic Stainless Steel

Thermal conductivity

20.0 °C

14 W/(m·K)

Show Material materials with Thermal conductivity of 14 W/(m·K)

Electrical

PropertyTemperatureValueComment

Electrical resistivity

23.0 °C

8.5E-7 Ω·m

Show Material materials with Electrical resistivity of 8.5E-7 Ω·m

Typical for Austenitic Stainless Steel

Chemical properties

PropertyValue

Carbon

0.015 %

Show Material materials with Carbon of 0.015 %

Chromium

16.5 - 18.5 %

Show Material materials with Chromium of 16.5 - 18.5 %

Manganese

2 %

Show Material materials with Manganese of 2 %

Molybdenum

0.2 %

Show Material materials with Molybdenum of 0.2 %

Nickel

14 - 16 %

Show Material materials with Nickel of 14 - 16 %

Nitrogen

0.11 %

Show Material materials with Nitrogen of 0.11 %

Phosphorus

0.03 %

Show Material materials with Phosphorus of 0.03 %

Silicon

3.7 - 4.5 %

Show Material materials with Silicon of 3.7 - 4.5 %

Sulfur

0.01 %

Show Material materials with Sulfur of 0.01 %