General
Property | Value | Comment |
---|---|---|
Density | 7.8 - 7.9 g/cm³ Show Material materials with Density of 7.8 - 7.9 g/cm³ | Typical for Chromium Molybdenum Steel |
Mechanical
Property | Temperature | Value | Condition | Related Standards | Shape | Comment |
---|---|---|---|---|---|---|
Elastic modulus | 200 - 215 GPa Show Material materials with Elastic modulus of 200 - 215 GPa | Typical for Chromium Molybdenum Steel | ||||
Elongation | 17.5 % Show Material materials with Elongation of 17.5 % | Predicted Value, A80 | ||||
17.5 % Show Material materials with Elongation of 17.5 % | Predicted Value, A200 | |||||
20.2 % Show Material materials with Elongation of 20.2 % | Predicted Value, A80 Transverse | |||||
21.2 % Show Material materials with Elongation of 21.2 % | Predicted Value, A5 | |||||
24.1 % Show Material materials with Elongation of 24.1 % | Predicted Value, A50 | |||||
20 °C | 20 % Show Material materials with Elongation of 20 % | quenched and tempered (+QT) | EN 10028-2 | Flat | Transverse | |
20 °C | 20 % Show Material materials with Elongation of 20 % | quenched and tempered (+QT) | EN 10028-2 | Flat | ||
Hardness, Brinell | 249 [-] Show Material materials with Hardness, Brinell of 249 [-] | Predicted Value, Transverse | ||||
Poisson's ratio | 0.29 [-] Show Material materials with Poisson's ratio of 0.29 [-] | Typical for Chromium Molybdenum Steel | ||||
Reduction of area | 41.6 % Show Material materials with Reduction of area of 41.6 % | Predicted Value | ||||
44.2 % Show Material materials with Reduction of area of 44.2 % | Predicted Value, Transverse | |||||
Shear modulus | 79.3 GPa Show Material materials with Shear modulus of 79.3 GPa | Predicted Value | ||||
Shear strength | 674.4 MPa Show Material materials with Shear strength of 674.4 MPa | Predicted Value | ||||
Tensile strength | 20 °C | 490 - 690 MPa Show Material materials with Tensile strength of 490 - 690 MPa | quenched and tempered (+QT) | EN 10028-2 | Flat | Transverse |
20 °C | 490 - 680 MPa Show Material materials with Tensile strength of 490 - 680 MPa | quenched and tempered (+QT) | EN 10028-2 | Flat | Transverse | |
20 °C | 490 - 670 MPa Show Material materials with Tensile strength of 490 - 670 MPa | quenched and tempered (+QT) | EN 10028-2 | Flat | Transverse | |
20 °C | 490 - 690 MPa Show Material materials with Tensile strength of 490 - 690 MPa | quenched and tempered (+QT) | EN 10028-2 | Flat | ||
20 °C | 490 - 680 MPa Show Material materials with Tensile strength of 490 - 680 MPa | quenched and tempered (+QT) | EN 10028-2 | Flat | ||
20 °C | 490 - 670 MPa Show Material materials with Tensile strength of 490 - 670 MPa | quenched and tempered (+QT) | EN 10028-2 | Flat | ||
20 °C | 500 - 690 MPa Show Material materials with Tensile strength of 500 - 690 MPa | quenched and tempered (+QT) | EN 10028-2 | Flat | Transverse | |
20 °C | 500 - 680 MPa Show Material materials with Tensile strength of 500 - 680 MPa | quenched and tempered (+QT) | EN 10028-2 | Flat | Transverse | |
20 °C | 500 - 670 MPa Show Material materials with Tensile strength of 500 - 670 MPa | quenched and tempered (+QT) | EN 10028-2 | Flat | Transverse | |
20 °C | 500 - 690 MPa Show Material materials with Tensile strength of 500 - 690 MPa | quenched and tempered (+QT) | EN 10028-2 | Flat | ||
20 °C | 500 - 680 MPa Show Material materials with Tensile strength of 500 - 680 MPa | quenched and tempered (+QT) | EN 10028-2 | Flat | ||
20 °C | 500 - 670 MPa Show Material materials with Tensile strength of 500 - 670 MPa | quenched and tempered (+QT) | EN 10028-2 | Flat | ||
20 °C | 510 - 690 MPa Show Material materials with Tensile strength of 510 - 690 MPa | quenched and tempered (+QT) | EN 10028-2 | Flat | Transverse | |
20 °C | 510 - 680 MPa Show Material materials with Tensile strength of 510 - 680 MPa | quenched and tempered (+QT) | EN 10028-2 | Flat | Transverse | |
