General
Property | Value | Comment |
---|---|---|
Density | 7.8 - 7.9 g/cm³ Show Material materials with Density of 7.8 - 7.9 g/cm³ | Typical for Chromium Molybdenum Steel |
Mechanical
Property | Temperature | Value | Condition | Related Standards | Shape | Comment |
---|---|---|---|---|---|---|
Elastic modulus | 200 - 215 GPa Show Material materials with Elastic modulus of 200 - 215 GPa | Typical for Chromium Molybdenum Steel | ||||
Elongation | 15.9 % Show Material materials with Elongation of 15.9 % | Predicted Value, A200 | ||||
16.4 % Show Material materials with Elongation of 16.4 % | Predicted Value, A80 | |||||
18.9 % Show Material materials with Elongation of 18.9 % | Predicted Value, A5 | |||||
20.2 % Show Material materials with Elongation of 20.2 % | Predicted Value, A80 Transverse | |||||
23.4 % Show Material materials with Elongation of 23.4 % | Predicted Value, A50 | |||||
20 °C | 18 % Show Material materials with Elongation of 18 % | quenched and tempered (+QT) | EN 10028-2 | Flat | Transverse | |
20 °C | 18 % Show Material materials with Elongation of 18 % | quenched and tempered (+QT) | EN 10028-2 | Flat | ||
Hardness, Brinell | 250 [-] Show Material materials with Hardness, Brinell of 250 [-] | Predicted Value, Transverse | ||||
Poisson's ratio | 0.29 [-] Show Material materials with Poisson's ratio of 0.29 [-] | Typical for Chromium Molybdenum Steel | ||||
Reduction of area | 43.7 % Show Material materials with Reduction of area of 43.7 % | Predicted Value, Transverse | ||||
43.8 % Show Material materials with Reduction of area of 43.8 % | Predicted Value | |||||
Shear modulus | 79.1 GPa Show Material materials with Shear modulus of 79.1 GPa | Predicted Value | ||||
Shear strength | 684.8 MPa Show Material materials with Shear strength of 684.8 MPa | Predicted Value | ||||
Tensile strength | 20 °C | 580 - 760 MPa Show Material materials with Tensile strength of 580 - 760 MPa | quenched and tempered (+QT) | EN 10028-2 | Flat | Transverse |
20 °C | 580 - 760 MPa Show Material materials with Tensile strength of 580 - 760 MPa | quenched and tempered (+QT) | EN 10028-2 | Flat | ||
Yield strength | 290.4 MPa Show Material materials with Yield strength of 290.4 MPa | Predicted Value, RP1 | ||||
327.8 MPa Show Material materials with Yield strength of 327.8 MPa | Predicted Value, RP1 Transverse | |||||
479.7 MPa Show Material materials with Yield strength of 479.7 MPa | Predicted Value, RP02 Transverse | |||||
483.5 MPa Show Material materials with Yield strength of 483.5 MPa | Predicted Value, RP05 | |||||
566.8 MPa Show Material materials with Yield strength of 566.8 MPa | Predicted Value, RP002 | |||||
20 °C | 415 MPa Show Material materials with Yield strength of 415 MPa | quenched and tempered (+QT) | EN 10028-2 | Flat | Transverse | |
20 °C | 415 MPa Show Material materials with Yield strength of 415 MPa | quenched and tempered (+QT) | EN 10028-2 | Flat | ||
50 °C | 405 MPa Show Material materials with Yield strength of 405 MPa | quenched and tempered (+QT) | EN 10028-2 | Flat | RP02 | |
100 °C | 390 MPa Show Material materials with Yield strength of 390 MPa | quenched and tempered (+QT) | EN 10028-2 | Flat | RP02 | |
150 °C | 370 MPa Show Material materials with Yield strength of 370 MPa | quenched and tempered (+QT) | EN 10028-2 | Flat | RP02 | |
200 °C | 365 MPa Show Material materials with Yield strength of 365 MPa | quenched and tempered (+QT) | EN 10028-2 | Flat | RP02 | |
250 °C | 360 MPa Show Material materials with Yield strength of 360 MPa | quenched and tempered (+QT) | EN 10028-2 | Flat | RP02 | |
300 °C | 355 MPa Show Material materials with Yield strength of 355 MPa | quenched and tempered (+QT) | EN 10028-2 | Flat | RP02 | |