20 °C | 510 - 670 MPa Show Material materials with Tensile strength of 510 - 670 MPa | quenched and tempered (+QT) | EN 10028-2 | Flat | Transverse | |
20 °C | 510 - 690 MPa Show Material materials with Tensile strength of 510 - 690 MPa | quenched and tempered (+QT) | EN 10028-2 | Flat | ||
20 °C | 510 - 680 MPa Show Material materials with Tensile strength of 510 - 680 MPa | quenched and tempered (+QT) | EN 10028-2 | Flat | ||
20 °C | 510 - 670 MPa Show Material materials with Tensile strength of 510 - 670 MPa | quenched and tempered (+QT) | EN 10028-2 | Flat | ||
Yield strength | 260.1 MPa Show Material materials with Yield strength of 260.1 MPa | Predicted Value, RP1 | ||||
321.6 MPa Show Material materials with Yield strength of 321.6 MPa | Predicted Value, RP1 Transverse | |||||
359.3 MPa Show Material materials with Yield strength of 359.3 MPa | Predicted Value, RP05 | |||||
464.2 MPa Show Material materials with Yield strength of 464.2 MPa | Predicted Value, RP02 Transverse | |||||
529.9 MPa Show Material materials with Yield strength of 529.9 MPa | Predicted Value, RP002 | |||||
20 °C | 380 MPa Show Material materials with Yield strength of 380 MPa | quenched and tempered (+QT) | EN 10028-2 | Flat | Transverse | |
20 °C | 380 MPa Show Material materials with Yield strength of 380 MPa | quenched and tempered (+QT) | EN 10028-2 | Flat | ||
20 °C | 390 MPa Show Material materials with Yield strength of 390 MPa | quenched and tempered (+QT) | EN 10028-2 | Flat | Transverse | |
20 °C | 390 MPa Show Material materials with Yield strength of 390 MPa | quenched and tempered (+QT) | EN 10028-2 | Flat | ||
20 °C | 400 MPa Show Material materials with Yield strength of 400 MPa | quenched and tempered (+QT) | EN 10028-2 | Flat | Transverse | |
20 °C | 400 MPa Show Material materials with Yield strength of 400 MPa | quenched and tempered (+QT) | EN 10028-2 | Flat | ||
50 °C | 365 MPa Show Material materials with Yield strength of 365 MPa | quenched and tempered (+QT) | EN 10028-2 | Flat | RP02 | |
50 °C | 375 MPa Show Material materials with Yield strength of 375 MPa | quenched and tempered (+QT) | EN 10028-2 | Flat | RP02 | |
50 °C | 384 MPa Show Material materials with Yield strength of 384 MPa | quenched and tempered (+QT) | EN 10028-2 | Flat | RP02 | |
100 °C | 346 MPa Show Material materials with Yield strength of 346 MPa | quenched and tempered (+QT) | EN 10028-2 | Flat | RP02 | |
100 °C | 355 MPa Show Material materials with Yield strength of 355 MPa | quenched and tempered (+QT) | EN 10028-2 | Flat | RP02 | |
100 °C | 364 MPa Show Material materials with Yield strength of 364 MPa | quenched and tempered (+QT) | EN 10028-2 | Flat | RP02 | |
150 °C | 334 MPa Show Material materials with Yield strength of 334 MPa | quenched and tempered (+QT) | EN 10028-2 | Flat | RP02 | |
150 °C | 343 MPa Show Material materials with Yield strength of 343 MPa | quenched and tempered (+QT) | EN 10028-2 | Flat | RP02 | |
150 °C | 352 MPa Show Material materials with Yield strength of 352 MPa | quenched and tempered (+QT) | EN 10028-2 | Flat | RP02 | |
200 °C | 326 MPa Show Material materials with Yield strength of 326 MPa | quenched and tempered (+QT) | EN 10028-2 | Flat | RP02 | |
200 °C | 335 MPa Show Material materials with Yield strength of 335 MPa | quenched and tempered (+QT) | EN 10028-2 | Flat | RP02 | |
200 °C | 344 MPa Show Material materials with Yield strength of 344 MPa | quenched and tempered (+QT) | EN 10028-2 | Flat | RP02 | |
250 °C | 322 MPa Show Material materials with Yield strength of 322 MPa | quenched and tempered (+QT) | EN 10028-2 | Flat | RP02 | |
250 °C | 330 MPa Show Material materials with Yield strength of 330 MPa | quenched and tempered (+QT) | EN 10028-2 | Flat | RP02 | |
250 °C | 339 MPa Show Material materials with Yield strength of 339 MPa | quenched and tempered (+QT) | EN 10028-2 | Flat | RP02 | |
300 °C | 318 MPa Show Material materials with Yield strength of 318 MPa | quenched and tempered (+QT) | EN 10028-2 | Flat | RP02 | |
300 °C | 327 MPa Show Material materials with Yield strength of 327 MPa | quenched and tempered (+QT) | EN 10028-2 | Flat | RP02 | |
300 °C | 335 MPa Show Material materials with Yield strength of 335 MPa | quenched and tempered (+QT) | EN 10028-2 | Flat | RP02 | |
350 °C | 314 MPa Show Material materials with Yield strength of 314 MPa | quenched and tempered (+QT) | EN 10028-2 | Flat | RP02 | |
350 °C | 322 MPa Show Material materials with Yield strength of 322 MPa | quenched and tempered (+QT) | EN 10028-2 | Flat | RP02 | |
350 °C | 330 MPa Show Material materials with Yield strength of 330 MPa | quenched and tempered (+QT) | EN 10028-2 | Flat | RP02 | |
400 °C | 306 MPa Show Material materials with Yield strength of 306 MPa | quenched and tempered (+QT) | EN 10028-2 | Flat | RP02 | |
400 °C | 314 MPa Show Material materials with Yield strength of 314 MPa | quenched and tempered (+QT) | EN 10028-2 | Flat | RP02 | |
400 °C | 322 MPa Show Material materials with Yield strength of 322 MPa | quenched and tempered (+QT) | EN 10028-2 | Flat | RP02 | |
450 °C | 293 MPa Show Material materials with Yield strength of 293 MPa | quenched and tempered (+QT) | EN 10028-2 | Flat | RP02 | |
450 °C | 301 MPa Show Material materials with Yield strength of 301 MPa | quenched and tempered (+QT) | EN 10028-2 | Flat | RP02 | |
450 °C | 309 MPa Show Material materials with Yield strength of 309 MPa | quenched and tempered (+QT) | EN 10028-2 | Flat | RP02 |
Thermal
Property | Value | Condition | Related Standards | Shape | Comment |
---|---|---|---|---|---|
Coefficient of thermal expansion | 1.1e-05 - 1.4e-05 1/K Show Material materials with Coefficient of thermal expansion of 1.1e-05 - 1.4e-05 1/K | Typical for Chromium Molybdenum Steel | |||
Max service temperature | 20 - 530 °C Show Material materials with Max service temperature of 20 - 530 °C | quenched and tempered (+QT) | EN 10028-2 | Flat | Long |
530 °C Show Material materials with Max service temperature of 530 °C | quenched and tempered (+QT) | EN 10028-2 | Flat | Long | |
Melting point | 1382 - 1529 °C Show Material materials with Melting point of 1382 - 1529 °C | Typical for Chromium Molybdenum Steel | |||
Specific heat capacity | 448 - 502 J/(kg·K) Show Material materials with Specific heat capacity of 448 - 502 J/(kg·K) | Typical for Chromium Molybdenum Steel | |||
Thermal conductivity | 36 - 43 W/(m·K) Show Material materials with Thermal conductivity of 36 - 43 W/(m·K) | Typical for Chromium Molybdenum Steel |
Electrical
Chemical properties
Property | Value | Condition | Related Standards | Shape |
---|---|---|---|---|
Carbon | 0.17 % Show Material materials with Carbon of 0.17 % | quenched and tempered (+QT) | EN 10028-2 | Flat |
Chromium | 1 - 1.5 % Show Material materials with Chromium of 1 - 1.5 % | quenched and tempered (+QT) | EN 10028-2 | Flat |
Copper | 0.3 % Show Material materials with Copper of 0.3 % | quenched and tempered (+QT) | EN 10028-2 | Flat |
Manganese | 0.4 - 0.65 % Show Material materials with Manganese of 0.4 - 0.65 % | quenched and tempered (+QT) | EN 10028-2 | Flat |
Molybdenum | 0.45 - 0.65 % Show Material materials with Molybdenum of 0.45 - 0.65 % | quenched and tempered (+QT) | EN 10028-2 | Flat |
Nickel | 0.3 % Show Material materials with Nickel of 0.3 % | quenched and tempered (+QT) | EN 10028-2 | Flat |
Nitrogen | 0.012 % Show Material materials with Nitrogen of 0.012 % | quenched and tempered (+QT) | EN 10028-2 | Flat |
Phosphorus | 0.015 % Show Material materials with Phosphorus of 0.015 % | quenched and tempered (+QT) | EN 10028-2 | Flat |
Silicon | 0.5 - 0.8 % Show Material materials with Silicon of 0.5 - 0.8 % | quenched and tempered (+QT) | EN 10028-2 | Flat |
Sulfur | 0.005 % Show Material materials with Sulfur of 0.005 % | quenched and tempered (+QT) | EN 10028-2 | Flat |
0.01 % Show Material materials with Sulfur of 0.01 % | quenched and tempered (+QT) | EN 10028-2 | Flat |
Technological properties
Property | ||
---|---|---|