350 °C | 352 MPa Show Material materials with Yield strength of 352 MPa | quenched and tempered (+QT) | EN 10028-2 | Flat | RP02 | |
400 °C | 350 MPa Show Material materials with Yield strength of 350 MPa | quenched and tempered (+QT) | EN 10028-2 | Flat | RP02 | |
450 °C | 340 MPa Show Material materials with Yield strength of 340 MPa | quenched and tempered (+QT) | EN 10028-2 | Flat | RP02 |
Thermal
Property | Value | Condition | Related Standards | Shape | Comment |
---|---|---|---|---|---|
Coefficient of thermal expansion | 1.1e-05 - 1.4e-05 1/K Show Material materials with Coefficient of thermal expansion of 1.1e-05 - 1.4e-05 1/K | Typical for Chromium Molybdenum Steel | |||
Max service temperature | 20 - 450 °C Show Material materials with Max service temperature of 20 - 450 °C | quenched and tempered (+QT) | EN 10028-2 | Flat | Long |
450 °C Show Material materials with Max service temperature of 450 °C | quenched and tempered (+QT) | EN 10028-2 | Flat | Long | |
Melting point | 1382 - 1529 °C Show Material materials with Melting point of 1382 - 1529 °C | Typical for Chromium Molybdenum Steel | |||
Specific heat capacity | 448 - 502 J/(kg·K) Show Material materials with Specific heat capacity of 448 - 502 J/(kg·K) | Typical for Chromium Molybdenum Steel | |||
Thermal conductivity | 36 - 43 W/(m·K) Show Material materials with Thermal conductivity of 36 - 43 W/(m·K) | Typical for Chromium Molybdenum Steel |
Electrical
Chemical properties
Property | Value | Condition | Related Standards | Shape |
---|---|---|---|---|
Boron | 0.003 % Show Material materials with Boron of 0.003 % | quenched and tempered (+QT) | EN 10028-2 | Flat |
Calcium | 0.015 % Show Material materials with Calcium of 0.015 % | quenched and tempered (+QT) | EN 10028-2 | Flat |
Carbon | 0.1 - 0.15 % Show Material materials with Carbon of 0.1 - 0.15 % | quenched and tempered (+QT) | EN 10028-2 | Flat |
Chromium | 2.75 - 3.25 % Show Material materials with Chromium of 2.75 - 3.25 % | quenched and tempered (+QT) | EN 10028-2 | Flat |
Copper | 0.25 % Show Material materials with Copper of 0.25 % | quenched and tempered (+QT) | EN 10028-2 | Flat |
Manganese | 0.3 - 0.6 % Show Material materials with Manganese of 0.3 - 0.6 % | quenched and tempered (+QT) | EN 10028-2 | Flat |
Molybdenum | 0.9 - 1.1 % Show Material materials with Molybdenum of 0.9 - 1.1 % | quenched and tempered (+QT) | EN 10028-2 | Flat |
Nickel | 0.25 % Show Material materials with Nickel of 0.25 % | quenched and tempered (+QT) | EN 10028-2 | Flat |
Niobium | 0.07 % Show Material materials with Niobium of 0.07 % | quenched and tempered (+QT) | EN 10028-2 | Flat |
Nitrogen | 0.012 % Show Material materials with Nitrogen of 0.012 % | quenched and tempered (+QT) | EN 10028-2 | Flat |
Phosphorus | 0.015 % Show Material materials with Phosphorus of 0.015 % | quenched and tempered (+QT) | EN 10028-2 | Flat |
Silicon | 0.15 % Show Material materials with Silicon of 0.15 % | quenched and tempered (+QT) | EN 10028-2 | Flat |
Sulfur | 0.005 % Show Material materials with Sulfur of 0.005 % | quenched and tempered (+QT) | EN 10028-2 | Flat |
0.01 % Show Material materials with Sulfur of 0.01 % | quenched and tempered (+QT) | EN 10028-2 | Flat | |
Titanium | 0.03 % Show Material materials with Titanium of 0.03 % | quenched and tempered (+QT) | EN 10028-2 | Flat |
Vanadium | 0.2 - 0.3 % Show Material materials with Vanadium of 0.2 - 0.3 % | quenched and tempered (+QT) | EN 10028-2 | Flat |
Technological properties
Property | ||
---|---|---|
Supplier Disclaimer | The given information is a rough description and some properties can depend on various factors such as product thickness. Please contact the supplier or refer to the related norm or standard for further information. |